Semiconductor-based metal oxide gas detector of five mixed from zinc chloride Z and tin chloride S salts Z:S ratio 0, 25, 50, 75 and 100% were fabricated on glass substrate by a spray pyrolysis technique. With thickness were about 0.2 ±0.05 μm using water soluble as precursors at a glass substrate temperature 500 ºC±5, 0.05 M, and their gas sensing properties toward CH4, LPG and H2S gas at different concentration (10, 100, 1000 ppm) in air were investigated at room temperature which related with the petroleum refining industry.
Furthermore structural and morphology properties were scrutinize. Results shows that the mixing ratio affect the composition of formative oxides were (ZnO, Zn2SnO4, Zn2SnO4+ZnSnO3, ZnSnO3, SnO2) ratios ment

Surfaces quality is one of the most specified customer requirements for machine parts. The major indication of surfaces quality on machined parts is surface roughness. The research aim is to study the cutting conditions and their effects on the surface roughness. This paper utilizes regression models to predict surface roughness over the machining time for variety of cutting conditions in turning. In the experimental part for turning, different types of materials (Aluminum alloy, Copper alloy, and Gray cast iron) were considered with different cutting speed ( ) and feed rate ( ). A mathematical Model depending on statistical-mathematical method between surface roughness (Rz ) and cutting condition ( , ) were derived, for the three materials

Abstract: Stars whose initial masses are between (0.89 - 8.0) M☉ go through an Asymptotic Giant Branch (AGB) phase at the end of their life. Which have been evolved from the main sequence phase through Asymptotic Giant Branch (AGB). The calculations were done by adopted Synthetic Model showed the following results: 1- Mass loss on the AGB phase consists of two phases for period (P <500) days and for (P>500) days; 2- the mass loss rate exponentially increases with the pulsation periods; 3- The expansion velocity VAGB for our stars are calculated according to the three assumptions; 4- the terminal velocity depends on several factors likes metallicity and luminosity. The calculations indicated that a super wind phase (S.W) developed on the A

This study was performed by using the unsaturated polyester resin as matrix to the
composite materials with the rice husk as reinforced materials . The research included study
of wear test on the composite material The results show that the, wear is increased with the
increase of applied load and distance slipping and also with time increase . moreover the
shows that the higher value wear rate( 1.91gm/cm) from the load (20) N and the higher value
wear rate (1.43gm/cm) from the higher distance (4cm) and from the higher time (6min) higher
wear rate (5.33gm/cm).

Design of experiments (DOE) was made by Minitab software for the study of three factors used in the precipitation process of the Sodium Aluminate solution prepared from digestion of α-Al₂O₃  to determine the optimum conditions to a produce Boehmite which is used in production of ɤ-Al₂O₃ during drying and calcination processes, the factors are; the temperature of the sodium aluminate solution, concentration of HCl acid added for the precipitation and the pH of the solution at which the precipitation was ended. The design of the experiments leads to 18 experiments.

   The results show that the optimum conditions for the precipitation of the sodium aluminate solution which

Biological Activity of Complexes of Some Amino Acid

 The   aim  of   this   work   is   the   synthesis  of   new   derivatives  of   barbiturate   of  D-erythroascorbic acid. To obtain these derivatives, the 5,6-O-isopropylidene-L-ascorbic acid (4) was chosen, which was prepared from the reaction of L-ascorbic acid (3) as a starting material with dry acetone in the presence of hydrogen chloride. The esterification of hydroxyl groups at C-2 and C-3 positions with excess of benzoyl chloride in dry pyridine was obtained compound (5). Hydrolysis for compound (5) in acetic acid (65%) gave the compound (6). Oxidation of the product (6) with sodium periodate results an Al