The aim of this paper, study the effect of carbon nanotubes on the electrical properties of polyvinylchloride. Samples of polyvinylchloride carbon nanotubes composite prepared by using hot press technique. The weight percentages of carbon nanotubes are 0,5,10 and 20wt.%. Results showed that the D.C electrical conductivity increases with increasing of the weight percentages of carbon nanotubes. Also, the D.C electrical conductivity changed with increase temperature for different concentrations of carbon nanotubes. The activation energy of D.C electrical conductivity is decreased with increasing of carbon nanotubes concentration.

The physical and morphological characteristics of porous silicon (PS) synthesized via gas sensor was assessed by electrochemical etching for a Si wafer in diluted HF acid in water (1:4) at different etching times and different currents. The morphology for PS wafers by AFM show that the average pore diameter varies from 48.63 to 72.54 nm with increasing etching time from 5 to 15min and from 72.54 to 51.37nm with increasing current from 10 to 30 mA. From the study, it was found that the gas sensitivity of In2O3: CdO semiconductor, against NO2 gas, directly correlated to the nanoparticles size, and its sensitivity increases with increasing operating temperature.

Polyaniline membranes of aniline were produced using an electrochemical method in a cell consisting of two poles. The effect of the vaccination was observed on the color of membranes of polyaniline, where analysis as of blue to olive green paints. The sanction of PANI was done by FT-IR and Raman techniques. The crystallinity of the models was studied by X-ray diffraction technique. The different electronic transitions of the PANI were determined by UV-VIS spectroscopy. The electrical conductivity of the manufactured samples was measured by using the four-probe technique at room temperature. Morphological studies have been determined by Atomic force microscopy (AFM). The structural studies have been measured by (SEM).

Intellectual property rights of all kinds، and their nature، are considered a tool in the hands of their owner that enables him to monopolize the benefits that you confer on them without any dispute or mediation from anyone. Intellectual property on its intellectual product، and preventing others from exploiting it without obtaining the permission of its owner All of this is reflected positively on the progress of the industrial and commercial field، and this justifies the protection provided by the laws regulating intellectual property rights to its owner، whether at the national or international level، and with our recognition of the right of the owner of intellectual property rights to enjoy the exclusive use of his right، and

Spectral and linear optical properties for a mixture of Rhodamine B (RB) and Fluorescein Sodium (Na Fl) organic laser dyes were determined at different concentrations 10-3, 10-4 M in ethanol solvent at room temperature. The intensity of absorption range is towards longer wavelengths (red shift). The quantum efficiency diminished while the radiative and fluorescence life time increased when increment concentration, organic laser dyes have a spectrum within the range 540-500 nm. Results demonstrate that a mixture of laser dyes are effective optical materials when contrasted with individual laser dyes. It can be utilized as resonator in cavity lasers.

The influence of pre- shot peening and welding parameters on mechanical and metallurgical properties of dissimilar and similar aluminum alloys AA2024-T3 and AA6061-T6 joints using friction stir welding have been studied. In this work, numbers of plates were equipped from sheet alloys in dimensions (150*50*6) mm then some of them were exposed to shot peening process before friction stir welding using steel ball having diameter 1.25 mm for period of 15 minutes. FSW joints were manufactured from plates at three welding speeds (28, 40, 56 mm/min) and welding speed 40mm/min was chosen at a rotating speed of 1400 rpm for welding the dissimilar pre- shot plates. Tow joints were made at rotational speed of 1000 rpm and welding speed of 40m/min f