The photo-electrochemical etching (PECE) method has been utilized to create pSi samples on n-type silicon wafers (Si). Using the etching time 12 and 22 min while maintaining the other parameters 10 mA/cm2 current density and HF acid at 75% concentration.. The capacitance and resistance variation were studied as the temperature increased and decreased for prepared samples at frequencies 10 and 20 kHz. Using scanning electron microscopy (SEM), the bore width, depth, and porosity % were validated. The formation of porous silicon was confirmed by x-ray diffraction (XRD) patterns, the crystal size was decreased, and photoluminescence (PL) spectra revealed that the emission peaks were centered at 2q of 28.5619° and 28.7644° for etching time 12 and 22 min, respectively. Studying the capacitance and resistivity during temperature increasing and decreasing for both itching times shows clearly that the prepared pSi as a thermal sensor is working better and in more selectivity for 20 min itching time
In This paper, CuO thin films having different thickness (250, 300 , 350 and 400) nm were deposited on glass substrates by thermal vacuum evaporator. The thermal oxidation of this evaporated film was done in heated glass at temperature (300 in air at one hour. The study of X-ray diffraction investigated all the exhibit polycrystalline nature with monoclinic crystal structure include uniformly grains. Thin film’s internal structure topographical and optical properties. Furthermore, the crystallization directions of CuO (35.54 , 38.70 ) can be clearly observed through an X-ray diffraction analysis XRD, Atomic Force Microscope AFM (topographic image) showed that the surface Characteristics , thin films crystals grew with increases in either
... Show MoreIn this study, the ZnTe thin films were deposited on a glass substrate at a thickness of 400nm using vacuum evaporation technique (2×10-5mbar) at RT. Electrical conductivity and Hall effect measurements have been investigated as a function of variation of the doping ratios (3,5,7%) of the Cu element on the thin ZnTe films. The temperature range of (25-200°C) is to record the electrical conductivity values. The results of the films have two types of transport mechanisms of free carriers with two values of activation energy (Ea1, Ea2), expect 3% Cu. The activation energy (Ea1) increased from 29meV to 157meV before and after doping (Cu at 5%) respectively. The results of Hal
... Show MoreThis research includes a study of dezincification by corrosion from brass alloys in three types of media, which are acidic solution, basic and slat solution in different percentages. The study show the higher dezincification occurs in basic solution which decrease the fatigue properties where the fatigue properties are inversely proportional with dezincification.
Thin films of Zinc Selenide ZnSe have been prepared by using thermal evaporation in vacuum technique (10-5Torr) with thickness (1000, 2700, 4000) A0 and change electrode material and deposited on glass substrates with temperature (373K) and study some electrical properties at this temperature . The graphs shows linear relation between current and voltage and the results have shown increases in the value of current and electrical conductivity with increase thickness and change electrode material from Aluminum to Copper
This work is related to the investigation of the effects of porous silicon (PSi) morphologies on the performance of plasmonic gold nanoparticles (Au-NPs) hot spot SERS sensors for the detection of amoxicillin molecules. Two Si wafers with different resistivity values of 10 and 100 Ω.cm were used to synthesize a PSi layer of pores- and mud-like structures, respectively, by pulsed photo chemical etching process. The hot spot SERS sensors were synthesized by incorporating the Au-NPs within the PSi morphologies of pores- and mud- like structures which are characterized by high density of nucleation sites. Plasmonic Au- NPs with different sizes and hot spot regions were incorporated into the porous structures by the ion reduction proces
... Show MoreIn this work, varying compositions of SiO2 micro filler were added
with the Polyvinyl Chloride (PVC) and samples have been prepared
using film casting technique. The results have been analyzed and
compared for PVC samples with (1 wt%, 3 wt%, 5 wt% and 10 wt%)
SiO2 micro filler. Mechanical characteristics such as tensile strength,
elongation at break and Young`s modulus were measured for all the
samples, where the tensile strength was increased from 8.39 Mpa for
purified PVC to 16 Mpa for 3% SiO2/PVC composite. Also, thermal
conductivity measurement values illustrated that composite materials
have a good thermal insulation at 10 wt. %, thermal conductivity was
decreased from 0.1684 W/m.
Need organizations today to move towards strategic thinking which means analyzing situations faced by particular challenges of change in the external environment, which makes it imperative for The Organization That to reconsider their strategies and orientations and operations, a so-called re-engineering to meet those challenges and pressures, to try to achieve improvement root in the installation of the organization and methodscompletion of its work towards achieving high levels of performance and that is reflected to achieve its objectives, and this is what aims to Current search to deal with implications characteristics of strategic thinking in the stages of application re-engineering business of the company General Industries
... Show MoreIn this work, (CdO)1-x (CoO)x thin films were prepared on glass slides by laser-induced plasma using Nd:YAG laser with (λ=1064 nm) and duration (9 ns) at different laser energies (200-500 mJ) with ratio (x=0.5), The influence of laser energy on structural and optical properties has been studied. XRD patterns show the films have a structure of polycrystalline wurtzite. As for AFM tests results for the topography of the surface of the film, where the results showed that the grain size and the average roughness increase with increasing laser energy. The optical properties of all films were also studied and the results showed that the absorption coefficient for within the wavelength range (280-1100 nm), The value of the optical power gap fo
... Show MoreCadmium sulfide (CdS) nanocrystalline thin films have been prepared by chemical bath deposition (CBD) technique on commercial glass substrates at 70ºC temperature. Cadmium chloride (CdCl2) as a source of cadmium (Cd), thiourea (CS(NH2)2) as a source of sulfur and ammonia solution (NH4OH) were added to maintain the pH value of the solution at 10. The characterization of thin films was carried out through the structural and optical properties by X-ray diffraction (XRD) and UV-VIS spectroscopy. A UV-VIS optical spectroscopy study was carried out to determine the band gap of the nanocrystalline CdS thin film and it showed a blue shift with respect to the bulk value (from 3.9 - 2.4eV). In present w
... Show MoreIn this work, we presented a study of the structural formula for a new series of complexes with Ag(I), Cu(II), Zn(II), and Cd(II) derived from the guanine azo dye ligand 2-amino-8-((3-hydroxyphenyl)diazinyl)-1,7-dihydro-6H-purin-6-one (HAG), which is investigated using various physicochemical analyses, spectroscopic techniques (FT-IR, U.V-VIS, and 1H NMR), thermogravimetric analysis (TGA). In addition, elemental analyses, magnetic susceptibility, and molar conductance measurements were all stabilized. As well as the mole ratio, stability constant, and Gibbs free energy were studied for all complexes, where they showed high stability and spontaneous synthesis. The Cu(II) complex was suggested to have octahedral stere
... Show More