Hard-grade asphalt binders like AC20-30 typically exhibit excessive stiffness, reduced penetration, and compromised workability, necessitating modification before use in paving applications. This study evaluates the efficacy of regular polyalphaolefin (PAO), a synthetic olefin-based lubricant, as a performance-enhancing modifying agent for such binders. AC20-30 was blended with PAO at dosages ranging from 2 wt.% to 10 wt.%, and the modified binders were characterized via penetration, ductility, softening point, and rotational viscosity measurements, alongside advanced rheological and chemical-morphological analyses. Incorporating PAO in AC20-30 asphalt progressively reduced the binder stiffness and enhanced its flexibility, with all modifie

Cadmium Oxide thin films were deposited on glass substrate by spray pyrolysis technique at different temperatures (300,350,400, 500)oC. The optical properties of the films were studied in this work. The optical band-gap was determined from absorption spectra, it was found that the optical band-gap was within the range of (2.5-2.56)eV also width of localized states and another optical properties.

The Asphalt cement is produced as a by-product from the oil industry; the asphalt must practice further processing to control the percentage of its different ingredients so that it will be suitable for paving process. The objective of this work is to prepare different types of modified Asphalt cement using locally available additives, and subjecting the prepared modified Asphalt cement to testing procedures usually adopted for Asphalt cement, and compare the test results with the specification requirements for the modified Asphalt cement to fulfill the paving process requirements. An attempt was made to prepare the modified Asphalt cement for pavement construction in the laboratory by digesting each of the two penetration grade Asphalt c

The local asphalt concrete fracture properties represented by the fracture energy, J-integral, and stress intensity factor are calculated from the results of the three point bending beam test made for pre notches beams specimens with deformation rate of 1.27 ^mm/min. The results revealed that the stress intensity factor has increased by more than 40% when decreasing the testing temperature 10˚C and increasing the notch depth from 5 to 30^mm. The change of asphalt type and content have a limited effect of less than 6%.

GaN thin films were deposited by thermal evaporation onto
glass substrates at substrate temperature of 403 K and a thickness of
385 nm . GaN films have amorphous structure as shown in X-ray
diffraction pattern . From absorbance data within the range ( 200-
900 ) nm direct optical energy gap was calculated . Also the others
optical parameters like transmittance T, reflectance R , refractive
index n , extinction coefficient k , real dielectric constant 1 Î , and
imaginary dielectric constant 2 Î were determined . GaN films
have good absorbance and minimum transmittance in the region of
the visible light .

The effect of annealing temperature (Ta) on the electrical properties like ,D.C electrical conductivity (σ DC), activation energy (Ea),A.C conductivity σa.c ,real and imaginary (ε1,ε2) of dielectric constants ,relaxation time (τ) has been measured of ZnS thin films (350 nm) in thickness which were prepared at room temperature (R.T) using thermal evaporation under vacuum . The results showed that σD.C increases while the activation energy values(Ea) decreases with increasing of annealing temperature.(Ta) from 303- 423 K .
The density of charge carriers (nH) and Hall mobility (μH) increases also with increasing of annealing temperature Hall effect measurements showed that ZnS films were n-type converted to p-type at high annealin

In the present work, lead silicate glasses have been prepared with
different amount of lead oxide content. Structure properties such as
X-ray diffraction, AFM, and FTIR analyses have been done. The
exceeding of PbO content more than 25wt% revealed a decreasing in
density. The X- ray revealed that the strongest peak related to
Hexagonal silica dioxide and the other crystal phases formed were
related to silica oxide (SiO2) and lead oxide (PbO). Growth and
decayed phases in X-ray have been observed with changing lead
oxide content. Homogeneous surface was obtained using AFM
analyzer with an average diameter around 100 nm. Infrared spectrum
is characterized by the presence of large absorption band between
120

Objective: This study aimed to evaluate the effect of coating titanium (Ti) dental implant with polyether ketone ketone (PEKK) polymer using magnetron sputtering on osseointegration, trying to overcome some of the problems associated with Ti alloys. Material and Methods: Implants were prepared from grade (II) commercially pure titanium (CP Ti), then laser was used to induce roughness on the surface of Ti. PEKK was deposited on the surface of Ti implants by radiofrequency (RF) magnetron sputtering technique. The implants were divided in to three groups: without coating (Ls), with PEKK coating using argon (Ar) as sputtering gas (Ls-PEKK-Ar), and with PEKK coating using nitrogen (N) as sputtering gas (Ls-PEKK-N). All the implants were implante

A field trial was conducted at Abu-Ghraib research station , Baghdad , Iraq . The objectives were to study the effect of nitrogen fertilizer and planting space on the performance of rape seed. A split-plot in a randomized complete of block design with three replications were used. Five levels of nitrogen fertilizer ( 120,160,200,240,280 Kg / ha ) were assigned to main plots, where as planting space in sub-plots. The result obtained confirmed that 280,240 kg / ha nitrogen maximized seed yield 1.830 , 1.773 ton/ha, oil yield,0.843,0.824 ton/ha .Results showed that planting space 30 cm produced the highest seed yield 1.90 ton / ha and oil yield , 0.884 ton / ha . Interactions between nitrogen fertilizer and p

The Current status of biomedical waste of solid, liquid and gaseous formulations from medical and educational laboratories in Iraqi universities and research centers was assessed using a well-structured questionnaire. The questionnaire was distributed to scientists, researchers, medical technicians and graduate students who are directly involved in laboratoiy daily activities. The responses were analyzed statistically and interpreted accordingly. The results showed diat the frequency of questionnaire respondent's affiliation gave the highest percentage frequency (69.4%) with the questionnaire of Technical Medical Institute/Al-Mansour while constitute die responses of the Dnig Control Department/Ministry of Sciences and Technology gave the l