Abstract

    Binary polymer blend was prepared by mechanical mixing method of unsaturated polyester resin with Nitrile Butadiene Rubber (NBR) with different weight ratios (0, 5, 10 and 15) % of (NBR). Tensile characteristics and wear rates of these blends were studied for all mixing ratios. The microstructure of fracture surfaces of the prepared samples were investigated by optical microscope. The results were showed that strain rates of the resin material increase after blending it with rubber while the ultimate tensile strength and Young’s modulus values of it will decrease. It is also noticed that the wear rate of resin decreases with increasing of (NBR) content.

Keywords:<

       In this paper we offer two new subclasses of an open unit disk of r-fold symmetric bi-univalent functions. The Taylor-Maclaurin coefficients  have their coefficient bounds calculated. Furthermore, for functions in , we have solved Fekete-  functional issues. For the applicable classes, there are also a few particular special motivator results.

The results of the present study showed that twenty-five samples were collected for the age group 35–40 years and four samples for the age group 65–70 years for both genders. The results showed that 48 (48%) of the samples were obtained from the hands, 16 (16%) from the legs, 12 (12%) from the abdominal area, and 10 (10%) from the chest area. The four (4%) samples were obtained from burns in the back and thighs area. The samples taken according to the cause of burns were 40 (40%) due to hot water, hot liquids, or hot steam, followed by 18 (18%) due to the use of hot tools, 15 (15%) due to fires, 12 (12%) due to electric currents, 10 (10%) due to chemicals such as strong acids, alkaline lye, paint thinner, or gasoline, and 5 (5%) due

In this research prepared two composite materials , the first prepared from unsaturated polyester resin (UP) , which is a matrix , and aluminum oxide (Al2O3) , and the second prepared from unsaturated polyester resin and aluminum oxide and copper oxide (CuO) , the two composites materials (Alone and Hybrid) of percentage weight (5,10,15)% . All samples were prepared by hand layup process, and study the electrical and thermal conductivity. The results showed decrease electrical conductivity from (10 - 2.39) ×10-15 for (Up+ Al2O3) and from (10 - 2.06)×10-15 for (Up+ Al2O3+ CuO) .But increase thermal conductivity from( 0.17 - 0.505) for (Up+ Al2O3) and from (0.17 - 0.489) for (Up+ Al2O3+ CuO).

Unsaturated soil can raise many geotechnical problems upon wetting and drying resulting in swelling upon wetting and collapsing (shrinkage) in drying and changing in the soil shear strength. The classical principles of saturated soil are often not suitable in explaining these phenomena. In this study, expansive  soil (bentonite and sand) were tested in different water contents and dry unit weight chosen from the compaction curve to examine the effect of water content change on soil properties (swelling pressure, expansion index, shear strength (soil cohesion) and soil suction by the filter paper method). The physical properties of these soils were studied by conducting series of tests in laboratory. Fitting methods

In this research work a composite material was prepared contains a matrix which is unsaturated polyester resin (UPE) reinforced with carbon nanotube the percentage weight (0.1, 0.2, 0.4.0.5) %, and Zn particle the percentage weight (0.1, 0.2,0.4,0.5)%.
All sample were prepared by hand lay-up, process the mechanical tests contains hardness test, wear rate test, and the coefficient of thermal conductivity. The results showed a significant improvement in the properties of overlapping, Article containing carbon nano-tubes and maicroparticles of zinc because of its articles of this characteristics of high quality properties led to an, an increase in the coefficient of the rmalconductivity, and increase the hardness values with increased pe

Molecular interactions between 2-isopropenylnaphthalene-methacrylic acid (IPNMA) block copolymer( as a model for water- soluble polymer) and methanol at several temperatures were studied using fluorescence techniques , Fluorescence spectrum for (IPNMA) exhibits two emission bands at around 342 nm and 387 nm corresponding to the monomer and the excimer bands , respectively .The fluorescence spectra of dilute solution of (IPNMA) in methanol were recorded in temperature range of 8- 45?C . Plot of the excimer to monomer intensity ratio Ie/Im versus temperature was obtained, which shows double lines with positive slopes crossing at 25?C , the increasing of slope value above this temperature is s

Detection of pathogenic bacteria, such as Listeria  monocytogenes, in food is crucial for safeguarding public health in Iraq.  Forty five samples of frozen meat (15 samples of each of minced red meat, chicken, and fish) were collected from different markets in Baghdad city. Molecular (RT-PCR) and culturing (conventional microbiological examination) methods were used to determine the level of contamination of L. monocytogenes in these types of meat.

For the culturing method, TSYEB broth was used as an enrichment medium, whereas BALCAM medium (HiMedia) with the listeria selective supplement FD061 was used as a selective medium, for the isolation and identification of this bacterium. The isolates were con

This study was performed by using the unsaturated polyester resin as matrix to the
composite materials with the rice husk as reinforced materials . The research included study
of wear test on the composite material The results show that the, wear is increased with the
increase of applied load and distance slipping and also with time increase . moreover the
shows that the higher value wear rate( 1.91gm/cm) from the load (20) N and the higher value
wear rate (1.43gm/cm) from the higher distance (4cm) and from the higher time (6min) higher
wear rate (5.33gm/cm).

Four antimony compounds were used in this inves as additives to retard combustion of unsaturated polyester and epoxy resins, namely: 1. Tetraethyl ammonium tribromoethylantimonates (additive I). 2. Tetraethyl ammonium chlorodibromoethylantimonates (additive II). 3. Tetraethyl ammonium trichloroethylantimonates (additive III). 4. Tetraethyl ammonium bromodichloroethylantimonates (additive IV). The effects of these additives on flammability of unsaturated polyester and epoxy resins have been studied by using sheets of the resins with weight percentages of (0.5,1.0,1.5,2.0,2.5&3.0%) of the additives in dimensions of (150 X150X3)mm .Three standard test methods were used to measure the flame retardation which are: (ASTM:D -2863), (ASTM:D-635