Fe, Co and Sb nanopowders were fruitfully prepared by electrical wire explosion method in Double distilled and de-ionized water (DDDW) media. The formation of iron, cobalt and antimony (FeCoSb) alloy nanopowder was monitored by X-ray diffraction. The x-ray diffraction pattern indicates that there are iron, cobalt and antimony peaks. Optical properties of this alloy nanoparticles were characterized by UV-Visible absorption spectra. The absorption peak position is shifted to the lower wavelengths when the current increases. That means the mean size of the nanoparticles controlled by changing the magnitude of the current. The surface morphological analysis is carried out by employing Scanning Electron Microscope (SEM). Particles with varies

 In the present work polymer electrolytes were formulated using the solvent casting technique. Under special conditions, the electrolyte content was of fixed ratio of polyvinylpyrolidone (PVP): polyacrylonitrile (PAN) (25:75), ethylene carbonate (EC) and propylene carbonate (PC) (1:1) with 10% of potassium iodide (KI) and iodine I₂ = 10% by weight of KI. The conductivity was increased with the addition of ZnO nanoparticles. It is also increased with the temperature increase within the range (293 to 343 K). The conductivity reaches maximum value of about (0.0296 S.cm^-1) with (0.25 g) ZnO. The results of FTIR for blend electrolytes indicated a significant degree of interaction between the polymer blend (PVP and PAN)

With the narratives and sayings in the biography of the Prophet and the science of the Koran, Orientalists used this case as a pretext to distort the biography of the Prophet and his character and patience for his call. Researcher in the folds of his research.

In This research a Spectroscopic complement and Thermodynamic properties for molecule PO2 were studied . That included a calculation of potential energy . From the curve of total energy for molecule at equilibrium distance , for bond (P-O), the degenerated of bond energy was (4.332eV) instate of the vibration modes of ( PO2 ) molecule and frequency that was found active in IR spectra because variable inpolarization and dipole moment for molecule. Also we calculate some thermodynamic parameters of ( PO2 ) such as heat of formation , enthalpy , heat Of capacity , entropy and gibb's free energy Were ( -54.16 kcal/mol , 2366.45 kcal/mol , 10.06 kcal /k/mol , 59.52 k

The atmospheric air cold plasma has been used to manufacture gold nanomaterials for treating parasitic leishmaniasis. This study experimentally assessed the treatment of Leishmania parasites (L. donovani and L. tropica) by gold nanoparticles. Specifically, atmospheric pressure nonthermal plasma was generated using different diameters (1.0, 2.8, 3.8 and 4.3 mm) of high voltage electrode. Aqueous gold tetrachloride salts (HAuCl4·4H2O) were used as precursor to produce gold nanoparticles. UV-vis spectroscopy and x-ray diffraction were conducted for characterization of the nanoparticles. The optimum condition (a diameter of 1 mm) was chosen to prepare gold nanoparticles, where the grain size was found to be 17 nm. Accordingly, the nanoparticle

Synthesis of new nucleoside analogues of the type : 3¢ , 3¢ - gem – di – C – nitromethly , expected to have useful application in the chemotherapeutic treatment of AIDS , cancer and microbial infections. The synthesis involved the condensation of the appropriate sugar derivative ( i.e . 3¢ , 3¢ –  gem – di – C – nitromethly – 1–  ribofuranose ) with nitrogen bases , such as , uracil and theophllin following a multi step scheme starting from diacetone golucose (1) (scheme 1) .The prepared compound were identified by spectroscopic methods ; ir , mass , ¹H and ¹³C nmr.

Nano gamma alumina was prepared by double hydrolysis process using aluminum nitrate nano hydrate and sodium aluminate as an aluminum source, hydroxyle poly acid and CTAB (cetyltrimethylammonium bromide) as templates. Different crystallization temperatures (120, 140, 160, and 180) ⁰C and calcinations temperatures (500, 550, 600, and 650) ⁰C were applied. All the batches were prepared at PH equals to 9. XRD diffraction technique and infrared Fourier transform spectroscopy were used to investigate the phase formation and the optical properties of the nano gamma alumina. N₂ adsorption-desorption (BET) was used to measure the surface area and pore volume of the prepared nano alumina, the particle size and the

Two samples of (Ag NPs-zeolite) nanocomposite thin films have been prepared by easy hydrothermal method for 4 hours and 8 hours inside the hydrothermal autoclave at temperatures of 100°C. The two samples were used in a photoelectrochemical cell as a photocatalyst inside a cell consisting of three electrodes: the working electrode photoanode (AgNPs-zeolite), platinum as a cathode electrode, and Ag/AgCl as a reference electrode, to study the performance of AgNPs-zeolite under dark current and 473 nm laser light for water splitting. The results show the high performance of an eight-hour sample with high crystallinity compared with a four-hour sample as a reliable photocatalyst to generate hydrogen for renewable energies.