Cadmium oxide thin films were prepared by D.C magnetron plasma sputtering using different voltages (700, 800, 900, 1000, 1100 and 1200) Volt. The Cadmium oxide structural properties using XRD analysis for just a voltage of 1200 volt at room temperature after annealing in different temperatures (523 and 623) K were studied .The results show that the films prepared at room temperature have some peaks belong to cadmium element along the directions (002), (100), (102) and (103) while the other peaks along the directions of (111), (200) and (222) belong to cadmium oxide. Annealed samples display only cadmium oxide peaks. Also, the spectroscopic properties of plasma diagnostic for CdO thin films were determined and the results show that the el

structural and electrical of CuIn (Sex Te1-x)2

CdS and CdS:Sn thin films were successfully deposited on glass
substrates by spray pyrolysis method. The films were grown at
substrate temperatures 300 C°. The effects of Sn concentration on the
structural and optical properties were studied.
The XRD profiles showed that the films are polycrystalline with
hexagonal structure grown preferentially along the (002) axis. The
optical studies exhibit direct allowed transition. Energy band gap
vary from 3.2 to 2.7 eV.

Rare earth elements (Cerium, Lanthanum and Neodymium) doped CdS thin films are prepared using the chemical Spray Pyrolysis Method with temperature 200 oC. The X-ray diffraction (XRD) analysis refers that pure CdS and CdS:Ce, CdS:La and CdS:Nd thin films showed the hexagonal crystalline phase. The crystallite size determined by the Debye-Scherrer equation and the range was (35.8– 23.76 nm), and it was confirmed by field emission scanning electron microscopy (FE-SEM). The pure and doped CdS shows a direct band gap (2.57 to 2.72 eV), which was obtained by transmittance. The room-temperature photoluminescence of pure and doped CdS shows large peak at 431 nm, and two small peaks at (530 and 610 nm). The Current – voltage measurement in da

Four Se70Ge20Sb10 alloy samples were prepared using the melt quenching technique. To improve the energy states of the mobility gap, the samples were exposed to gamma radiation from 60Co source at various doses of 600, 1200, 1500, and 2000 Gy. The electrical characteristics were examined both before and after irradiation. The conductivity analysis revealed that all of our samples were impacted by gamma radiation. The reorganization of the amorphous lattice and the degree of radiation-induced disorder have been involved in the changes that occurred in the electrical characteristics of the irradiated samples. All irradiated and non-irradiated samples feature three conduction mechanisms at low temperatures, where the electrical conducti

The synthesis of the bisaldehyde ligand 2-(1,1-dimethyl-1,3-dihydro-2H-benzo[e]indol-2-ylidene)malonaldehyde (B) and its coordinated compounds with Cr(III), Mn(II), Fe(II), Co(II), Ni(II) and Cu(II) ions are reported. The synthetic route of B was completed by adopting the Vilsmeier-Haack reaction. This was based on the mixing of 1,1,2-trimethyl-1H-benzo[e]indole with phosphoryl trichloride and N, N-dimethylformamide (anhydrous) that gave the aminomethylenemalondialdehyde. The use of POCl3 and DMF was aimed to give the Vilsmeier-Haack intermediate, which was kept at 5°C and then heated with stirring at 85°C. The addition of an aqueous NaOH solution (35%) to the reaction mixture resulted in the isolation of B. The monomeric coordinated comp

Structural and optical properties of CdO and CdO0.99Cu0.01 thin
films were prepared in this work. Cadmium Oxide (CdO) and
CdO0.99Cu0.01semiconducting films are deposited on glass substrates
by using pulsed laser deposition method (PLD) using SHG with Qswitched
Nd:YAG pulsed laser operation at 1064nm in 6x10-2 mbar
vacuum condition and frequency 6 Hz. CdO and CdO0.99Cu0.01 thin
films annealed at 550 C̊ for 12 min. The crystalline structure was
studied by X-ray diffraction (XRD) method and atomic force
microscope (AFM). It shows that the films are polycrystalline.
Optical properties of thin films were analyzed. The direct band gap
energy of CdO and CdO0.99Cu0.01 thin films were determined from
(αhυ)1/2 v

This study reports the formation, characterisation and biological evaluation of a Schiff base ligand and its corresponding metal complexes. The Schiff base ligand (HL) was prepared through a condensation reaction involving isonicotinohydrazide and N'-((1R,2R,4R,5S, E)-2,4-bis(4-chlorophenyl)-3-azabi cyclo[3.3.1]nonan-9-ylidene) isonicotinohydrazide (M) in EtOH solvent and (3-5) drops of conc. HCl. The interaction of HL with selected metal chlorides including Mn(+2), Co(+2), Ni(+2), Cu(+2) and Zn(+2) in a 2:1 (L:M) mole ratio resulted in the synthesis of complexes with the general formula [M(HL)Cl2] (where: M = Mn(+2),Co(+2) and Ni(+2)) and [M`(HL)Cl2] (where M` =  Cu(+2) and Zn(+2)). The characterisation of the prepared compounds w