In this research the a-As flims have been prepared by thermal evaporation with thickness 250 nm and rata of deposition r_d(1.04nm/sec) as function to annealing temperature (373 and 473K), from XRD analysis we can see that the degree of crystalline increase with T_a, and I-V characteristic for dark and illumination shows that forward bias current varieties approximately exponentially with voltage bias. Also we found that the quality factor and saturation current dependence on annealing temperatures.

Phosphorus and dye (direct black) removal for small – scale wastewater applications were investigated using oven dried alum sludge (ODS).The use of alum sludge not only provides a low cost technique but also reduces the hazard and the cost related to the disposal of large amount of alum sludge. Phosphorus and dye removal exceeds 90% for all operating conditions applied in the research.
The residuals generated during the treatment of wastewater were further tested to study the possibility of aluminum leaching from oven dried alum sludge during the adsorption of phosphorus and dye. These tests observed a reduction in aluminum leaching indicating a lower risk imposed on land and surface water based on disposal options rather than on al

 Thin films were prepared from melting coumrin C 2 dye in solvent DMF with PMMA with the same  solvent and concentrations(1*10-2    5*10-3, 1*10-3  )M ,Films were either left on Flat surface for24hours or dried in avacuum oven for five hours at a temperature of 80c.The relative intensity of both the absorption and fluorescece spectrum are found to be increased with the increase of thickness of these films and concentration  .Also the thickness of these films was measured by Mickelsons interfearing method.Also quantum efficiency of these films were measured too

In this experimental study, which was carried out in photonics laboratory at Strathclyde University, UK, dynamics of a multi-Quantum well semiconductor active medium laser, was studied. This is in order to study its emission stability and pulse shape development under the influence of strong optical feedback level with different deriving currents, in the free space transmission medium. An external stable resonator was constructed by inserting high reflectivity dielectric mirror outside the laser output, 20 cm apart from it, which is an extralarge external cavity. Controlling the reflected back optical power was done by using a nonpolarized (50:50) beam splitter. The external resonator supported by focusing (plano-convex) lens in order to

This study focused on the role and importance of alkaloid compounds in Punica granatum peels which is one of many wide distribution medicinal fruits. Two kinds of pathogenic fungi were isolated from patients in Baghdad to be tested, also a type of extracts was prepared, alkaloids were isolated and partially purified and detected by two ways, a classic depended technique also used for determine these alkaloids, results showed an observed differences among extracts or treatments towards the fungi samples. So this study was one of the scientific applications to find natural alternative compounds that inhibit the growth of several pathogenic organisms that cause dangers and harms for human health.

   In this research the effect of grain size and effect of La2O3 doping on densification  rate for the  initial and intermediate  stages of sintering were studied .The experimental results for α – cristobilite powder are modeled using ( L2-Regression ) technique in studying  the effect of grain size and La2O3 doping using  three particles size (6.12, 8.92, 13.6 ) µm, with undoped  initial powder and with La2O3 doping . The mathematical simulation showes that the densification rates increase as the initial particles sizes decrease and vice versa. This shows that the densification depends directly on the initial compact density which reflects the contacts area between the particles . How

In this report Silver doped Tin Sulfide (SnS) thin films with ratio of (0.03) were prepared using thermal evaporation with a vacuum of 4*10-6 mbar on glass with (400) nm thickness and the sample annealing with ( 573K ). The optical constants for the wavelengths in the range (300-900) nm and Hall effect for (SnS and SnS:3% Ag) films are investigated and calculated before and after annealing at 573 K. Transition metal doped SnS thin films the regular absorption 70% in the visible region, the doping level intensification the optical band gap values from 1.5- 2 eV. Silver doped tin sulfide (SnS) its direct optical band gap. Hall Effect results of (SnS and SnS:3% Ag) films show all films were (p-type) electrical conductivity with resistivity of

Thin films of pure polycarbonate (PC) with anthracene doping PC films for different doping ratios (10, 20, 30, 40, 50 and 60 ml) were prepared by using a casting method. The influence of anthracene doping ratio on photo-fries rearrangement of polycarbonate was systematic investigated. Furthermore, pure PC and anthracene doping PC films were irradiated via UV light at a wavelength (254 nm) for different periods (5, 240, 288, and 360 hrs). The photo-fries rearrangement occurring in pure PC and anthracene doping PC films were monitored using UV and FTIR spectroscopies. The photo-fries rearrangement leads to scission the carbonate linkage and formation phenylsalicylate and dihydroxybenzophenes. The result of the UV spectrum confirms disappea