This study investigates the influence of silver oxide (Ag2O) concentration on the optical characteristics of phosphate bioactive glasses (PBGs). PBGs have emerged as promising alternatives to conventional silicate glasses in the medical field due to their excellent bioactivity and chemical resistance. Samples with varying Ag2O concentrations (0, 0.25, 0.5, and 0.75g) were sintered at 780°C for 2 hrs in an electric furnace. The samples were subjected to Fourier transfer infrared spectroscopy (FTIR), ultraviolet-visible (UV-Vis) spectroscopy, and photoluminescence (PL) tests to assess their functional groups and optical properties. By analyzing the FTIR spectrum of phosphate bioactive glass containing different amounts of Ag2O, it is

The aim of this study to evaluate the effects of die holes diameter and speed of die on the performance of machine and feed pellet quality. Machine productivity (Kg.h-1), consumed power (kW), pellet durability (%) and pellet bulk density (g.cm-3) was studied. The study factors consisted of three diameter of die holes (3, 4, and 5 mm), and three speeds die (280, 300, and 320 rpm). Results showed with increasing of die holes diameter from 3 to 4 and to 5 mm give a significant increase in machine productivity, while consumed power, pellet durability and pellet bulk density a significant decreased. By increasing the die speed, from 280 to 300 then to 320 rpm, the machine productivity increased significantly, while consumed power, pellet durabil

Polyacrylamide Solutions of different concentrations (0.2, 0.4, 0.6, 0.8, 1.0 %) of Ag nanoparticles and ZnO nanoparticles were prepared, the viscosities and surface tension were measured for all solutions, where measurements indicated an increase in these properties with increased concentration, where the relative viscosity of polyacrylamide/zinc nanoparticles increased from 1.275 to 2.243, and the relative viscosity of polyacrylamide/silver nanoparticles increased from 1.178 to 1.934. Viscosity is significant parameters during electrospinning process. While the surface tension of the polyacrylamide/zinc nanoparticles has changed from 0.0343 Nm-1 to .0.0.0 Nm-1 and changed from .0.000Nm-1 to.0.0.0 Nm-1. Also the constants KH and KK were

A precise evaluation of caries excavation endpoint is essential in clinical and laboratory investigations. Caries invasion differentiates dentin into structurally altered layers. This study assessed these changes using Raman spectroscopy and Vickers microhardness. Ten permanent molars with occlusal and proximal carious lesions were assessed and compared at 130 points utilizing four Raman spectroscopic peaks: phosphate v1 at 960 cm−1, amide I (1650 cm−1), amide III (1235 cm−1) and the C-H bond of the pyrrolidine ring (1450 cm−1). The phosphate-to-amide I peak ratio and collagen integrity peak ratio (amide III: C-H bond) of carious zones were calculated and compared in both lesions. The former ratio was correlated to 130 Vicke

Acrylic polymer/cement nanocomposites in dark and light colors have been developed for coating floors and swimming pools. This work aims to emphasize the effect of cement filling on the mechanical parameters, thermal stability, and wettability of acrylic polymer. The preparation was carried out using the casting method from acrylic polymer coating solution, which was added to cement nanoparticles (65 nm) with weight concentrations of (0, 1, 2, 4, and 8 wt%) to achieve high-quality specifications and good adhesion. Maximum impact strength and Hardness shore A were observed at cement ratios of 2 wt% and 4 wt%, respectively. Changing the filling ratio has a significant effect on the strain of the nanocomposites. The contact angle was i

New types of hydrodesulfurization (HDS) catalyst Re-Ni-Mo/ γ-Al₂O₃ was prepared and tested separately with two prepared conventional HDS catalysts (Ni-Mo/ γ-Al₂O₃ and Co-Mo//γ-Al₂O₃) by using a pilot plant hydrotreatment unit. Activities of three prepared hydrodesulfurization catalysts were examined in hydrodesulfurization (HDS) of atmospheric gas oil at different temperatures 275 to 350 °C and LHSV 1 to 4 h^-1, the reactions conducted under constant pressure 40 bar and H₂/HC ratio 500 ml/ml .Moreover, the hydrogenation of aromatic (HAD) in gas oil has been studied. HDS was much improved by adding promoter Re to the Ni-Mo/Al₂O₃

New types of hydrodesulfurization (HDS) catalyst Re-Ni-Mo/ γ-Al2O3 was prepared and tested separately with two prepared conventional HDS catalysts (Ni-Mo/ γ-Al2O3 and Co-Mo//γ-Al2O3) by using a pilot plant hydrotreatment unit. Activities of three prepared hydrodesulfurization catalysts were examined in hydrodesulfurization (HDS) of atmospheric gas oil at different temperatures 275 to 350 °C and LHSV 1 to 4 h-1, the reactions conducted under constant pressure 40 bar and H2/HC ratio 500 ml/ml .Moreover, the hydrogenation of aromatic (HAD) in gas oil has been studied. HDS was much improved by adding promoter Re to the Ni-Mo/Al2O3 catalyst. The results showed that Re-Ni-Mo/ γ-Al2O3 have more activity in desulfurization than Ni-Mo//γ-Al2O3

New types of hydrodesulfurization (HDS) catalyst Re-Ni-Mo/ γ-Al2O3 was prepared and tested separately with two prepared conventional HDS catalysts (Ni-Mo/ γ-Al2O3 and Co-Mo//γ-Al2O3) by using a pilot plant hydrotreatment unit. Activities of three prepared hydrodesulfurization catalysts were examined in hydrodesulfurization (HDS) of atmospheric gas oil at different temperatures 275 to 350 °C and LHSV 1 to 4 h-1, the reactions conducted under constant pressure 40 bar and H2/HC ratio 500 ml/ml .Moreover, the hydrogenation of aromatic (HAD) in gas oil has been studied. HDS was much improved by adding promoter Re to the Ni-Mo/Al2O3 catalyst. The results showed that Re-Ni-Mo/ γ-Al2O3 have more activity in desulfurization than Ni-Mo//