Fractographic Analysis of Tensile Failures of Zirconia Epoxy Nanocomposites
...Show More Authors

This work characterizes the fractographic features of the neat epoxy and ZrO2 epoxy nanocomposites. All samples were subjected to a tensile test to determine the tensile strength and tensile modulus. SEM images were used to study the morphology of the fractured surface. The fractographic of the fracture surfaces were studied by microstructure analysis program (j-images) to specify the effect of ZrO2 nanoparticles on tensile performance and failure mechanism for ZrO2 epoxy nanocomposites. The tensile test results show that the addition of ZrO2 nanoparticles (2, 4, 6, 8, and 10 vol.%) to the epoxy matrix leads to increase the tensile strength about 40% for optimal content of ZrO2 nanoparticles at 4 vol.%, tensile modules of ZrO2 epoxy nanocomposites increased about 200% for optimal content of ZrO2 nanoparticles at 4 vol.%. SEM images show that the patterns of fractured surfaces of ZrO2 epoxy nanocomposites are different from the pattern of the neat epoxy. The fracture roughness of ZrO2 epoxy nanocomposites increased with the increases of the percentages of ZrO2 nanoparticles, where the increment of fracture roughness about 30% for optimal content of ZrO2 nanoparticles at 4 vol.% can be indicator for the improvement of mechanical properties (tensile strength and modules).

Scopus Clarivate Crossref
View Publication Preview PDF
Quick Preview PDF
Publication Date
Fri Oct 01 2010
Journal Name
Iraqi Journal Of Physics
Effect ofweight percentage chopped carbon fibers on the mechanism of cracks propagation for Epoxy composites
...Show More Authors

In this research, the mechanism of cracks propagation for epoxy/ chopped carbon fibers composites have been investigated .Carbon fibers (5%, 10%, 15%, and 20%) by weight were used to reinforce epoxy resin. Bending test was carried out to evaluate the flexural strength in order to explain the mechanism of cracks propagation. It was found that, the flexural strength will increase with increasing the percentage weight for carbon fibers. At low stresses, the cracks will state at the lower surface for the specimen. Increasing the stresses will accelerate the speed of cracks until fracture accorded .The path of cracks is changed according to the distributions of carbon fibers

View Publication Preview PDF
Publication Date
Sun Jun 11 2017
Journal Name
Ibn Al-haitham Journal For Pure And Applied Sciences
Study the Electromechanical Strength Properties for Epoxy Dispersed Silica Powder Composite
...Show More Authors

  Powder Silica (SiO2) was added to epoxy polymer with different weight percentages  (3.75,7.5,11.25 and 15 wt%) for particle size ï‚£ 63 µm. Hand lay-up method it is used to prepared (Epoxy-Silica) composite, and cutting appropriate specimens for testing. Electrical strength varies nonlinearly with specimens thickness, also decreasing with average time for the rise of voltage decreases due to electro thermal effects. Clearly, electrical strength decreases with the increase of the proportion of added silica. The hardness, tensile strength and young modulus increased with the added silica increases due to changing in material characteristics from ductility to brittle. Microscopic cracks and irregularity deformation were a

... Show More
View Publication Preview PDF
Crossref (3)
Crossref
Publication Date
Sun Dec 01 2019
Journal Name
Materials Science-poland
Electrical and thermal characteristics of MWCNTs modified carbon fiber/epoxy composite films
...Show More Authors
Abstract<p>To enhance interfacial bonding between carbon fibers and epoxy matrix, the carbon fibers have been modified with multiwall carbon nanotubes (MWCNTs) using the dip- coating technique. FT-IR spectrum of the MWCNTs shows a peak at 1640 cm<sup>−1</sup> corresponding to the stretching mode of the C=C double bond which forms the framework of the carbon nanotube sidewall. The broad peak at 3430 cm<sup>−1</sup> is due to O–H stretching vibration of hydroxyl groups and the peak at 1712 cm<sup>−1</sup> corresponds to the carboxylic (C=O) group attached to the carbon fiber. The peaks at 2927 cm<sup>−1</sup> and 2862 cm<sup>−1</sup> ar</p> ... Show More
View Publication
Scopus (35)
Crossref (34)
Scopus Clarivate Crossref
Publication Date
Wed Jan 01 2020
Journal Name
Advanced Composites Letters
Enhanced thermal and electrical properties of epoxy/carbon fiber–silicon carbide composites
...Show More Authors

The silicon carbide/carbon fiber (SiC/CF) hybrid fillers were introduced to improve the electrical and thermal conductivities of the epoxy resin composites. Results of Fourier transform infrared spectroscopy revealed that the peaks at 3532 and 2850 cm−1 relate to carboxylic acid O–H stretching and aldehyde C–H stretching appearing deeper with an increased volume fraction of SiC. Scanning electron microscopic image shows a better interface bonding between the fiber and the matrix when the volume fraction of SiC particles are increased. As frequency increases from 102 Hz to 106 Hz, dielectric constants decrease slightly. Dissipation factor (tan δ) values keep low a

... Show More
View Publication
Scopus (28)
Crossref (36)
Scopus Clarivate Crossref
Publication Date
Thu Oct 20 2022
Journal Name
Ibn Al-haitham Journal For Pure And Applied Sciences
Fabrication of Natural Gelcoats (Epoxy/ Pumpkin Peels Fibers) Composites with High Mechanical and Thermal Properties
...Show More Authors

     Pumpkin waste powder was used as a coloring and strengthening filler in epoxy to prepare a natural gelcoat . The Pumpkin powder was mixed with different weight ratios (1, 2, 3, 4, 5, 6, 7, and 8%) to the epoxy matrix to select the best value of powder addition. The effect of the pumpkin particle size on the mechanical properties (impact, flexural, hardness, and wear loss) using two different sizes (2.5 and 1.25 microns) was studied. The impact strength increased from (10.09 KJ/ m2) for neat epoxy to (14.79 KJ/ m2) for epoxy with  1% of micron pumpkin fibers ( MPF) with particle size 2.5 micrometer and (14.21 KJ/ m2) for epoxy with 4% (1.25 MPF), flexural strength increased from (41.94 MPa) for n

... Show More
View Publication Preview PDF
Crossref (3)
Crossref
Publication Date
Mon Feb 04 2019
Journal Name
Iraqi Journal Of Physics
Structure dependence of gamma ray irradiation effects on polyurethane and epoxy resin studied by PAL technique
...Show More Authors

Positron annihilation lifetime (PAL) technique has been employed to
study the microstructural changes of polyurethane (PU), EUXIT 101
and epoxy risen (EP), EUXIT 60 by Gamma-ray irradiation with the
dose range (95.76 - 957.6) kGy. The size of the free volume hole and
their fraction in PU and EP were determined from ortho-positronium
lifetime component and its intensity in the measured lifetime spectra.
The results show that the irradiation causes significant changes in the
free volume hole size (Vh) and the fractional free volume (Fh), and
thereby the microstructure of PU and EP. The results indicate that
the γ-dose increases the crystallinity in the amorphous regions of PU
and increas

... Show More
View Publication Preview PDF
Crossref (1)
Crossref
Publication Date
Mon Jun 17 2019
Journal Name
Ibn Al-haitham Journal For Pure And Applied Sciences
Hard and Tough Epoxy Resins Modified with Thermosetting Materials
...Show More Authors

Epoxy resins were modified by some thermosetting materials using unsaturated polyesters which were cured with styrene , MMA ,and MA . When unsaturated Polyester ( as thermosetting material ) was used , and cured with styrene showed better results than acrylic monomers . Thermal stability rised on modification of epoxy resins with unsaturated polyester . The new formulation had converted the epoxy resin from hard brittle material to hard and tough material .

Thermal analysis were studied using ( DSC ) and physicomechanical characteristics were measured .

View Publication Preview PDF
Publication Date
Mon Nov 14 2022
Journal Name
Journal Of Reinforced Plastics And Composites
Effect of phosphoric acid molarity on the structural, thermal, mechanical, and electrical properties of polyimide/polyaniline nanocomposites
...Show More Authors

In this paper, we used two monomers, 3,3',4,4'-benzophenone tetracarboxylic dianhydride (BTDA) and m,m'-diaminobenzophenone (m, m’-DABP), to produce polyamide acid and then converted it to polyimide (PI). The effects of phosphoric acid (H3PO4) molarity (1, 2, and 3 M) on the structural, thermal, mechanical, and electrical characteristics of the polyimides/polyaniline (PI/PANI) nanocomposites were studied. Two sharp reflection peaks were developed by the addition of PANI to PI. When 3 M H3PO4 is added, the crystalline sharp peak loses some of its intensity. The complex formation of PI/PANI-H3PO4 was confi

... Show More
View Publication
Scopus (11)
Crossref (10)
Scopus Clarivate Crossref
Publication Date
Mon Apr 03 2023
Journal Name
Polymer Composites
Effect of silver nanoparticles on structural, thermal, electrical, and mechanical properties of poly(vinyl alcohol) polymer nanocomposites
...Show More Authors

View Publication
Scopus (24)
Crossref (26)
Scopus Clarivate Crossref
Publication Date
Tue Aug 06 2024
Journal Name
Fullerenes, Nanotubes And Carbon Nanostructures
Preparation and characterization of PVA/MWCNT nanocomposites: a composition dependence study of structural, optical and mechanical properties
...Show More Authors

View Publication
Scopus (1)
Crossref (2)
Scopus Clarivate Crossref