Abstract

 Nano-crystalline ZSM-5 zeolite was synthesized by hydrothermal method using chelating agent and two gel compositions:Compositionɪ:Al₂O₃:86SiO₂:5.5TPA:12.7Na₂O:3.4Trien:3320H₂O.Compositionɪɪ:Al₂O₃:68SiO₂:5.4TPA:10Na₂O:2.6Trien:2626H₂O.Study of hydrothermal reaction factors on characteristics of nano- sized zsm-5 has been carried on ,among them are crystallization temperature, crystallization time and concentration of template ( TPAOH ) solution. Synthesis was accomplished in PTFE lined autoclave ( reactor ) . The product were characterized by X-ray diffraction ( XRD ),Atomic force microsc

Zeolite Y nanoparticles were synthesized by sol - gel method. Dffirent samples using two silica sources were prepared.
Sodium metasilicate (Na2SiO3) (48% silica) and silicic acid silica (H2SiO3) (75% silica) were employed as silica
source and aluminum nitrate (Al(NO3)3.9H2O) was the aluminum source with tetrapropylammonium hydroxide
(TPAOH) as templating agent.
The synihesized-samples were characterized by X-ray diffraction, showed the requirement of diffirent aging time for
complete crystallization to be achieved. Transmission Electronic Microscope (TEM) images, showed the particles were
in the same range of 30 - 75 nm. FT-IR spectroscory, showed the synthesized samples having the zeolite Y crystal
properties. The i

Worldwide attention is being focused on  nanocrystalline  zeolites  and they are replacing conventional ones due to their pronounced potential in many fields. In this study, NaY zeolite has been prepared hydrothermally using sol –gel method and modified to the proton type by ion –exchange process. Characterization is made using X-ray diffraction (XRD), thermogravimetric analysis (TGA),  Fourier transform infrared spectroscopy (FTIR),  Atomic force microscopy (AFM), Brunauer –Emmet- Teller (BET) nitrogen adsorption method, Ammonia Temperature programmed desorption (NH₃-TPD) and Scanning electron microscopy( SEM).  The effect of aging time, silica to alumina ratio is studied and the results sh

L-arabinose isomerase from Escherichia coli O157:H7 Was immobilized with activated Bentonite from local markets of Baghdad, Iraq by 10% 3-APTES and treated with 10% aqueous glutaraldehyde, the results refer that the yield of immobilization was 89%, and pH profile of free and immobilized L-arabinose isomerase was 7 and 7.5 and it is stable at 6-8 for 60 min respectively, while, the optimum temperature was 30 and 35°C and it was stable at 35 and 40°C for 60 min but it loses more than 60 and 30% from its original activity at 50°C for free and immobilized L-arabinose isomerase respectively. Immobilized enzyme retained its full activity for 32 day, but it retained 73.58% of its original activity after storage for 60 d

Soil is a crucial component of environment. Total soil analysis may give information about possible enrichment of the soil with heavy metals. Heavy metals, potentially contaminate soils, may have been dumped on the ground. chromium, nickel and cadmium,

Light naphtha one of the products from distillation column in oil refineries used as feedstock for gasoline production. The major constituents of light naphtha are (Normal Paraffin, Isoparaffin, Naphthene, and Aromatic). In this paper, we used zeolite (5A) with uniform pores size (5Aº) to separate normal paraffin from light naphtha, due to suitable pore size for this process and compare the behavior of adsorption with activated carbon which has a wide range of pores size (micropores and mesopores) and high surface area. The process is done in a continuous system - Fixed bed reactor- at the vapor phase with the constant conditions of flow rate 5 ml/min, temperature 180^oC, pressure 1.6 bar and 100-gram weight o

Aniline and its derivatives are common contaminants in various wastewaters and represent a serious worry for societies health and a challenge to ecologists due to their dangers effects on to the human health.

ZSM-5 zeolite was prepared from locally available materials (kaolin and rice husk) for adsorption of aniline from synthetic wastewater. Characterization of the prepared zsm-5, kinetics and thermodynamic of the adsorption process were investigated.

The characterization results of the prepared zsm-5 zeolite showed that the surface area was 270.1 m²/g and pore volume 0.21828 cm³/g. The silica to alumina ratio (Si/Al) was 166. 47 and the sodium content was 11 wt. %. The atomic force microscope (AFM)

In this work, the synergistic effect of chlorinated rubber (additive I),with zeolite 3A (additive II), zeolite 4A (additive III), and zeolite 5A (additive IV) in (1:1) weight percentage, on the flammability for unsaturated polyester resin was studied in the weight ratios for (3,7,10,13&15%) by preparing films of (130×130×3) mm in diameters. Three standard test methods used to measure were the flame retardation which are; ASTM: D-2863, ASTM: D- 635& ASTM: D-3014. Results obtained from these tests indicated that all of the additives were effective additive IV has the highest efficiency as a flame retardant.

In the present work, zeolite Y has been synthesized successfully by sol-gel method.Zeolite was synthesized by crystallization of the final gel which consist from seeding and feed stock gels at  85 ^oC. HY zeolite was prepared by an ion exchange process with ammonium chloride solution and then loaded with different percentages of  platinum and titanium by the wet - impregnation method.

X-ray Diffraction (XRD), X-ray Florescence (XRF), Scanning Electron Microscopy (SEM), BET surface area and, Crushing strength were used to characterize the synthesized and prepared catalysts . Results showed high crystallinity  90%  with silica to alumina ratio 5 for HY, high surface area of 600 m²/g and pore