The reaction of starting materials (L-asCl2):bis[O,O-2,3;O,O-5,6-(chloro(carboxylic) methylidene)]- -L-ascorbic acid] with glycine gives new product bis[O,O-2,3,O,O-5,6-(N,O-di carboxylic methylidene N-glycine)-L-ascorbic acid] (L-as-gly) which is isolated and characterized by, Mass spectrum UV-visible and Fourier transform infrared spectrophotometer (FT-IR) . The reaction of the (L-as-gly) with M+2; Co(II) Ni(II) Cu(II) and Zn(II) has been characterized by FT- IR , Uv-Visible , electrical conductivity, magnetic susceptibility methods and atomic absorption and molar ratio . The analysis showed that the ligand coordinate with metal ions through mono dentate carboxylic resulting in six-coordinated with Co(II) Ni(II) Cu(II) ions while with

I've been in this research preparation and diagnostic complexes mixed Kandat of Alcavaúan Alpiculan ion Althaaossianat with some metal ions has been reactive in ethanol solvent and distilled water by (1:1) and water complexes and lotions to the accounts of the metal in the complex

Ortho amino hydrazobenzene (L) has been prepared from the reaction of ortho amino phenyl thiol with phenyl hyrazan in mole ratio(1:1). It has been characterized by elemental analysis (C, H, N), IR, UV–Vis. The complexes of the bivalent ions (Co, Ni, Cu, Zn, Pd, Cd, Hg and Pb) and the trivalent (Cr) have been prepared and characterized too. The structural have been established by elemental analysis(C,H,N), IR , UV – Vis spectra , conductivity measurements , atomic absorption and magnetic susceptibility . The complexes showed characteristic behaviour of octahedral geometry around the metal ion and the( N,N) ligand coordinated in bidentate modeexcept with pd showed square planer. ? ,kf , ?max for the complexes were estimated too . ? for Co

Some physical and chemical characteristics of Jurf Al- Sakar drinking water plant in Babylon governorate have been studied. Seven locations for this plant were selected. These were the drinking water treatment plant source on Euphrates River before entering the plant, precipitation, filtration and collection tanks, and also after leaving the plant at distances of one meter, 4 and 8 km. The samples were collected bimonthly from October, 2002 to August, 2003. Some results match with the national and international standard characters while the other characters (Turbidity, total hardness, calcium, nitrate, phosphate and the biological oxygen demand values) were not match. The present study showed that drinking water treatment plant is undrinka

Abstract

In this manuscript, a simple new method for the green synthesis of platinum nanoparticles (Pt NPs) utilizing F. carica Fig extract as reducing agent for antimicrobial activities was reported. Simultaneously, the microstructural and morphological features of the synthesized Pt NPs were thoroughly investigated. In particular, the attained Pt NPs exhibited spherical shape with diameter range of 5-30 nm and root mean square of 9.48 nm using Transmission Electron Microscopy (TEM) and Atomic Force Microscopy (AFM), respectively. Additionally, the final product (Pt NPs) was screened as antifungal and antibacterial agent against Candida and Aspergillus species as well as Gram-positive Staphyllococcus aureus and G

In this work, copper substituted cobalt ferrite nanoparticles with
chemical formula Co1-xCuxFe2O4 (x=0, 0.3, and 0.7), has been
synthesized via hydrothermal preparation method. The structure of
the prepared materials was characterized by X-ray diffraction (XRD).
The (XRD) patterns showed single phase spinel ferrite structure.
Average crystallite size (D), lattice constant (a), and crystal density
(dx) have been calculated from the most intense peak (311).
Comparative standardization also performed using smaller average
particle size (D) on the XRD patterns of as-prepared ferrite samples
in order to select most convenient hydrothermal synthesis conditions
to get ferrite materials with smallest average particl

The fabrication of Solid and Hollow silver nanoparticles (Ag NPs) has been achieved and their characterization was performed using transmission electron microscopy (TEM), zeta potential, UV–VIS spectroscopy, and X-ray diffraction (XRD). A TEM image revealed a quasispherical form for both Solid and Hollow Ag NPs. The measurement of surface charge revealed that although Hollow Ag NPs have a zeta potential of -43 mV, Solid Ag NPs have a zeta potential of -33 mV. According to UV-VIS spectroscopy measurement Solid and Hollow Ag NPs both showed absorption peaks at wavelengths of 436 nm and 412 nm, respectively. XRD pattern demonstrates that the samples' crystal structure is cubic, similar to that of the bulk materials, with