Global warming and environmental damage have become major problems. The production of Portland cement releases large quantities of gas, which cause pollution to the atmosphere. This problem can be solved via the use of sustainable materials, such as glass powder. This study investigates the effect of partial replacement of cement with sustainable glass powder at various percentages (0, 15, 20, and 25%) by weight of cement on some mechanical properties (compressive strength, flexural strength, absorption, and dry density) of Reactive Powder Concrete (RPC) containing a percentage of Polypropylene fibers (PRPC) of 1% by weight. Furthermore, steam curing was performed for 5 hours at 90oC after hardening the sample directly. The RPC was

Interested current Research measuring damage currency Swap by converting The ministry of higher Education and scientific Research money The Iraqi dinar To U.S dollar by Trade Bank Of Iraq , And that The damage Generated resulting from Deferent Between the Exchange Rate adopted From Central Bank of Iraq and Market Exchange Rate adopted by The Trade Bank Of Iraq , and Which led to the greet damage ( losses ) in Bearing by the ministry, which led to the reduction of the financial allocations for licensed curriculum outside of Iraq , and this in turn leads  to reduction in the number of students Sender ( scholarships )  outside Iraq.

Where the estimated loss (damage) that suffer by the Ministry of H

                The characteristics of sulfur nanoparticles were studied by using atomic force microscope (AFM) analysis. The atomic force microscope (AFM) measurements showed that the average size of sulfur nanoparticles synthesized using thiosulfate sodium solution through the extract of cucurbita pepo extra was 93.62 nm. Protecting galvanized steel from corrosion in salt media was achieved by using sulfur nanoparticles in different temperatures. The obtained data of thermodynamic in the presence of sulfur nanoparticles referred to high value as compares to counterpart in the absence of sulfur nanoparticles, the high inhibition efficiency (%IE) and corrosion resistance were at high temperature, the corrosion rate or weig

The exploitation of obsolete recyclable resources including paper waste has the advantages of saving resources and environment protection. This study has been conducted to study utilizing paper waste to adsorb phenol which is one of the harmful organic compound byproducts deposited in the environment. The influence of different agitation methods, pH of the solution (3-11), initial phenol concentration (30-120ppm), adsorbent dose (0.5-2.5 g) and contact time (30-150 min) were studied. The highest phenol removal efficiency obtained was 86% with an adsorption capacity of 5.1 mg /g at optimization conditions (pH of 9, initial phenol concentration of 30 mg/L, an adsorbent dose of 2 g and contact time of 120min and at room temperature).

The availability of low- cost adsorbent namely Al-Khriet ( a substance found in the legs of Typha  Domingensis) as an agricultural waste material, for the removal of lead and cadmium from aqueous solution was investigated. In the batch tests experimental parameters were studied, including adsorbent dosage between (0.2-1) g, initial metal ions concentration between (50-200) ppm (single and binary) and contact time (1/2-6) h. The removal percentage of each ion onto Al-Khriet reached equilibrium in about 4 hours. The highest adsorption capacity was for lead (96%) while for cadmium it was (90%) with 50 ppm ions concentration, 1 g dosage of adsorbent and pH 5.5. Adsorption capacity in the binary mixture were reduce at about 8% for lead a

Spent catalysts for sulfuric acid production have large amount of vanadium and due to environmental authority it is required to reduce the vanadium contain of the spent catalyst. Experimental investigation was conducted to study the vanadium recovery from spent catalyst via leaching process using sodium hydroxide to study the effect of process variables (temperatures, sodium hydroxide molarities, leaching time and particle size) on vanadium recovery. The effect of process variables (temperature, particle size,molarities of sodium hydroxide and leaching time) on the percentages of vanadium recovery were investigated and discussed .It was found that the percentage of vanadium recovery increased with increasing temperature up to 100 , incre

The research aims to identify the possibility of applying environmental fines to commercial shops and restaurants to reduce the environmental pollution represented by the wastes generated from them. The research sample was divided into two groups, including the first (20) commercial shops (meat shops and slaughter it, fruits & vegetables, legumes and accessories) and second (30) Restaurant in the city of Baghdad on both sides of Karkh and Rusafa. The quality of the waste was classified into carton, plastic, aluminum, glass, paper, cork and food waste. The study revealed the possibility of applying environmental fines to restaurants and shops to reduce the waste generated from them throughout the year and to apply continuous monitorin

Abstract

 Metal cutting processes still represent the largest class of manufacturing operations. Turning is the most commonly employed material removal process. This research focuses on analysis of the thermal field of the oblique machining process. Finite element method (FEM) software DEFORM 3D V10.2 was used together with experimental work carried out using infrared image equipment, which include both hardware and software simulations. The thermal experiments are conducted with AA6063-T6, using different tool obliquity, cutting speeds and feed rates. The results show that the temperature relatively decreased when tool obliquity increases at different cutting speeds and feed rates, also it

Nano γ-Al₂O₃ support was prepared by co-precipitation method by using different calcination temperatures (550, 600, and 750) ^oC. Then nano NiMo/γ-Al₂O₃ catalyst was prepared by impregnation method were nickel carbonate (source of Ni) and ammonium paramolybdate (source of Mo) on the best prepared nano γ-Al₂O₃ support at calcination temperature 550 ^oC. Make the characterizations for prepared nano γ-Al₂O₃ support at different temperatures and for nano NiMo/γ-Al₂O₃ catalyst like X-ray diffraction, X-ray fluorescent, AFM, SEM, BET surface area, and pore volume.

The N