In this work, the characterization and application of thin films composite incorporated titanium dioxide (TiO₂) (0.8)% volume ratio for (Rutile) nanostructure with poly [2- methoxy-5-(2’-ethylhexoxy-p-phenylene vinylene] (MEH-PPV) were deposited by a spin-coating technique. The optical properties for deposited (MEH-PPV/TiO₂) nanocomposite thin films have two peaks which are the Q-band in the visible region and B-band in ultraviolet. This study shows that the absorption spectrum of organic polymer mixing with TiO₂ increased with increasing the volume ratios TiO₂. The I-V characteristic of nanocomposite thin films shows that the current at dark and light condition

Poly [2-methoxy-5-(2-ethylhexyloxy)-1, 4-phenylenevinyl] (MEH-PPV) thin films were created in this study using both spin coating and drop casting processes. MEH-PPV thin films generated by Ferric Chloride (FeCl3) doping (0.03, 0.06, 0.09, and 0.12 wt%) were studied for some physical features using Fourier-Transform Infrared Spectroscopy (FTIR), Field Emission Scanning Electron Microscopy (FE-SEM), and Energy Dispersive X-ray Spectroscopy (EDX). An FTIR test showed that there was no chemical reaction that occurred between Ferric Chloride (FeCl3) and MEH-PPV, but rather a physical one, that is, an organic material composite occurred. As for FE-SEM, the pure sample MEH-PPV formed uniformly, but when FeCl3 was added by weight, we have differ

Organic light emitting diodes (OLEDs) were fabricated containing host molecule of conjugated polymer MEH-PPV poly (2-methoxy-5-(2'-ethylhexyloxy)-1,4-phenlenevinylene) which was dissolved in chloroform solvent and doped with guest molecules MWCNTs that were dissolved in DMF solvent with different volume ratios 0.05 and 0.15, nanocomposite system which acts as active layer in OLEDs device. The Poly(3,4-ethylenedioxythiophene):poly-(styrenesulfonate) "PEDOT:PSS" and Tris98-hydroxyquinoline) aluminum "Alq3" as hole transport layer HTL and electron transport layer ETL were used respectively, to enhanced the injection charge from the electrodes to the active layer. Spin coating method used for achieving facile and low cost OLED. The absorption s

     In this work proton exchange membranes were prepared by a modified microwave casting solution technique, using the polymers blend (polyethersulfone (PES), polystyrene (PS), polyvinylidenefluride (PVDF)). Modified casting method was used to overcome the poor compatibility between hydrophilic, (PES, PS) and hydrophobic PVDF, by cooling the substrate during the film casting process to (4.5-5.5^oC). Membranes were chemically modified by three reaction types to study the differences between their effects on the required properties for microbial fuel cell application. These methods use blend organic sulfonic acid precasting process and sulfonation by sulfuric acid post-casting process (APS), blending organic

      Layer by layer development two features of pulsed laser deposition PLD, with a high kinetic energy and sharp instantaneous deposition rating. Layered films of polymer/metal/ceramic nanocomposites consisting of polystyrene PS(as substrate) , tin Sn and cadmium oxide CdO were deposited by PLD. Structure for layered samples were measured  by XRD X ray diffraction, there were appearance of peaks  which reflected  to formation of new compounds result of  reaction between layers. Particles size  was calculated using two methods and it give nanoscale. Microstrain was also calculated  and exhibited  high value (0.01) for sample p/m.

In this work we present a detailed study on anisotype nGe-pSi heterojunction (HJ) used as photodetector in the wavelength range (500-1100 nm). I-V characteristics in the dark and under illumination, C-V characteristics, minority carriers lifetime (MCLT), spectral responsivity, field of view, and linearity were investigated at 300K. The results showed that the detector has maximum spectral responsivity at λ=950 nm. The photo-induced open circuit voltage decay results revealed that the MCLT of HJ was around 14.4 μs

This research including, CO3O4 was prepared by the chemical spry pyrolysis, deposited film acceptable to assess film properties and applications as photodetector devise, studying the optical and optoelectronics properties of Cobalt Oxide and effect of different doping ratios with Br (2, 5, 8)%. the optical energy gap for direct transition were evaluated and it decreases as the percentage Br increase, Hall measurements showed that all the films are p-type, the current–voltage characteristic of Br:CO3O4 /Si Heterojunction show change forward current at dark varies with applied voltage, high spectral response, specific detectivity and quantum efficiency of CO3O4 /Si detector with 8% of Br ,was deliberate, extreme value with 673nm.