In this study, the photodegradation of Congo red dye (CR) in aqueous solution was investigated using Au-Pd/TiO₂ as photocatalyst. The concentration of dye, dosage of photocatalyst, amount of H₂O₂, pH of the medium and temperature were examined to find the optimum values of these parameters. It has been found that 28 ppm was the best dye concentration. The optimum amount of photocatalyst was 0.09 g/75 mL of dye solution when the degradation percent was ~ 96 % after irradiation time of 12 hours, while the best amount of hydrogen peroxide was 7μl/75 mL of dye solution at degradation percent ~97 % after irradiation time of 10 hours, whereas pH 5 was the best value to carry out the reaction at the highest deg

Complexes of Au(III) ,Pd (II) , Pt (IV ) and Rh(III) with S – propynyle -2- thiobenzimidazole (BENZA) have been prepared and characterized by IR and UV- Visible spectral methods in addition to magnetic and conductivity measurements and micro – elemental analysis (CHN).The probable structures of the new complexes have been suggested.

     Bimetallic Au –Pt catalysts supporting TiO₂ were synthesised using two methods; sol immobilization and impregnation methods. The prepared catalyst underwent a thermal treatment process at 400^◦ C, while the reduction reaction under the same condition was done and the obtained catalysts were identified with transmission electron microscopy (TEM) and energy-dispersive spectroscopy (EDS). It has been found that the prepared catalysts have a dimension around 2.5 nm and the particles have uniform orders leading to high dispersion of platinum molecules .The prepared catalysts have been examined as efficient photocatalysts to degrade the Crystal violet dye under UV-light. The optimum values of Bimetallic Au –

Photocatalyst composed of core/shell magnetic zincoxysulfide nanocomposite coated with sulfonated polyindole ([email protected]/SPID) has been prepared and used for simultaneous photocatalytic H2 production and Bisphenol A (BPA) degradation. XRD, FE-SEM, EDX, BET surface area, UV-vis DRS and VSM were used to characterize the synthesized nanocomposites. The photocatalytic performance was evaluated using batch reactor under visible light irradiation. The photocatalytic activity of [email protected]/SPID nanocomposite was revealed to exceed that of [email protected] nanocomposite due to the heterojunctions between SPID and [email protected] species. The results exhibited that the effect of BPA initial concentration was found to be effectual on the improvement

This work is related to the investigation of the effects of porous silicon (PSi) morphologies on the performance of plasmonic gold nanoparticles (Au-NPs) hot spot SERS sensors for the detection of amoxicillin molecules. Two Si wafers with different resistivity values of 10 and 100 Ω.cm were used to synthesize a PSi layer of pores- and mud-like structures, respectively, by pulsed photo chemical etching process. The hot spot SERS sensors were synthesized by incorporating the Au-NPs within the PSi morphologies of pores- and mud- like structures which are characterized by high density of nucleation sites. Plasmonic Au- NPs with different sizes and hot spot regions were incorporated into the porous structures by the ion reduction proces

2-benzamide benzothiazole complexes of Pd(II) , Pt(IV) and Au(III) ions were prepared by microwave assisted radiation. The ligand and the complexes were isolated and characterized in solid state by using FT-IR, UV-Vis spectroscopy, flame atomic absorption, elemental analysis CHNS , magnetic susceptibility measurements , melting points and conductivity measurements. The nature of complexes in liquid state was studied by following the molar ratio method which gave results approximately identical to those obtained from isolated solid state; also, stability constant of the prepared complexes were studied and found that they were stable in molar ratio 1:1.The complexes have a sequar planner geometry except Pt(IV) complex has octahedral .

 In research we prepared electrical conductive polymer mixture wich consisted of three polymers [pectin, poly vinyl acetate and poly Aniline] was prepared then doping silver nanoparticles. Meaning it was conducting research on the three stages the first is  Preparing triple polymer blend , Preparing silver nanoparticles and Tchoub mix triple Article nanoparticles in different proportions to get (Nanopolymer composites), and Preparing and making chips complexes in (casting method) for the purpose of measuring electrical conductivity her. Also we examined samples spectrum infrared (FT-IR), X-ray diffraction), SEM microscope and atomic force microscopy AFM. Electrical conductivity of the device chips have been measured (LCR) resul

The reclamation of makeup water is studied in terms of breakthrough time (i.e., the leakage of the cations). Makeup water was subjected to lab-scale ion exchangers of two types: strong acid cation and weak base anion exchanger. The experimental investigation was directed to study the ion exchanger performance in terms of four different parameters (i.e., copper concentration, total dissolved solids (TDS), feed rate and bed depth). Box-Wilson composite rotatable design was adopted in designing the experiments. Breakthrough times of the effluent stream are measured in terms of copper concentration of 2 to 25 ppm, TDS concentration of 250 to 1250 ppm, feed rate of 0.38 to 5.34 l/h and bed depth of 5 to 70 cm. Simulation the effect of the stu

In this study, a new Azo ligand 5-((2-(1H-indol-2-yl)ethyl)diazinyl)-2-aminophenol is synthesized from a reaction of Tryptamine with 2-aminophenol. The ligand and their metal ion complexes Ni(II), Pd(II) , Pt(IV) and Au(III) have been synthesized and characterized by various analytical techniques, including elemental microanalysis, metal content, chloride-containing, measurement of electrical conductivity, magnetic susceptibility, ¹H and ¹³C-NMR, FT-IR, UV-Vis, mass spectra (MS), and thermal analysis (TGA and DSC) curves. The DCS curve was used to calculate the thermodynamic parameters ΔH, ΔS, and ΔG. The characterization results promote the metal complexes of azo ligand structures. The results indicate that the