An experiment was conducted in the Date Palm Research Units labs / College of Agricultural Engineering Sciences / University of Baghdad to assess the tolerance toward salinity stress in potato after two mutagens treatments in vitro. Potato cv. Arizona and Rivera nodal segments were irradiated with four dosages of gamma rays at 0, 10, 20, and 30 Gray and immersed in (EMS) with four concentrations included 0, 10, 20, and 30 mM. The survival rates after mutagenesis treatments were calculated and 449 lines were obtained. The lines were tested for salinity tolerance by growing in MS medium supplemented with four concentrations of NaCl at 0, 100, 150, and 200 mM and data were analyzed according to the CRD with 10 replicates and means were

      The activity concentration of natural radioactivity levels, of artificial cesium and transfer factor from soil to plants in agricultural areas at Al- Yusiefya region were determined by using NaI (Tl) detector spectrometer. Ten species of leafy plants have been selected: Spinach, Parsley, Watercress, Lettuce, Rashad, Radish, Green onion, Turnip green, Green beet and Mint. The mean activity concentrations of ²³⁸U, ²³²Th, ⁴⁰K and ¹³⁷Cs in leafy vegetable samples were  12.4±3.8, 14.8±4.7, 283±93 and 1.06±0.99  Bg/kg, and in soil samples were 15.9±4.3, 16.1±5.2, 298.5±3.9, and 1.11±0.37 Bq/kg. The radiation hazard indices were evaluated (radium

The effect of 0.662MeV gamma radiation on the optical properties of the CdTe thin films was studied. 300nm thickness of CdTe samples were irradiated with doses (10, 20, 30,60krad) in room temperature. The absorption spectra for all the samples were recorded using UV- Visible spectrometer in order to calculate the energy gap, width of localized states and optical constants(refractive index, extinction coefficient, real and imaginary parts of dielectric constant). The optical energy gap was found to decrease from (1.53 to 1.48 eV), while the width of localized states increased from (1.34 to 1.49 eV) with the increasing of radiation dose. The behavior of energy gap with the irradiation dose makes the material a good candidate for dosimetry

Positron annihilation lifetime has been utilized for the first time to investigate the free - volume hole properties in thermolumenscent dosimeter ( TLD ) as a function of gamma-dosc . The hole volume, free volume fraction determined form orthopsitronium lifetime are found to be ?lamatically increase to large values , and then to minimum values as a function ofgamma-dose . The free - volume holes size is found to be 0.163nm’ and to have maximum of 0.166nm^ at the gamma-dose of 0.1 and 0.8 Gy, respectively-

I n vitro rooting plantlets of three sugarcane genotypes(Co.j.64, Co.j.86 and Missan) were cultured in the field after exposed at different doses of gamma rays (1,2,3,4,) kr. Data of reduction percentage on vegetative growth, roots number, length per plant and their diameter were investigated. Results showed gradual reductions in number of shoots, length and diameter as according to increasing of gamma doses. The reduction percentage in shoot number, length were reached 57.86,70.36 % at 4 kr respectively which have mean number and length per plant reached (9.27 and 55.33 cm) as compared with the control treatment ,While 1 kr caused higher percent in diameter reached 9.69 % with mean of diameter per plant reached 2.57 cm. Mean time , Ge

The creation and characterisation of biodegradable blend films based on chitosan and polyvinyl alcohol for application in a range of packaging is described. The compatibility between the chitosan and PVA polymers was good. Composite films had a compact and homogeneous structure, according to the morphology analysis. The mechanical test result of PVA/CH at concentrations 5% showed, that The higher values of TS recorded in sample (p1, with 40 MPa) while the lower values appeared in sample (p9, with 22.09 MPa), the TS decreased gradually as the amount of PVA increased in blend film. While the blend film of pure Chitosan exhibits a poor mechanical strength which makes it a poor candidate for packaging but Blending CH with PVA together improved

In this study, tin oxide (SnO2) and mixed with cadmium oxide (CdO) with concentration ratio of (5, 10, 15, 20)% films were deposited by spray pyrolysis technique onto glass substrates at 300ºC temperature. The structure of the SnO2:CdO mixed films have polycrystalline structure with (110) and (101) preferential orientations. Atomic force microscopy (AFM) show the films are displayed granular structure. It was found that the grain size increases with increasing of mixed concentration ratio. The transmittance in visible and NIR region was estimated for SnO2:CdO mixed films. Direct optical band gap was estimated for SnO2 and SnO2 mixed CdO and show a decrease in the energy gap with increasing mixing ratio. From Hall measurement, it was fou