Moisture damage is described as a reduction in stiffness and strength durability in asphalt mixtures due to moisture. This study investigated the influence of adding nano silica (NS) to the Asphalt on the moisture susceptibility of hot-mix-asphalt (HMA) mixtures under different aging conditions. NS was mixed with asphalt binder at concentrations of 2%, 4%, and 6% by weight of the binder. To detect the microstructure changes of modified Asphalt and estimate the dispersion of NS within the Asphalt, the field emission scanning electron microscope (FE-SEM) was used. To examine the performance of Asphalt mixed with NS at different aging stages (short-term and long-term aging), asphalt mixture tests such as Marshall stability,

This work has been done to prepare a series of new alkene compounds derived from 4-thiozolidinones by substituting different aldehydes, P-acetamido-phenol, and 2-mercapto-benzoimidazole, which were used as starting materials to form ester [I]a,b and then make hydrazides [II]a,b, which were used to prepare 1, 3, and 4-oxadiazoles [III]a,b, which were then used for prepared Schiff bases [IV]a-f, The next step was the synthesis of 4-thiazoldinone derivatives [V]a-f  from Schiff bases. The final step was the synthesis of alkenes [VII]a-f, the prepared derivatives were identified with spectral methods (FT-IR, 1H-NMR, mass, and CHNS). The antibacterial activity of the prepared derivatives was evaluated against four types of bacteria, pos

Background: In spite of all efforts, Non-small cell lung cancer (NSCLC) is a fatal solid tumor with a poor prognosis as of its high metastasis and resistance to present treatments. Tyrosine kinase inhibitors (TKI) such as erlotinib are efficient in treating NSCLC but the emergence of chemoresistance and adverse effects substantially limits their single use. Objective: in this study, the combination treatments of either 2-deoxy-D-glucose (2DG) or cinnamic acid (CINN) with erlotinib (ERL) were tested for their possible synergistic effect on the proliferation and migration capacity of NSCLC cells. Methods: In this study, NSCLC model cell line A549 was used to investigate the effects of single compounds and their combination on cell gro

Zinc Oxide nanoparticles were prepared using pulsed laser ablation process from a pure zinc metal placed inside a liquid environment. The latter is composed of acetyltrimethylammonium bromide (CTAB) of 10−3 molarity and distilled water. A Ti:Sapphire laser of 800 nm wavelength, 1 kHz pulse repetition rate, 130 fs pulse duration is used at three values of pulse energies of 0.05 mJ, 1.11 mJ and 1.15 mJ. The evaluation of the optical properties for the obtained suspension was applied through ultraviolet–visible absorption spectroscopy test (UV/VIS). The result showed peak wavelengths at 210 nm, 211 nm and 213 nm for the three used pulse energies 0.05 mJ, 1.11 mJ and 1.15 mJ respectively. This indicates a blue shift,

Pseudomonas aerogenosa lipopolysaccharidewas extracted by hot phenol method and purified by gel filtration method using the Sephadex G-200 gel and detected by the limulus amebocyt lysate (EU/ml 0.03)(Wako Chemicals USA, Inc.). The inhibitory effect of partially purified LPS on Candida glabrata yeast was studied in a microdilution method. This study found that LPS has an inhibitory effect on Candida glabrata with the lower concentrations. The inhibitory effect of LPS which treated with heating was studied under boiling and wet heat effect. The toxicity of LPS on Candida glabrata was not affected when treated with heating LPS and the results were similar to those found in untreated LPS

In this study, the photodegradation of Congo red dye (CR) in aqueous solution was investigated using Au-Pd/TiO2 as photocatalyst. The concentration of dye, dosage of photocatalyst, amount of H2O2, pH of the medium and temperature were examined to find the optimum values of these parameters. It has been found that 28 ppm was the best dye concentration. The optimum amount of photocatalyst was 0.09 g/75 mL of dye solution when the degradation percent was ~ 96 % after irradiation time of 12 hours, while the best amount of hydrogen peroxide was 7μl/75 mL of dye solution at degradation percent ~97 % after irradiation time of 10 hours, whereas pH 5 was the best value to carry out the reaction at the highest degradation percent. In additio