Premature degradation is the problem of maxillofacial silicones, significantly affected by ultraviolet exposure, contributing to silicones photodegradation. Degradation necessitates frequent replacement of prostheses that increase the total cost of rehabilitation.

In this research, the study effect of irradiation on structural and optical properties of thin film (CdO) by spray pyrolysis method, which deposited on glasses substrates at a thickness of (350±20)nm , The flow rate of solution was 5 ml/min and the substrate temperature was held constant at 400˚C.The investigation of (XRD) indicates that the (CdO) films are polycrystalline and type of cubic. The results of the measuring of each sample from grain size, micro strain, dislocation density and number of crystals the grain size decreasing after irradiation with gamma ray from(27.41, 26.29 ,23.63)nm . The absorbance and transmittance spectra have been recorded in the wavelength range (300-1100) nm in order to study the optical properties. the op

An oxidative polymerization approach was used to create polyaniline (PANI) and Fe₂O₃ /PANI nanoparticle combination. Various characterization approaches were used to investigate the structural, morphological, and Fe₂O₃ /PANI nanoparticle structures. The findings support the synthesis of polycrystalline nanoparticle PANI and Fe₂O₃ /PANI spherical nanoparticle composites. Gram-positive bacteria are tested for antibacterial activity. Various quantities of Nanoparticles of PANI and Fe₂O₃ /PANI nanoparticle composites were used to test Staph-aureus and gram-negative bacteria, E-coli, and candida species. PANI has antibacterial properties against all microo

Mechanical and thermal properties of composites, consisted of unsaturated polyester resin, reinforced by different kinds of natural materials (Orange peels and Date seeds) and industrial materials (carbon and silica) with particle size 98 µm were studied. Various weight ratios, 5, 10, and 15 wt. % of natural and industrial materials have been infused into polyester. Tensile, three-point bending and thermal conductivity tests were conducted for the unfilled polyester, natural and industrial composite to identify the weight ratio effect on the properties of materials. The results indicated that when the weight ratio for polyester with date seeds increased from 10% to 15%, the maximum Young’s modulus decreased by 54%. When the weight rat

                 The research deals with the concept of a New Urbanism as an urban development strategy in the suburbs of cities or in its centers that are affected by pedestrian-oriented design and the possibility of walking, as well as integrating economic classes through the diversity of housing and its costs, and this works to facilitate access to jobs and services while providing more diverse neighborhoods and reducing the use of cars , As designing separate houses in the suburbs and increasing car trips poses a threat to the environment and the quality of urban life, and thus the new urban provides a good strategy for developing

Iraqi kaolin was used for the preparation and characterization of NaY zeolite for biodiesel production via esterification reaction. Oleic acid was used usually as a typical simulated feedstock of high acid number for the esterification reaction.

   The chemical composition for the prepared Nay zeolite is as following:  (Ca₂.6Na₁.K_0.1)(Al₆.3Si₁₇.₇)O₄₈.16H₂O, the silica to alumina ratio in the prepared catalyst was found equal to 2.6 and Na₂O content was 12.26 wt. %, with relative crystallinity equal to 147.4 % obtained by the X-ray diffraction. The surface area result shows that the prepared catalyst has 330 m²

In this work, silver (Ag) self-metallization on a polyimide (PI) film was prepared through autocatalytic plating. PI films were prepared through the solution casting method, followed by etching with potassium hydroxide (KOH) solution, sensitization with tin chloride (SnCl₂), and the use of palladium chloride (PdCl₂) to activate the surface of PI. Energy-dispersive X-ray analysis (EDX) showed the highest peak in the (Ag) region and confirmed the presence of AgNPs. The diffraction peaks at 2θ = 38.2^°, 44.5^°, 64.6^°, and 78.2^° represented the 111, 200, 220, and 311 planes of Ag, respectively. The FT–IR an