Copper oxide thin films were deposited on glass substrate using Successive Ionic Layer Adsorption and Reaction (SILAR) method at room temperature. The thickness of the thin films was around 0.43?m.Copper oxide thin films were annealed in air at (200, 300 and 400°C for 45min.The film structure properties were characterized by x-ray diffraction (XRD). XRD patterns indicated the presence of polycrystalline CuO. The average grain size is calculated from the X-rays pattern, it is found that the grain size increased with increasing annealing temperature. Optical transmitter microscope (OTM) and atomic force microscope (AFM) was also used. Direct band gap values of 2.2 eV for an annealed sample and (2, 1.5, 1.4) eV at 200, 300,400oC respect

In this study, new oxazolidinone and thiazolidinone derivatives were synthesized through a three-step process. In the first step, o-aminothiophenol was reacted with p-aminobenzoic acid in hydrochloric acid to produce an amine containing a thiazole ring, achieving a product yield of 80%. The second step involves synthesizing Schiff bases (E1-E4) by reacting 4-(benzo[d]thiazol-2-yl)aniline with various aromatic aldehydes in the presence of glacial acetic acid. This reaction yields products of 76% to 90%. In the third step, the Schiff derivatives (E1-E4) are reacted with glycolic acid and thioglycolic acid to obtain the desired products. Oxazolidinone derivatives (N1-T1) were produced with rates ranging from 66% to 74%, while thiazolidin

Objective: To diagnose the function of natural biomolecules in the biological reduction of metal salts during nanoparticle synthesis.Study Design: Experimental studyPlace and Duration of Study: This study was conducted at the College of Education for Pure Sciences/Ibn Al- Haitham at the University of Baghdad from 1st January 2024 to 31st March 2025. Methods: Capsicum plant extract was used and treated with a readily available inorganic salt (CaSO4 2H2O). It was used as a basic material to obtain particles.Results: Calcium peroxide nanoparticles in the form of a yellowish-white powder were confirmed by using, UV, XRD, SEM, TEM, AFM, and EDX, confirmed that the compound is calcium peroxide nanoparticles with an average nano size of 31

Polyaniline Multi walled Carbon nanotubes (PANI/MWCNTs) nanocomposite thin films have been prepared by non-equilibrium atmospheric pressure plasma jet on glass substrate with different weight percentage of MWCNTs 1, 2, 3, 4%. The diameter of the MWCNTs was in the range of 8-55 nm and length - - 55 55 μm. the nanocomposite thin films were characterized by UV-VIS, XRD, FTIR, and SEM. The optical studies show that the energy band gap of PANI/MWCNTs nanocomposites thin films will be different according to the MWCNTs polyaniline concentration. The XRD pattern indicates that the synthesized PANI/MWCNTs nanocomposite is amorphous. FTIR reveals the presence of MWCNTs nanoparticle embedded into polyaniline. SEM surface images show that the MWCNT

Objective: To diagnose the function of natural biomolecules in the biological reduction of metal salts during nanoparticle synthesis.Study Design: Experimental studyPlace and Duration of Study: This study was conducted at the College of Education for Pure Sciences/Ibn Al- Haitham at the University of Baghdad from 1st January 2024 to 31st March 2025. Methods: Capsicum plant extract was used and treated with a readily available inorganic salt (CaSO4 2H2O). It was used as a basic material to obtain particles.Results: Calcium peroxide nanoparticles in the form of a yellowish-white powder were confirmed by using, UV, XRD, SEM, TEM, AFM, and EDX, confirmed that the compound is calcium peroxide nanoparticles with an average nano size of 31

The electrical properties of pure NiO and NiO:Au Films which are
deposited on glass substrate with various dopant concentrations
(1wt.%, 2wt%, 3wt.% and 4wt.%) at room temperature 450 Co
annealing temperature will be presented. The results of the hall effect
showed that all the films were p-type. The Hall mobility decreases
while both carrier concentration and conductivity increases with the
increasing of annealing temperatures and doping percentage, Thus,
indicating the behavior of semiconductor, and also the D.C
conductivity from which the activation energy decrease with the
doping concentration increase and transport mechanism of the charge
carriers can be estimated.

Cu X Zn1-XO films with different x content have been prepared by
pulse laser deposition technique at room temperatures (RT) and
different annealing temperatures (373 and 473) K. The effect of x
content of Cu (0, 0.2, 0.4, 0.6, 0.8) wt.% on morphology and
electrical properties of CuXZn1-XO thin films have been studied.
AFM measurements showed that the average grain size values for
CuXZn1-xO thin films at RT and different annealing temperatures
(373, 473) K decreases, while the average Roughness values increase
with increasing x content. The D.C conductivity for all films
increases as the x content increase and decreases with increasing the
annealing temperatures. Hall measurements showed that there are
two