Thick films of poly(vinyl chloride)(PVC)& PVC doped with Zn(etx)2 salt complex have been prepared by cast method with fixed thickness almost (120±5) Microns. Optical studies were carried out in the wavelengths region(200-900)nm based on absorption & transmition measurement. Optical parameters such as absorption coefficient(?) ,refraction index(n) and extinction coefficient(K) were observed to be effected by adding the dopant.Electrical parameters such as real(?)& imaginary(?) part of dielectric constant were also calculated part of dielectric constant were also calculated from the optical parameters using Maxwell equation.

The photostabilization? of poly vinyl chloride (PVC) ? films has been investigated by using diamine derivatives. The? (PVC) films were? contained 0.5% weight? of diamine derivatives which prepared by the method of casting. The photostabilizations? ?of these compounds were determined by monitoring the carbonyl index value with irradiation time. Also, the effect ?of concentrations of additives (range 0.1-0.5wt) on the rate of photostabilization? process was studied. Therefore we found? that a increased photostabilization rates was increase with increasing? concentrations of compound. Besides, the influence? on film thickness? of photostabilization process was also studied; ?and the results? showed that? the increasing of film thickness incr

The Rate theory of crack growth in PVC pipe has been studied for creep and fatigue crack propagation. Rate theory function parameters, (RTFP), were estimated theoretically from exponential function parameters, (EFP), to experimental data of crack velocity versus stress intensity factor ,(V-K) diagram, to creep crack propagation . Also (RTFP) were estimated theoretically from (EFP) to experimental data of (V-?K) diagram to fatigue crack propagation. Temperature effect with (RTFP) was discussed. Crack velocity function denoted with stress intensity factor and temperature degrees has been determined to fatigue and creep crack propagation theoretically and comparative results this function with experimental data of (V-K or ?K) diagram .

Theligand4-[5-(2-hydoxy-phenyl)- [1,3,4- thiadiazole-2- ylimino methyl]-1,5-dimethyl -2-phenyl-1,2-dihydro-pyrazol-3-one [HL1] is prepared and characterized. It is reacted with poly(vinyl chloride) (PVC) in THF to form the PVC-L compounds ,PVC-L interacted with ions of transition metals to form PVC-L-MII complexes .All prepared compounds are characterized by FTIR spectroscopy, u.v-visible spectroscopy, C.H.N.S. analysis and some of them by 1HNMR

Poly vinyl alcohol has been studied for its ability to form crystallites by using annealing method. Semicrystalline films of poly vinyl alcohol (PVA) were prepared by casting 11.5 wt. % and 13 wt. % PVA aqueous solution onto glass slides at annealing temperature range 90 -120°C and duration time 15- 60 minute. This allowed the macromolecules to form crystallites, small regions of folded and compacted chains separated by amorphous regions where single PVA chain may pass through several of these crystallites. Degree of crystallinity of PVA films (hydrogels) was determined by method of density; on the other hand the swelling behavior was conducted by the determination of water uptake, wet degree of crystallinity, gel fraction and solubilit

Three new polyphosphates were synthesized in good yields by reacting diethylenetriamine with the appropriate phosphate ester in ethanol under acidic conditions. The polyphosphate structures were determined using FT-IR and 1H-NMR spectroscopies, and their elemental compositions were confirmed by EDX spectroscopy. Polyphosphates were added to poly(vinyl chloride) (PVC) at low concentrations to fabricate thin films. The PVC films were irradiated with ultraviolet light for long periods, and the effect of polyphosphates as the photostabilizer was investigated by determining changes in the infrared spectra (intensity of specific functional group peaks), reduction in molecular weight, weight loss, and surface morphology. Minimal changes we

Three N-(hydroxylphenyl) dimethylmaleimides were directly prepared in good yields (81-86)% from the reaction of dimethylmaleic anhydride with amino phenols. The prepared imides were esterified to the corresponding benzoates, methacrylates and cinnamates via their reaction with different acid chlorides in the presence of triethylamine. The prepared esters were tested as plasticizers for PVC via preparing of thirty six samples of PVC with the prepared esters in certain weight ratio followed by recording their softening points. Comparison the results with the universal plasticizers for PVC (DOP) and (DBP) indicated that the prepared esters in general have high plasticizing efficiency.

New polymers were prepared from a monomer (5-vinyl-1H-tetrazole), which was prepared from acrylonitrile with sodium azide in the presence of ZnCl2.Another monomer (Methyl acrylate) was also used. Co-monomers were polymerized usingBPO as initiator. The second step was the preparation of copoly acid hydrazide from the reaction of compound2 with hydrazine hydrate, followed by the reaction with carbon disulphide in the presence of KOH to obtain copoly (5-subs.-2-mercapto-1,3,4-thiadiazole). Next,compound4 was reacted with chloroacetyl chloride to yield compound4 5 which was reacted with (hydrazine hydrate , phenyl hydrazine and 2,4-di nitro phenyl hydrazine) as shown in scheme(1). Physical properties of all the prepared copolymers were chara