The synthesis of zeolite NaX from locally available kaolin has been studied. The operating conditions for zeolite NaX production from kaolin with good crystallinity were as follows; a gel formation step of metakaolin in alkaline medium in presence of additional silica to crystallize the zeolite was achieved at 60 oC for 1 hr,and with stirring. In ageing step of the reactants at room temperature for 5 days and crystallization step at 87±2 oC for 24 hr. The catalytic activity of catalyst prepared from local kaolin was studied by using cumene cracking as a model for catalytic cracking and compared with standard HY zeolite and HX zeolite catalysts. The activity test was carried out in a laboratory continuous flow unit with fixed bed reactor

Condensation of 1,2- dibromo ethane with para hydroxy benzoic acid gave 1,2-Ethane-bis- 4-oxybenzoic [1]. This Compound was converted with the thionyl chloride to give 1,2-Ethane-bis- 4-oxybenzoyl chloride [2]. Reaction of compound [2] with thiosemicarbizades gave 1,2-Ethanebis[4-oxybenzoyl-thiosemicarbazide] [3] and opteined 1,2-Ethane-bis[3-mercapto-5-phenoxy- 1,2,4-triazole] [4] from treatment compound [3] with NaOH (4%) .The new compounds 1,2- Ethane-bis[3-(substituted thioacyl)-4-(substituted acyl)-5 phenoxy-1,2,4-triazole] [5a-d] and 1,2- Ethane-bis[3-(substituted alkylthio)-5 phenoxy-1,2,4-trizole] [5e-f] derived from compound [4] were synthesized and characterized by physical and spectral data. All the compounds [4], [5a-d] and [5e-

Synthesis and study liquid crystalline properties of new compounds with terminal groups of amides ([III]a-c,[IV]a-c and [VI]n), alkoxy series[V]n or ester with azo linkage ([IX]a-c and[X]a-c) containing thaizole ring. These series were synthesized by many steps starting from 4- hydroxyacetophenone or 4-aminoacetophenone. The synthesized compounds were characterized using melting points, FTIR, C.H.N.S analysis and for some of them 1H NMR spectroscopy. The liquid crystalline properties were studied by hot stage polarizing microscopy and differential scanning calorimetry DSC. All compounds of series [III]a-c,[IV]a-c and compounds [V]n showed enantiotropic liquid crystal. While the series [VI]n showed nematic mesomorphism except [VI]8 did not s

Four complexes of Co(II),Ni(II),Cu(II) and Zn(II) with the azo ligand (4-chloro-N-(2-(dimethylamino)ethyl)-5-((2-hydroxy- 4,6-dimethylphenol)diazenyl)-2-methoxybenzamide) L. The structure of ligand and complexes were confirmed on the basis of their analytical and spectral data, these dyes were tested as dyeing in cotton fabric, and also testing in light and cleaner firmness. Also, antimicrobial and antifungal activities of ligand and their complexes were evaluated and the results showed that the ZnL compound showed the higher antibacterial activity with inhibition zone of 13mm against Staphyloco-ccus epidermidis, Steptococcus sp. and Escherichia coli compared with ligand and other metal complexes .In case of ZnL compound the antifungal acti

Four complexes of Co(II),Ni(II),Cu(II) and Zn(II) with the azo ligand (4-chloro-N-(2-(dimethylamino)ethyl)-5-((2-hydroxy-4,6-dimethylphenol)diazenyl)-2-methoxybenzamide) L. The structure of ligand and complexes were confirmed on the basis of their analytical and spectral data, these dyes were tested as dyeing in cotton fabric, and also testing in light and cleaner firmness. Also, antimicrobial and antifungal activities of ligand and their complexes were evaluated and the results showed that the ZnL compound showed the higher antibacterial activity with inhibition zone of 13mm against Staphyloco-ccus epidermidis, Steptococcus sp. and Escherichia coli compared with ligand and other metal complexes .In case of ZnL compound the antifungal activ

This paper concerns is the preparation and characterization of a bidentate ligand [4-(5,5- dimethyl-3-oxocyclohex-1-enylamino)-N-(5-methylisoxazol-3-yl) benzene sulfonamide]. The ligand was prepared from fusing of sulfamethoxazole and dimedone at (140) ºC for half hour. The complex was prepared by refluxing the ligand with a bivalent cobalt ion using ethanol as a solvent. The prepared ligand and complex were identified using Spectroscopic methods. The proposed tetrahedral geometry around the metal ions studied were concluded from these measurements. Both molar ratio and continuous variation method were studied to determine metal to ligand ratio (M:L). The M to L ratio was found to be (1:1). The adsorption of cobalt complex was carried out

Abstract. In this work, Bi2O3 was deposited as a thin film of different thickness (400, 500, and 600 ±20 nm) by using thermal oxidation at 573 K with ambient oxygen of evaporated bismuth (Bi) thin films in a vacuum on glass substrate and on Si wafer to produce n-Bi2O3/p-Si heterojunction. The effect of thickness on the structural, electrical, surface and optical properties of Bi2O3 thin films was studied. XRD analysis reveals that all the as deposited Bi2O3 films show polycrystalline tetragonal structure, with preferential orientation in the (201) direction, without any change in structure due to increase of film thickness. AFM and SEM images are used to investigate the influences of film thickness on surface properties. The optical measur