The study involved the removal of acidity from free fatty acid via the esterification reaction of oleic acid with ethanol. The reaction was done in a batch reactor using commercial 13X zeolite as a catalyst. The effects of temperatures (40 to 70 °C) and reaction time (up to 120 minutes) were studied using 6:1 mole ratio of pure ethanol to oleic acid and 5 wt. % of the catalyst. The results showed that acid removed increased with increasing temperature and reaction time. Also, the acidity removal rises sharply during the first reaction period and then changes slightly afterward. The highest acidity removal value was 67 % recorded at 110 minutes and 70 °C. An apparent homogeneous reversible reaction kinetic model has been proposed a

Gingival carcinoma is a malignant neoplasm affecting the oral mucosa and is associated with significant morbidity and mortality. Allium ampeloprasum var. porrum water extracts have gotten a lot of attention because of their bioactive components, such as polyphenols, flavonoids, and alkaloids, which have a variety of pharmacological activities, including antiproliferative actions. This study aimed to evaluate the histological and molecular effects of Allium ampeloprasum (leek) water extract on the proliferation of the murine gingival cancer cell line. Histological evaluation was conducted to examine morphological changes induced by extract treatment. Molecular mechanisms underlying the observed histological changes were investigated

Background: Alterations in the microhardness and roughness are commonly used to analyze the possible negative effects of bleaching products on restorative materials. This in vitro study evaluated the effect of in-office bleaching (SDI pola office +) on the surface roughness and micro-hardness of four newly developed composite materials (Z350XT –nano-filled, Z250XT-nano-hybrid, Z250-mico-hybrid and Silorane-silorane based). Materials and methods: Eighty circular samples with A3 shading were prepared by using Teflon mold 2mm thickness and 10mm in diameter. 20 samples for each material, 10 samples for base line measurement (surface roughness by using portable profillometer, and micro-hardness by usingDigital Micro Vickers Hardness Test

Preparation of superposed thin film (CdTe)1-xSex / ZnS) with concentration of (x= 0.1, 0.3, 0.5) at a temperature of substrate (Ts= 80 0C) by using Thermal Vacuum Evaporation System. The measurement of X-ray diffraction shows that the compounds CdTe, ZnS, (CdTe)1-xSex and (CdTe)1-xSex / ZnS have a polycrystalline structure, the C-V characteristic shows that the capacitance degrease by increasing the concentration (x) in reverse bias, while the I-V characteristic shows the current dark (Id) increase in forward and reverse bias by increasing (x) and the photocurrent (Iph) increase in reverse bias by increasing the concentration (x), the values of photocurrent are greater than from the values of the dark current for all concentrations

Background: Salivary immunoglobulin IgA plays an essential role in the immune response against dental caries. This studywas conducted to compare the salivary IgA levels and flow rate of stimulated saliva in caries active and caries free children. Materials and methods: The present study included sixty healthy children age 7-10 yearswho were divided into two groups. They were caries free and caries active children (30 children in each group). Assessment and recording of caries – experience were through the application of Decayed, Missing and Filled Tooth Index (DMFT) and (dmft) index, for permanent and deciduous teeth respectively. After dental examination, stimulated saliva samples were collected from the subjects and performed und

The technical of Flame Thermal Spray had been used in producing a cermet
composite based on powders of stabilized zirconium oxide containing amount of
Yatteria oxide (ZrO2- 8Y2O3) reiforced by minerals powders of bonding material
(Ni-Cr- Al- Y) in different rates of additions (25, 35, 50) on stainless steel base type
(304) after preparing it by the way of Grit Blasting.
Before heat treatment, the coated cermet layers were characterized for porosity
and electric resistivity. All samples were heat treated in vacuum furnace at different
temperature and times. The physical tests had been operated after heat treatment
and gave best results especially porosity, which found to be reduced dramatically
and producing hig