Nano particles of Cadmium Oxide (CdO) thin films were prepared by spray pyrolysis technique. The synthesized film is annealed at (200 , 300, 450) o C for 3 hours .  The XRD and AFM for the analysis of its structural and micro-structural characteristic has been preformed. The average grain size was found to be about 32.50 nm .There is a preferred orientation along (200)   plane  with texture coefficient 1.79, 1.644, 1.763 and 1.792  for deposited and annealed films, corresponding to grain size 57,58 ,51 and 51 nm. The variations of stress with temperature is ranged from 0.157 - 0.376 GPa .
 

The molar ratio(x) of Li-Ni ferrites in the formula Li0.5-0.5xNixFe2.5-
0.5xO4 was varied in range 0.1-1.0 by hydrothermal process. The
XRD, SEM, and TEM tests were conducted to examine the samples
crystalline phase and to characterize the particles shapes and sizes.
The high purity spinel structure was obtained at med and high x
values. SEM and TEM images showed the existence of different
ferrite particles shapes like nanospheres and nanorods. The
maximum particle size is around (20nm). These size encourage
occurrence of super paramagnetic state. The reflection loss and
insertion loss as microwave losses of Li-Ni ferrite-epoxy composite
of 1mm thickness and mixing ratio 39.4 wt was investigated. The
mini

Background: Alcohol remains the single most significant cause of liver disease throughout the Western world, responsible for between 40 and 80% of cases of cirrhosis in different countries. There are no characteristic sonographic features of ALD. Many of the factors underlying the development of alcoholic liver injury remain unknown, and significant questions remain about the value of even very basic therapeutic strategies.
Patients and Methods: A total number of 50 patients with ALD were studied. Abdominal Doppler ultrasonography to determine the ratio of the left to right portal vein (PV) was done. They were compared with 50 healthy persons (control) and 50 patients with comparable CLD due to other causes.
Results: The diameter o

     The secondary sex ratio (SSR) is affected by many factors, including the concentration of hormones and infection with some pathogens such as Toxoplasma gondii. This study aimed to evaluate the effect of hormone variability concentrations and toxoplasmosis infection on the secondary sex ratio. 150 pregnant women were selected, 60 infected with late toxoplasmosis (LT), 60 infected with early toxoplasmosis (ET) and 30 seronegative to toxoplasmosis. After tracking the birth outcomes of these women, we calculated SSR in each group. During the second and third trimesters of pregnancy, estrogen, testosterone, progesterone, TSH, T4 and T3 concentrations were measured. The results of the three groups were compared. The results s

    In this  work , impact strength and the water absorption  ratio of powders of white and brown local chicken eggshell reinforced epoxy with different volume fractions ( 1 , 2 , 3 , 4 and  5 % ) were studied .       The experimental results show that composite filled by ( 1 % Vol . )of white eggshell powder exhibited  maximum  impact  strength and high resistance to tape water , so we choose this volume fraction to use the epoxy composite in coating . Optical microscopic observations are taken to develop a better  understanding of the phenomena taking place in the material system at microscopic level .

Membrane manufacturing system was operated using dry/wet phase inversion process. A sample of hollow fiber membrane was prepared using (17% wt PVC) polyvinyl chloride as membrane material and N, N Dimethylacetamide (DMAC) as solvent in the first run and the second run was made using (DMAC/Acetone) of ratio 3.4 w/w. Scanning electron microscope (SEM) was used to predict the structure and dimensions of hollow fiber membranes prepared. The ultrafiltration experiments were performed using soluble polymeric solute poly ethylene glycol (PEG) of molecular weight (20000 Dalton) 800 ppm solution 25 °C temperature and 1 bar pressure. The experimental results show that pure water permeation increased from 25.7 to 32.2 (L/m2.h.bar) by adding aceton

In this study, an easy, low-cost, green, and environmentally
friendlier reagents have been used to prepare CdS QDs, in chemical
reaction method by mixed different ratio of CdO and sulfur in
paraffin liquid as solvent and oleic acid as the reacting media in
different concentration to get the optimum condition of the reaction
to formation CdS QDs. The results give an indication that the
behavior is at small concentration of 4ml of the oleic acid is best
concentration which give CdS QDs of small about to 9.23 nm with
nano fiber configuration.

Physical and chemical adsorption analyses were carried out by nitrogen gas using ASTM apparatus at 77 K and hydrogen gas using volumetric apparatus at room temperature respectively. These analyses were used for determination the effect of coke deposition and poisoning metal on surface area, pore size distribution and metal surface area of fresh and spent hydrodesulphurization catalyst Co-MoAl2O3 .Samples of catalyst (fresh and spent) used in this study are taken from AL-Dura refinery. The results of physical adsorption shows that surface area of spent catalyst reduced to third compare with fresh catalyst and these catalysts exhibit behavior of type four according to BET classification ,so, the pores of these samples are cylindrical, and the

Credit derivatives (CDs) have been increasingly acknowledged as an important requirement to hedge and transfer credit risk CR. Nonetheless, they have been extensively criticized for destabilizing the whole economic system bringing about the latest subprime credit crisis. The study’s main aim is to investigate the reason for the use of (CDs), whether it is used for hedging or trade purpose, for four of the US international financial institutions that had made it through the 2007 crisis to resume functioning post-crisis. This will be for three different and critical periods, namely the pre, during and after crisis periods (Q1, 2000-Q1, 2014). Adopting the SUR technique, the investigation of the factors that influence the net position of (CD

     Background: Thyroid cancer (TC) is an increasingly prevalent malignancy throughout the world. It has long been recognized that the incidence of TC is higher in women which increases with age. However, the association of gender disparity and age with TC aggressiveness and outcomes are still controversial. The aim of this study was focused on the association of age and gender with histopathological characteristics in TC. Methods: 153 patients who met the criteria, were selected.  The included cases were divided into four age groups (≤24 years, 25-44 years, 45-64 years, and ≥65 years). Demographic, age and pathological parameters were compared among them. The association of gender and age with