In this study, an easy, low-cost, green, and environmentally
friendlier reagents have been used to prepare CdS QDs, in chemical
reaction method by mixed different ratio of CdO and sulfur in
paraffin liquid as solvent and oleic acid as the reacting media in
different concentration to get the optimum condition of the reaction
to formation CdS QDs. The results give an indication that the
behavior is at small concentration of 4ml of the oleic acid is best
concentration which give CdS QDs of small about to 9.23 nm with
nano fiber configuration.

Three complexes of copper(II) and iron(II) with mixed ligands acetylacetonebis(thio-semicarbazone)- ABTSH2 and benzaldazine- BA have been prepared and characterized using different physico-chemical techniques including the determination of metal contents, mole-cular weight, measurement of molar conductivity, magnetic moment, molar refraction, infrared and electronic spectra. Accordingly, octahedral complexes having general formulaes [Cu2(ABTSH2)2(BA)2Cl2]Cl2 and [M2(ABTSH2)2(BA)2(SO4)2] {M= Cu(II) or (Fe(II)} have been proposed. The resulted complexes screened for antifungal activity in vitro against the citrus pathogen Aspergillus niger and Fusarium sp. which caused root rot of sugar and the beans pathogen Alternaria sp. All the complex

Many patients with advanced type 2 diabetes mellitus (T2DM) and all patients with T1DM require insulin to keep blood glucose levels in the target range. The most common route of insulin administration is subcutaneous insulin injections. There are many ways to deliver insulin subcutaneously, such as vials and syringes, insulin pens, and insulin pumps. Though subcutaneous insulin delivery is the standard route of insulin administration, it is associated with injection pain, needle phobia, lipodystrophy, noncompliance, and peripheral hyperinsulinemia. Therefore, the need exists to deliver insulin in a minimally invasive or noninvasive way and in the most physiological way. Inhaled insulin was the first approved noninvasive and alternative way

The influence of pre- shot peening and welding parameters on mechanical and metallurgical properties of dissimilar and similar aluminum alloys AA2024-T3 and AA6061-T6 joints using friction stir welding have been studied. In this work, numbers of plates were equipped from sheet alloys in dimensions (150*50*6) mm then some of them were exposed to shot peening process before friction stir welding using steel ball having diameter 1.25 mm for period of 15 minutes. FSW joints were manufactured from plates at three welding speeds (28, 40, 56 mm/min) and welding speed 40mm/min was chosen at a rotating speed of 1400 rpm for welding the dissimilar pre- shot plates. Tow joints were made at rotational speed of 1000 rpm and welding speed of 40m/min f