Solar cells thin films were prepared using polyvinyl alcohol (PVA) as a thin film, with extract of natural pigment from local flower. A concentration of 0.1g/ml of polyvinyl alcohol solution in water was prepared for four samples, with various concentrations of plant pigment (0, 15, 25 and 50) % added to each of the four solutions separately for preparing (PVA with low concentrated dye , PVA with medium concentrated dye and PVA with high concentrated dye ) thin films respectively . Ultraviolet absorption regions were obtained by computerized UV-Visible (CECIL 2700). Optical properties including (absorbance, reflectance, absorption coefficient, energy gap and dielectric constant) via UV- Vis were tested, too.  Fourier transform infra

The photonconductor detectors CdSe:Cu was fabricated as a thin film of (1 μm) in thickness using vacuum evaporation technique. doping with copper was made using vacuum annealing at 350oC under argon atmosphere . The spectral responsivity and spectral detectivity of the detector were determined as a function of incident wavelength on the sample. A remarkable improvement in performance was absorbed for the specimen, which doping with (1-5 wt%) Cu.
The spectral response increases with increasing of wavelength for incident radiation to maximum value, after that , it reduced sharply . There is a shifting for peak responsivity indirect of higher wavelength. The detectivity was increased with doping but its decreased as the concentration in

    Many designs have been suggested for unipolar magnetic lenses based on changing the width of the inner bore and fixing the other geometrical parameters of the lens to improve the performance of unipolar magnetic lenses. The investigation of a study of each design included the calculation of its axial magnetic field the magnetization of the lens in addition to the magnetic flux density using the Finite Element Method (FEM) the Magnetic Electron Lenses Operation (MELOP) program version 1 at three different values of current density (6,4,2 A/mm²). As a result, the clearest values and behaviors were obtained at current density (2 A/mm²). it was found that the best magnetizing properties, the high

Thin films of ZnO nano crystalline doped with different concentrations (0, 6, 9, 12, and 18 )wt. % of copper were deposited on a glass substrate via pulsed laser deposition method (PLD). The properties of ZnO: Cu thin-nanofilms have been studied by absorbing UV-VIS, X-ray diffraction (XRD) and atomic force microscopes (AFM). UV-VIS spectroscopy was used to determine the type and value of the optical energy gap, while X-ray diffraction was used to examine the structure and determine the size of the crystals.  Atomic force microscopes were used to study the surface formation of precipitated materials. The UV-VIS spectroscopy was used to determine the type and value of the optical energy gap.

?Natural Occurrence of aflatoxin Bi and B2 was investigated monthly in paddy rice stored for duration of six months. Aflatoxin B| was detected at the beginning of storage. The concentration of aflatoxin Bi in paddy and polished rice was found to be (0.3 and ()) ppb respectively while aflatoxin B2 W'as not detected in both paddy and polished rice afler six months of storage, concentration of aflatoxin Bi ‘ ’ ' reached 3 ppb in paddy rice and 0.9 ppb in polished rice, while the study proved that the concentration of aflatoxin in paddy rice was higher than polished rice as a result of processing which reduce the toxin

In this study, tin oxide (SnO2) and mixed with cadmium oxide (CdO) with concentration ratio of (5, 10, 15, 20)% films were deposited by spray pyrolysis technique onto glass substrates at 300ºC temperature. The structure of the SnO2:CdO mixed films have polycrystalline structure with (110) and (101) preferential orientations. Atomic force microscopy (AFM) show the films are displayed granular structure. It was found that the grain size increases with increasing of mixed concentration ratio. The transmittance in visible and NIR region was estimated for SnO2:CdO mixed films. Direct optical band gap was estimated for SnO2 and SnO2 mixed CdO and show a decrease in the energy gap with increasing mixing ratio. From Hall measurement, it was fou

The impact of decorating Fe, Ru, Rh, and Ir metals upon the sensing capability of a gallium nitride nanotube (GaNNT) in detecting chlorine trifluoride (CT) was scrutinized using the density functionals B3LYP and B97D. The interaction of the pristine GaNNT with CT was a physical adsorption with the sensing response (SR) of approximately 6.9. After decorating the above-mentioned metals on the GaNNT, adsorption energy of CT changed from −5.8 to −18.6, −18.9, −19.4, and −20.1 kcal/mol by decorating the Fe, Ru, Rh, and Ir metals into the GaNNT surface, respectively. Also, the corresponding SR dramatically increased to 39.6, 52.3, 63.8, and 106.6. This shows that the sensitivity of the metal-decorated GaNNT (metal@GaNNT) increased by in

(Sb₂S₃)_1-xSn_x thin films with different concentrations (0, 0.05 and
0.15) and thicknesses (300,500 and 700nm) have been deposited by
single source vacuum thermal evaporation onto glass substrates at
ambient temperature to study the effect of tin content, thickness and
on its structural morphology, and electrical properties. AFM study
revealed that microstructure parameters such as crystallite size, and
roughness found to depend upon deposition conditions. The DC
conductivity of the vacuum evaporated (Sb₂S₃)_1-x Sn_x thin films was
measured in the temperature range (293-473)K and was found to
increase on order of magnitude with