The corrosion behavior of bare and chemical conversion coated (through anodizing) aluminum ASA 606 I in stagnant chromic acid solutions . Solutions of 2, 6 & J O wt. % Cr03 at 45°C, have been investigated using polarization technique. The anodizing experiments were conducted under fixed conditions of 35 minute exposure time and 30 volt supplied voltage. The most important feature achieved was the great difference in behavior between the anodic polarization curves for bare and anodized aluminum in different concentrations of chromic acid solutions.

A variety of oxides were examined as additives to a V2O5/Al2O3 catalyst in order to enhance the catalytic performance for the vapor phase oxidation of toluene to benzoic acid. It was found that the modification with MoO3 greatly promoted the little reaction leading to improve catalyst performance in terms of toluene conversion and benzoic acid selectivity. The effect of catalyst surface area, catalyst promoters, reaction temperature, O2/toluene, steam/toluene, space velocity, and catalyst composition to catalyst performance were examined in order to increase the benzoic acid selectivity and yield.

In this work, studying the effect of ethylenediamine as a corrosion inhibitor was investigated for carbon steel in aerated HCl solution in range of 0.1-1N under dynamic conditions, i.e., rotational velocity of 400–1200 rpm in the temperature range 35 – 65 ºC.  Weight loss method was employed in absence and presence of the inhibitor as an adsorption type in concentration range 1000 – 5000 ppm using rotating cylinder specimens. The experimental results showed that corrosion rate in absence and presence of inhibitor is increased with increasing temperature, rotational velocity and concentration of acid. It is decreased with increasing inhibitor concentration for the whole range of temperature, rotational velocity and concentrati

Modified asphalt is considered one of the alternatives to address the problems of deficiencies in traditional asphalt concrete, as modified asphalt addresses many of the issues that appear on the pavement layers in asphalt concrete, resulting from heavy traffic and vehicles loaded with loads that exceed the design loads and the large fluctuations in the daily and seasonal temperatures of asphalt concrete. The current study examined the role of polyphosphoric acid (PPA) as a modified material for virgin asphalt when it was added in different proportions (1%, 2%, 3%, 4%) of the asphalt weight. The experimental program includes the volumetric characteristics associated with the Marshall test, the physical properties, and th

The rubber ropes exercises affected muscle groups, which in turn affects the corners of the conditions of the body before and over the barrier where affected the time passed. To change the angle of the approaching and payment impact on passing each times the barrier 1-5. That passed over the barrier 1and gate 5 impacts on the nature of the achievement, where time has become less. Find the values of cruise missiles and other phases and stages of pitch angle other categories which it enshrines stood as compelling rejection men's 110m hurdles. Find the value of the instant messaging distances between different barriers and stages. Studies by adding rubber sling barriers race categories, measurement of kinematic variables. Emphasis on the devel

A comparison study was made for the reaction of triruthenium carbonyl Ru3(CO)12 with azoarene ArN=NAr . This reaction was monitored in two kinds of solvents , toluene , and n- octane , which yielded new triruthenium carbonyl complex Ru3(μ3-NAr)2(CO)9 . The reactions of azoarenes ArN=NAr with Ru3(CO)12 formed the following trinuclear compound of Ru3((μ3- NAr)2(CO)9 (Ar-C6H4Br-4) in law yield . In addition , to new isomers species of mononuclear cyclometallated of Ru(BrC6H4N-NC6H4NBr-4)2(CO)2 in different percentages . The mechanism of the reaction domenstrates that the formation of trinuclear bis arylimido complexes , and ortho metallated was , the result of cleavage of nitrogen –nitrogen bond . Monitoring this gave evidence that the rea

In this study NiO - CoO bimetallic catalysts are prepared with two Ni/Co ratios (70:30 and 80: 20) using the precipitation method of nitrate salts. The effects of Ni /Co ratio and preparation methods on the catalyst are analyzed by using different characterization techniques, i.e. atomic absorption (AA) , XRD, surface area and pore volume measurements according to the BET method . The results indicate that the best catalyst is the one containing the percentage of Ni :Co ( 70 : 30 ). Experiments indicate that the optimal conditions to prepare catalyst are stirring for three hours at a temperature of 60oC of the preparation , pH= (8-9) , calcination temperature at 400oC for two hours