The (NiTsPc) thin films operating by vacuum evaporation technique are high recital and good desirable for number of applications, were dumped on glass substrates at room temperature with (200±20nm) thickness and doped with Al at different percentage (0.01,0.03) besides annealing the sample with 200˚C for 1 hours . The stimuluses of aluminum dopant percentage on characterization of the dropped (Ni Ts Pc) thin films were studied through X-ray diffraction in addition from the attained results, were all the films have polycrystalline in nature, as well the fallouts of XRD aimed at film illustrations polycrystalline, depending on the Al ratio doping, the results, SEM exposed the surface is regularly homogeneous. Utilizing first-ideolog

     With and without the use of magnetic fields, titanium dioxide (TiO₂) nanoparticles were synthesized using the hydrothermal method at extremely high temperatures and pressures. Titanium tetra isopropoxide [Ti(C₁₂H₂₈O₄)] was used for the preparation, which was performed at pH 7 and under temperatures of 160 and 190 ˚C. UV spectroscopy, XRD crystallography, FE-SEM microscopy were used for characterizations. From UV spectroscopy, the energy gap values were clearly affected by the increase in temperature and the presence of the magnetic field. At the temperatures of 160 and 190 ^oC for TiO₂ without magnetic field, FE-SEM microscopy images have shown an average c

Background: The association between diabetes and inflammatory dental diseases had been studied extensively for more than 50 years. A large evidence base suggests that diabetes is associated with an increased prevalence, extent and severity of gingivitis and periodontitis and loss of teeth. Many patients do not aware that they are diabetic.Objectives:The aim of the current study was to assess a fast, non-invasive, safe procedure to screen for diabetes and its severity in dental clinics and to assess the change in blood glucose level before and after tooth extraction during periodontalResults: there were no significant differences between the blood samples collected before tooth extraction from finger puncture method (FPB) and the gingival

In this paper investigate the influences of dissolved CO₂/H₂S gases, crude oil velocity and temperature on the rate of corrosion of crude oil transmission pipelines of Maysan oil fields southern Iraq. The Potentiostatic corrosion test technique was conducted into two types of carbon steel pipeline (materials API 5L X60 and API 5L X80). The computer software ECE electronic corrosion engineer was used to predict the influences of CO₂ partial pressure, the composition of crude oil, flow velocity of crude oil and percentage of material elements of carbon steel on the rate of corrosion. As a result, the carbon steel API 5L X80 indicates good and appropriate resistance to corrosion compared to carbon steel API

The aims of research is to know the effect of using the computer in

teaching physics to the fifth secondary grade on the achievement of the students and their retention of  information .

The sample consists of ( 50 ) students in the fillh secondary grade (scicnti fie  branch  )   in  Nassiriyah   secondary  school   in  Thi-qar governorate in ( 200 I - 2002 ) that chooses as random Iy and divided

to t>vo equivalent groups:control and experimental .

The researcher built the teaching plans of each group . The five lessons choice from curriculum , and desi b'Tl  five computer teaching programs , and final achievement test from multip

Flavonoids were extracted from Zizyphus spina-christi leaves by Ethyl acetate after acid digested and used as antioxidant. The dried extract was added separately to each sample of fat extracted from hallow cow and sheep bones as follows: T1 cow fat, T2 control for cow fat, T3 sheep fat and T4 control for sheep fat (the control T2 and T4 reffered to samples without added antioxidant).
Samples were stored at -18, 5, 25 and 55 °C for 28 days. The storage trials were conducted at -18, 5 and 25 °C for 28 days for T1, T2, T3 and T4. The chemical indices examined initially and at the end of storage period. PVs was 1.46, 1.46, 1.8 and 1.8 meq/ Kg oil respectively, FFA values were 0.245, 0.245, 0.244 and 0.244% respectively and TBA va

The major aim of this research is study the effect of the type of lightweight aggregate (Porcelinite and Thermostone), type and ratio of the pozzolanic material(SF and HRM) and the use of different ratios of w/cm ratio(0.32 and 0.35) on the properties of SCLWC in the fresh and hardened state. SF and HRM are used in three percentage 5%,10%, and 15% as a partial replacement by weight of
cement for all types of SCLWC. The requirements of self-compatibility for SCC are fulfilled by using the high performance superplasticizer (G51) at 1.2liter per 100 kg of cement. The values of air dry density and compressive strength at age of 28 days within the limits of structural lightweight concrete. The air dry density and compressive strength at a

This research includes using epoxy resin and polyurethane resin to form a blend (EP+PU)  with different resin ratios (90 – 10)%, (80 – 20)%, (70 – 30)%, and (60 – 40)% to achieve best ratio for impact strength as a function of better toughness; then reinforced with micro and nano (CdO) with weight fraction (0.02, 0.04, 0.06, 0.08). Mechanical properties were studied including hardness before and after exposure to UV irradiation. Results showed that the composite (nano CdO+ blend) had better properties compared with (micro CdO+ blend) composite. Also hardness show increases with increasing the weight fraction for all samples.

In this study a polymeric composite material was prepared by hand
lay-up technique from epoxy resin as a matrix and magnesium oxide
(MgO) as a reinforcement with different weight fraction (5,10,15,
and 20)% to resin. Then the prepared samples were immersed under
normal condition in H₂So₄(1 M) solution, for periods ranging up to
10 weeks. The result revealed that the diffusion coefficient
decreasing as the concentration of MgO increase. Also we studied
Hardness for the prepared samples before and after immersion. The
result revealed that the hardness values increase as the concentration
of MgO increase, while the hardness for the samples after immersion
in H₂SO₄ dec