This work deals with thermal cracking of three samples of extract lubricating oil produced as a by-product from furfural extraction process of lubricating oil base stock in AL-Dura refinery. The thermal cracking processes were carried out at a temperature range of 325-400 ºC and atmospheric pressure by batch laboratory reactor. The distillation of cracking liquid products was achieved by general ASTM distillation (ASTM D -86) for separation of gasoline fraction up to 220 ºC from light cycle oil fraction above 220 ºC. The comparison between the conversions at different operating conditions of thermal cracking processes indicates that a high conversion was obtained at 375°C, according to gasoline production. According to gasoline produ

Objective(s): Assess the effectiveness of osteoporosis prevention instruction program on nursing college students’
knowledge at Baghdad University.
Methodology: A quasi-experimental design was used to assess the effectiveness of osteoporosis prevention
instruction program on nursing college students at University of Baghdad from April 2011 to September 2011. A
random sample consisted of (40) females students from first year of Nursing College \ Baghdad University. The data
was collected by using constructed questionnaire, which consists of three parts. Part one: consists of demographic
information and health characteristics .Part two: consists of students’ daily life behaviors which include, dietary
behaviors, an

Some modified techniques are used in this article in order to have approximate solutions for systems of Volterra integro-differential equations. The suggested techniques are the so called Laplace-Adomian decomposition method and Laplace iterative method. The proposed methods are robust and accurate as can be seen from the given illustrative examples and from the comparison that are made with the exact solution.

In this article, the adsorption of Cu(ll) ion from aqueous solution into polyacrylic acid
(PAA) hydrogel bead has been investigated using a batch method of different
temperature (10-30 °C) and different contact time (1-48 hr) to reach the equilibrium of
adsorption. Initial concentration and adsorption capacity of the adsorbents is presented,
the time required to reach a maximum capacity of bead was about 24hr. The temperature
effect on adsorption was studied and the experimental data have been analyzed using the
Langmuir and freundlich isotherm models. The adEsorption capacity at equilibrium was
found to be 142.68 mg/g; more than 95% of studied cation was removed by the
adsorbent. The process is very efficient es

AA3003-H14 aluminum alloy plates were welded by friction stir welding and TIG welding.
Fatigue properties of the welded joints were evaluated based on the superior tensile properties for
FSW at 1500 rpm rotational speed and 80 mm/min welding speed. However, there is not much
information available on effect of welding parameters with evolution of fatigue life of friction stir
welds. The present study experimentally analyzed fatigue properties for base, FSW, and TIG welds
of AA 3003-H14 aluminum alloy. Fatigue properties of FSW joints were slightly lower than the
base metal and higher than TIG welding.

This study focuses on studying the effect of reinforced steel in detail, and steel reinforcement (tensile ratio, compression ratio, size, and joint angle shape) on the strength of reinforced concrete (compressive strength) Fc' and searching for the most accurate details of concrete divisions, their behavior, and corner resistance of reinforced concrete joint. The comparison of this paper with previous studies, especially in the studied properties. The conclusions of the chapter are summarized that these effects had a clear effect and a specific effect on the behavior and resistance of the reinforced concrete corner joints under the negative moments and under their influence and the resulting stress conditions. The types of defects that can