In the drilling and production operations, the effectiveness of cementing jobs is crucial for efficient progress. The compressive strength of oil well cement is a key characteristic that reflects its ability to withstand forceful conditions over time. This study evaluates and improves the compressive strength and thickening time of Iraqi oil well cement class G from Babylon cement factory using two types of additives (Nano Alumina and Synthetic Fiber) to comply with the American Petroleum Institute (API) specifications. The additives were used in different proportions, and a set of samples was prepared under different conditions. Compressive strength and thickening time measurements were taken under different conditions. The amoun

The present study intends to prepare nanofibers mat of polyacrylonitrile by electrospinning technique and investigates their adsorption capacity to Congo red dye from the aqueous solution, after characterize it by different techniques such as FTIR, SEM, EDA, XRD and BET. The influence factors on adsorption were studied including adsorbent dosage, initial concentration, contact time, pH and ionic strength. The results confirmed that the increasing in pH decreases the adsorption capacity. So, the optimum adsorbent dosage, initial concentration and contact time were 0.006 g, 25 mg/L and 150 min respectively. The isotherm models of Freundlich and Langmuir were applied on the experimental adsorption data to evaluate the maximum capacity and ener

   Linde Type-A (LTA) zeolite was modified by adding  lead sulfide into cavities of zeolite. The zeolite and zeolite –pbs  were characterized by FTIR, XRD, AFM and SEM. The adsorption of congo red (CR)  dye  from aqueous solution by zeolite and zeolite – pbs were studied. Different parameters like contact time, temperature and concentration of (CR) dye were investigated. The results show that at contact time of 45, 30 min for maximum adsorption of (CR) dye onto zeolite and zeolite -pbs respectively were observed. The kinetic data was analyzed using pseudo-first-order and pseudo-second-order kinetic models. The adsorption kinetics of (CR) dye  were fitted well with the pseudo-second-order k

     In this study, gamma ray transmission method have been used to determine the total porosity in four samples: pure Alumina  ( Al₂O₃   ),  Al₂O₃ + (0.2wt%)MgO ,  Al₂O₃ + (0.6wt% )Y₂O₃  and Al₂O₃+ (8wt% ) ZrO₂ .

      The experimental setup for the gamma ray transmission consist of ¹³⁷Cs gamma source ( 662 KeV  ), a  NaI (Tl) scintillation detector measured the attenuation of strongly collimated  gamma beam through alumina samples.

The porosity obtained by the gamma ray transmission method were compare

  This research  studyies the effect of MgO and ZrO2 as additives in sintering Al2O3 . The experimental results are modeled using ( L2 _ regression) technique , sintered density and grain size rate measurments were  accounted by utilizing experimental results of undoped , MgO doped and ZrO2  doped alumina impregrated with spherical large pores in final stage of sintering . The effect of each additive is inhibitian of the grain growth and increasing the densification rate which enhances the kinietics of densification and the removal of large and small pores.

In this research Epoxy resin was reinforced by nano alumina (AL2O3) particles in grain size(25-30 nm) with two weight ratios (2,4)% then compared with pure Epoxy. Four mechanical tests were performed on these materials include Hardness, flexural, impact & compression strengths before and after immersion in tap water and chemical solutions (CH3COOH) acid, (KOH) base at (0.5N) ,The diffusivity coefficients of all prepared samples were calculate after immersion in water and chemical solutions mentioned above , the results were showed that the Flexural, Impact & Hardness increase after addition the ceramic particles (AL2O3) while the immersion process results showed illustrated different values from sample to other.

The adsorption of Malonic acid, Succinic acid, Adipic acid, and Azelaic acid from their aqueous solutions on zinc oxide surface were investigated. The adsorption efficiency was investigated using various factors such as adsorbent amount, contact time, initial concentration, and temperature. Optimum conditions for acids removal from its aqueous solutions were found to be adsorbent dose (0.2 g), equilibrium contact time (40 minutes), initial acids concentration (0.005 M). Variation of temperature as a function of adsorption efficiency showed that increasing the temperature would result in decreasing the adsorption ability. Kinetic modeling by applying the pseudo-second order model can provide a better fit of the data with a greater correla