A single-crystalline semi-polar gallium nitride (11-22) was grown on m-plane (10-10) sapphire substrate by metal organic chemical vapor deposition. Three-step approach was introduced to investigate the grain size evolution for semi-polar (11-22) GaN. Such approach was achieved due to the optimized gallium to ammonia ratio and temperature variations, which led to high quality (11-22) oriented gallium nitride epilayers. The full width at half maximum values along (-1-123) and (1-100) planes for the overgrowth temperature of 1080°C were found to be as low as 0.37° and 0.49°, respectively. This was an indication of the enhanced coalescence and reduction in root mean square roughness as seen by atomic force microscopy. Surface analysi

Sustainable crop production in a coarse soil texture is challenging due to high water permeability and low soil water holding capacity. In this paper, subsurface water retention technology (SWRT) through impermeable polyethylene membranes was placed at depth 35 cm below ground surface and within the root zone to evaluate and compare the impact of these membranes and control treatment (without using the membranes) on yield and water use efficiency of eggplant inside the greenhouse. The study was conducted in Al-Fahamah Township, Baghdad, Iraq during spring growing season 2017. Results demonstrated the yield and water use efficiencies were 3.483 kg/m² and 5.653 kg/m³, respectively for SWRT treatment p

This study involved the effect of the aqueous extracts of two plants, Origanum vulgare L.(1), Trigonella Foenum Graecum L. (Fenugreek) seeds(2) on the growth of cancer cell lines. Rhabdomyo sarcomas (RD) of human cell line and female intestine cells of Albino mice (L20B) in vitro System. These extracts were compared with the known anticancer drug Cis-platinum(Cis-Pt) as a positive control. The phytochemical tests were used for screening the active compounds in plants. The inhibition activity assay was used as a parameter of the cytotoxic effect of these extracts. Cancer cell lines were treated with four concentrations of Cis-platin, 31.25, 62.5, 125 and 250 ?g/ml for 72 hour exposure time. The same concentrations were used for the other ext

   The present research was conducted to synthesis Y-Zeolite by sol-gel technique using MWCNT (multiwalled carbon nanotubes) as crystallization medium to get a narrow range of particle size distribution with small average size compared with ordinary methods. The phase pattern, chemical structure, particle size, and surface area were detected by XRD, FTIR, BET and AFM, respectively. Results shown that the average size of Zeolite with and without using MWCNT were (92.39) nm and (55.17) nm respectively .Particle size range reduced from (150-55) nm to (130-30) nm. The surface area enhanced to be (558) m²/g with slightly large pore volume (0.231) km³/g was obtained. Meanwhile, degree of crystallization decrease

In this work, The effect of annealing treatment at different temperatures (373, 423 and 473) K and chemical treatment with talwen at different immersion time (40, 60 and 80) min on structural and optical properties of the bulk heterojunction (BHJ) blend copper phthalocyanine tetrasulfonic acid tetrasodium salt/poly dioxyethylenethienylene doped with polystyrenesulphonic acid (CuPcTs/PEDOT:PSS) thin films were investigated. The films were fabricated using spin coating technique. X-ray diffraction (XRD) measurements displayed only one peak at 2θ =4.5o corresponding to (001) direction which has dhkl larger than for standard CuPcTs. The dhkl increase then decrease with increasing annealing temperature and
the time of chemical treatment w

The atmospheric air cold plasma has been used to manufacture gold nanomaterials for treating parasitic leishmaniasis. This study experimentally assessed the treatment of Leishmania parasites (L. donovani and L. tropica) by gold nanoparticles. Specifically, atmospheric pressure nonthermal plasma was generated using different diameters (1.0, 2.8, 3.8 and 4.3 mm) of high voltage electrode. Aqueous gold tetrachloride salts (HAuCl4·4H2O) were used as precursor to produce gold nanoparticles. UV-vis spectroscopy and x-ray diffraction were conducted for characterization of the nanoparticles. The optimum condition (a diameter of 1 mm) was chosen to prepare gold nanoparticles, where the grain size was found to be 17 nm. Accordingly, the nanoparticle

The reducing of erosion and the solubility of irrigation canals soils which constructed on gypsum soil is important in civil and water resources engineering. The main problem of gypsum soils is the presence of gypsum which represents one of most complex engineering problems, especially when accompanied by the moving of water which represent dynamic load along the canal. There are several solutions to this problem, in this research “Poly urethane” is used to give the gypsum soil sufficient hardness to reduce the solubility and erosion, after compacting the soil in the canal, percentages of Poly urethane was used to making cover to the soil by mixing percent of soil with Poly urethane, and the ratio was as follows: (5 and 10) % an