In this work, an experimental research on a low voltage DC magnetron plasma sputtering (0-650) volt is used for coating gold on a glass substrate at a constant pressure of argon gas 0.2 mbar and deposition time of 30 seconds. We focused on the effects of operating conditions for the system such as, electrode separation and sputtering current on coated samples under the influence of magnetic flux. Electron temperature and electrons and ions densities are determined by a cylindrical single Langmuir probe. The results show the sensitivity of electrode separation lead to change the plasma parameters. Furthermore, the surface morphology of gold coated samples at different electrode separation and sputtering current were studied by atomic forc

The best optimum temperature for the isolate was 30○C while the pH for the maximum mineral removal was 6. The best primary mineral removal was 100mg/L, while the maximum removal for all minerals was obtained after 8 hrs, and the maximum removal efficiency was obtained after 24 hrs. The results have proved that the best aeration for maximum removal was obtained at rotation speed of 150 rpm/ minute. Inoculums of 5ml/ 100ml which contained 106 cell/ ml showed maximum removal for the isolate.

Pulsed liquid laser ablation is considered a green method for the synthesis of nanostructures because there are no byproducts formed after the ablation. In this paper, a fiber laser of wavelength 1.064 µm, peak power of 1 mJ, pulse duration of 120 ns, and repetition rate of 20 kHz, was used to produce carbon nanostructures including carbon nanospheres and carbon nanorods from the ablation of asphalt in ethanol at ablation speeds of (100, 75, 50, 10 mm/s).  The morphology, composition and optical properties of the synthesized samples were studied experimentally using FESEM, HRTEM, EDS, and UV-vis spectrophotometer. Results showed that the band gap energy decreased with decreasing the ablation speed (increasing the ablation time), the mi

Ceramic coating compose from a ceramic mixture (MgO, Al₂O₃) and metall (Al-Ni) were produced by Thermal Spray Technique. The mixed ratio of used materials Al:Ni (50%) and 40% of Al₂O₃ and 10% MgO. This mixture was spray on a stainless steel substrate of type (316 L) by using thermal spray with flame method and at spraying distances (8, 12, 16 and 20) cm, then the prepared films were treated by laser and thermal treatment. After that performing a hardness and adhesion tests were eximined. The present study shows that the best value of the thermal treatment is 1000 ℃ for 30 mint; the optimum spray distance is 12 cm and most suitable laser is 500 mJ where the microscopic and mechanical character

The preparation and spectral characterization of complexes for Co(II), Ni(II), Cu(II), Cd(II), Zn(II) and Hg(II) ions with new organic heterocyclic azo imidazole dye as ligand 2-[(2`-cyano phenyl) azo ]-4,5-diphenyl imidazole ) (2-CyBAI) were prepared by reacting a dizonium salt solution of 2-cyano aniline with 4,5-diphenyl imidazole in alkaline ethanolic solution .These complexes were characterized spectroscopically by infrared and electronic spectra along with elemental analysis‚ molar conductance and magnetic susceptibility measurements. The data show that the ligand behaves a bidantate and coordinates to the metal ion via nitrogen atom of azo and with imidazole N3 atom. Octahedral environment is suggested for all metal complex

Background: With the increasing demand on esthetic orthodontic appliances, discoloration of clear elastomeric chains and modules remains an issue which concerns both orthodontics and patients. This in vitro study was conducted to evaluate the effect of exposing stretched clear elastomeric chains from six different companies (Ortho Technology, Ormco, Ortho Organizer, American Orthodontics, Opal and G&H companies) to three types of dietary media (tea, coffee and turmeric). Materials and methods: A total of 960 lengths of six modules were cut from short type elastomeric chain; 160 pieces from each brand. The specimens were stretched 50%, placed on plastic boards, and incubated in water at 37°C for 1 day, 7 days, 14 days and 28 days. Once a

Leiomyosarcoma (smooth muscle tumor) is a rare type of a malignant neoplasm of smooth
muscle. It is a resistant cancer, generally not very responsive to chemotherapy, radiationand surgery.The
aim of this study was to evaluate photodynamic therapy (PDT) as a possible basis for treatment using
(650 nm)diode laser with methyleneblue (MB) as a photosensitizer on leiomyosarcoma (LMS)cell line
(L20B) in vitro. The cytotoxic effects of 650nm diode laser 0.052 W/cm2 (power density) at different
exposure time (10, 20, and 30 min) with methylene blue at different concentrations (0.01% ,0.1 % ,1%)
was investigated on LMS cell line (L20 B). The cytotoxic effect of laser was increased with increasing
irradiation time for a certai