This study outlines the synthesis of substituted 1,2,4-triazole derivatives through the cyclization reaction of thiourea derivatives. The process begins with the reaction of different halides with KSCN to produce isothiocyanate derivatives. then followed by a reaction with isonicotinic acid hydrazide to yield thioureas (1-6), with a yield rate of (72-88%). Then, compounds (1-6) were treated with alkaline medium 4 N (NaOH) to produced 1,2,4-triazole derivatives (7-12) with a yield (51-69%).The structure of the prepared compounds was characterized using FTIR,1HNMR and 13CNMR spectroscopy. Some of the synthesized compounds were tested for antimicrobial activity when, compound 9 showed strong activity against gram positive bacteria (Sta

Since its invention by the Ancient Romans and later developed during the mid-18th century, the concrete structure and finish, has been considered as the most powerful, practical, economic and constructional material that meets the building’s architectural and aesthetical requirements. By creating unique architectural forms, the pioneer architects used concrete widely to shape up their innovative designs and buildings.

The pre-mixed ultra-high performance concrete which manufactured by Lafarge.

The transparent concrete and cement that allow the light beams to pass through them, introduces remarkable well-lit architectural spaces within the same structural criteria. This product is a recyclable, sustainab

The phenomenon of poverty is one of the most important phenomena facing the world at large. Despite the tremendous technological progress witnessed by mankind and despite the unprecedented high levels of world economic production, poverty remains the greatest challenge facing the world. Statistics and studies have shown that poverty is caused by several problems: (health, social, economic, educational, etc.) These problems are obstacles to the ability to obtain employment opportunities, which leads in the beginning to the growth phenomenon of unemployment, and ultimately to the growth of poverty.

The results of a range of research in the field of psychology have confirmed that children from poor homes suffer from a high level of

Abstract  

The aim of this paper is to investigate and discuss the mechanisms of corrosion of epoxy coatings used for potable water tanks. Two distinct types of Jotun epoxy coatings: Tankguard 412 contained polyamine cured epoxy and Penguard HB contained polyamide cured epoxy, were tested and studied using the electrochemical impedance spectroscopic (EIS) method. The porosity of epoxy coatings was determined using EIS method. The obtained results showed that the two epoxy coatings have excellent behavior when applied and tested in potable water of Basrah city. Polyamine is more resistance to water corrosion compared to polyamide curing epoxy and has high impedance values. Microscopic inspection after te

In this search, Ep/SiO2 at (3, 6, 9, 12 %) composites is prepared by hand Lay-up method, to measure the change in the thermal conductivity and Impact Strength of epoxy resin before and after immersion in H2SO4 Solution with a 0.3N for 10 days. The results before immersion decreases with the increase of the weight ratios of the reinforcement material (SiO2), It changed from (82.6×10-2 to 38.7×10-2 W/m.°C) with change weight ratios from (3 to 12) % respectively, but after immersion time in the chemical solution where it was (65.6×10-2 W/m.°C) at the weight ratios (6 %) and became (46.6 × 10-2 W/m.°C) after immersion in sulfuric acid. The results of the Impact strength decreased by increasing the percentage weight ratio, it changed f

Effect of nano and micro SiO2 particles with different weight percent (2,4,6,8 and 10) %wt on the Interlaminar fracture toughness (GIc) of 16-plies of woven roving glass fiber /epoxy composites prepared by hand lay – up technique were investigated. The specimens were tested using DCB test (mode I).
Area method was used to compute the interlaminar fracture toughness. The results show that, GIc would increase with the increasing in the filler content, the main failure in microcomposites and nanocomposites was delamination in the layers, the delamination reduced with increasing in the filler content.