Background: Recently, Poly propylene fibers with and without plasma treatment have been used to reinforce heat cure denture base acrylic but, so far some of properties like tensile strength , wettability and wear resistance not evaluated yet, the aim of the study is to clarify the influence of incorporation of treated and untreated fibers on these properties. Materials and methods: Twenty one specimens were fabricated for every tested property(tensile strength, wear resistance and wettability) that classified into three groups(control, untreated poly propylene fibers reinforced specimens and Oxygen plasma treated group)and for each test sevens amples were used(n=7). Tensile strength was tested using Instron universal testing machine, wear

Cadmium oxide (CdO) thin films were deposited using the sequencing ion layer adsorption and reaction (SILAR) method. In this study, the effect of the pH value of an aqueous solution of cadmium acetate at a concentration of 0.2 mol of the cadmium oxide film was determined. The solution source for the cadmium oxide film was cadmium ions and an aqueous ammonia solution. The CdO films were deposited on glass substrates at a temperature of 90 ℃. The cadmium oxide film thickness was determined by the weight difference method at pH values ​​(7.2, 8.2). X-ray diffraction (XRD) and scanning electron microscopy (SEM) showed that the size of the crystals increased with the increase in the solution (pH). While the UV-visible spectra of the fil

Thin films of CdTe were prepared with thickness (500, 1000) nm on the glass substrate by vacuum evaporation technique at room temperature then treated different annealing temperatures (373,473,and 573)K for one hour. Results of the Hall Effect and the electrical conductivity of (I-V) characteristics were measured in darkness and light.at different annealing temperature results show that the thin films have ability to manufacture solar cells, and found that the efficient equal to (2.18%) for structure solar cell (Algrid / CdS / CdTe /glass/ Al) and the efficient equal to (1.12%) for structure solar cell (Algrid / CdS / CdTe /Si/ Al) with thick ness of (1000) nm with CdTe thin films at RT.

Twenty five samples out of sixty wound swabs taken from burn patients were identified as P. aeruginosabacteria by conventional methods. Antibiotics susceptibility tests were performed against thirteen antibiotics. P. aeruginosa samples were treated with 0.5 mg/ml of Safranin O solution then irradiated with 532nm Q-switched Nd:YAG laser at four energy densities (0.324, 0.704, 1.380, and 1.831 J/cm2) for different times of 5, 8 and 11 minutes with 5Hz repetition rate. The viability, susceptibility to antibiotic and production of pyocyanin were determined before and after irradiation. The results showed that the number of CFU/ml of P. aeruginosa decreased with increasing the dose of irradiation. Complete killing of cells was observed at 1.8

Abstract:

Viral marketing has become one of the modern strategies adopted by organizations in the marketing of products and services. The idea of viral marketing focuses on the social relations between individuals and groups. As a result of the technological development, most organizations have resorted to using the Internet and its applications and social media to market and promote their products. To reach the largest number of consumers to display their products and services in many ways, including text, audio, visual or video and thus affect the behavior of the consumer.

The problem of the study was the following question (do viral marketing technologies have an impact on consumer behavior?)

In this research TiO2 nano-powder was prepared by a spray pyrolysis technique and then adds to the TiO2 powder with particle size (0.523 μm) in ratio (0, 5, 10, 15 at %) atomic percentage, and then deposition of the mixture on the stainless steel 316 L substrate in order to use in medical and industrial applications.
Structure properties including x-ray diffraction (XRD) and scanning electron microscope (SEM0, also some of mechanical properties and the effect of thermal annealing in different temperature have been studied. The results show that the particle size of a prepared nano-powder was 50 up to 75 nm from SEM, and the crystal structure of the powders (original and nano powder) was rutile with tetragonal cell. An improvement in