.Curcumin (Cur) and L phenylalanine (Phy) compounds were used to prepare two mixed ligand complexes with Cr (III) and Fe (III) ions. The synthesized complexes are characterized by using conductivity measurement and different spectral methods like FT-IR and UV- Vis .Molar conductance and analytical studies confirmed that the complexes exhibit octahedral geometry., suggest that the complexes are formed in 1: 1 :2 [ L : Metal : 2phe ] ratio and they proposed to have the general formulae [M(Cur)(phe)2] Cl (M= Cr (III) and Fe (III) The compound dyeing method was studied and applied to acrylic fabric.The antibacterial activity of curcumin, phenylalanine and their mixed ligand complexes were examined on pathogenic bacterial strains and showed good

The fabrication of Solid and Hollow silver nanoparticles (Ag NPs) has been achieved and their characterization was performed using transmission electron microscopy (TEM), zeta potential, UV–VIS spectroscopy, and X-ray diffraction (XRD). A TEM image revealed a quasispherical form for both Solid and Hollow Ag NPs. The measurement of surface charge revealed that although Hollow Ag NPs have a zeta potential of -43 mV, Solid Ag NPs have a zeta potential of -33 mV. According to UV-VIS spectroscopy measurement Solid and Hollow Ag NPs both showed absorption peaks at wavelengths of 436 nm and 412 nm, respectively. XRD pattern demonstrates that the samples' crystal structure is cubic, similar to that of the bulk materials, with

Nanoparticles generation by laser ablation of a solid target in a liquid environment is an easy method. Cadmium Telluride (CdTe) colloidal nanoparticles have been synthesized by laser ablation Nd:YAG with wavelengths of 1064nm and double frequency at 532 nm, number of pulses 50 pulses, with pulse energy= 620mJ, 700mJ of a solid target CdTe is immersed in double distilled deionized water (DDIW) and in methanol liquid. Influences of the laser energy and different solutions on the formation and optical characterization of the CdTe nanoparticles have been studied using atomic force microscope (AFM) and the UV-Vis absorption. As a results, it leads to the absorbance in UV-Vis spectra of samples prepared in water at laser wavelength of 532nm i

   This article includes the preparation of luminescence materials from rare earth (Eu ) ion doping Yttrium Oxide (Y₂O₃) 70% and SiO₂ 25% and study the characteristics of phosphors for ultraviolet to visible conversion. The phosphor materials have been synthesized by two steps: Preparing the powder by solid state method using Y₂O₃, SiO₂ and Eu₂O₃ with doping materials concentration (70%, 25% and 5%) respectively and different calcination temperature (1000, 1200 and 1400 ^oC).

   The second step is to prepare the colloid solution by dispersing the produced powder in a polyvinyl alcohol solution (4%) .

Powde

Biomimatic basic calcium phosphate ,known as Hydroxy apatite(HA), was
synthesised using calcium acetate and disodium phosphate dilute hot (boiling) solution of
both salts were added slowly to each other. A colloidal suspension formed was aged for few
days, then boiled for one hour to induced setting and coagulation of preapatite, and left to cool
until they reached room temperature.
The precipitate was filtered and washed with distilled water, then ethanol and dried.
The dried sample was calcined at 1100
o
C.The obtained solid lumps were then crushed
reground fine powder and analyzed for calcium to phosphorous ratio. X-ray analysis was
carried out to examine the solid sample. Chemical analysis for phos

The process for preparing activated carbon (AC) made from tea residue was described in this paper. Investigated were the physicochemical characteristics and adsorption efficiency of the produced AC. Activation with potassium hydroxide (KOH) and carbonization at 350 °C are the two key steps in the manufacturing of AC. The activated carbon was used to adsorb Tetracycline (TC). Different parameters were studied at room temperature to show their effects on the adsorption efficiency of TC. These parameters are the initial concentration of adsorbate TC, solution acidity pH, time of adsorption, and adsorbent dosage. The prepared active carbon was characterized using Fourier transform infrared spectroscopy (FTIR), scanning electron microsc

Schiff base of chitosan with Para-Dimethyl aminobenzaldehyde /PVA-Ag Nanocomposite have been prepared as antimicrobial polymer. The prepared chitosan Schiff base and chitosan Schiff base / PVA-Ag nanocomposite were characterized by FT-IR, SEM analysis and biological activity. The nanocomposite showed good activity against different types of bacteria.