Nanocrystalline micro-mesoporous ZSM/MCM-41 composite was synthesized using alkaline treatment method and two step of crystallization in poly tetraflouroethylene (PTFE) lined autoclave. The synthesized zeolites was characterized by X-Ray diffraction (XRD), Scanning electron microscopy (SEM), Transmission electron microscopy (TEM), Atomic force microscopy (AFM), Fourier transport infrared (FTIR), and N₂ adsorption-desorption (BET). It was approved that the best results for alkaline leaching can be got with 1.5M NaOH solution. High surface (BET) area of 630 m²/g with pore volume of 0.55 cm³/g has been got. AFM reports showed a nano-level size for average particle size of 50nm.

In this paper, some chalcone derivatives (C1, C2) were synthesized based on the reaction of equal amount of substituted acetophenone and substituted banzaldehyde in basic medium. Oxazine and thiazine derivatives were prepared from the reaction of chalcones (C1-C2) with urea and thiourea respectively in a basic medium. Pyrazole derivatives were prepared based on the reaction of chalcones with hydrazine mono hydrate or phenyl hydrazine in the presence of glacial acetic acid as a catalyst. The new synthesized compounds were identified using various physical techniques like1 H-NMR and FT-IR spectra.

The Mannich base ligand was synthesized in an ethanol medium through a condensation reaction of 2-mercaptobenzimidazole and ciprofloxacin at room temperature. Subsequently, several metal complexes of this ligand were prepared. To characterize both the base ligand and the metal complexes, various techniques were employed, including elemental analysis, FT-IR spectroscopy, UV-Vis spectroscopy, molar conductivity measurements, magnetic moment determination, and melting point analysis. The results were shown that the metal complexes formed have the formula [Cr(L)2Cl2] Cl.H2O and [Rh(L)2(H2O)2] Cl3.H2O, where L= mannich base ligand. Based on spectroscopic analytical, coordination with metal ions involves the 'N' donor atom of mannich base

Five membered heterocyclics derivatives were synthesized in this work by three routes. The first route includes the synthesis of N-benzoic acid 1,2,3,-triazole derivatives (3),(4) by diazotation of methyl-2-amino benzoate and treating the resulted salt (1) with sodium azide and ethyl acetoacetate or acetyl acetone, respectively. In the second route, derivatives of pyrazole (8) pyrazolin-5-one (9), (10) were prepared by the reaction of the salt (1) with some active methylene compounds to give the corresponding hydrazones derivatives (5-7) which then they were treated with hydrazine hydrate. The third route afforded the synthesis of three derivatives (12), (15a), (15b) of thiazolidinone by two different methods. AII compounds were confirmed b

           A  new  Schiff base  ligand  [2,3,8,9–tetra -phenyl-1,4,5,7,10,12-hexa azo-5,12- dihydro -6,11- dione 1,3,7,10-dudec-tetra-ene]  [H2L]  and  its  complexes In general formula [M(H2L)]Cl2 (where : M= CoII, NiII, and PdII) were prepared. This ligand was prepared in two steps,in the first step a solution of  benzil in methanol was reacted  under  reflux   with    semicarbazidhydrochlorid  to give an (intermediate compound)[benzyl bis–(Semicarbazone)] which was  reacted  in the  second   step with  benzil giving  the  mentioned  ligand. The

New 2-amino thiazole ,oxodiazole, sulphonilamide and diazin derivatives of N-(α-chloro aceto)-3-(tolyl imino)-5-bromo-2-oxo-indole(2) have been synthesized .The preparation process started by the reaction of 5-bromo isatin with  P-toluidine in the presence of glacial acetic acid and dimethylformamide(DMF) as a solvent to give  3-(tolyl imino)5-bromo-1H-indole-2-one.(1), Compound (1) with sodium hydride  in dimethylformamide(DMF) at 0C0 gave a suspension of the sodium salt of Schiff base derivative and subsequent reaction with monochloroacetylchloride obtained  the intermediate compound(2).Compound(2) was  reacted with different reagents  in four routes.The first route involved direct reaction with substituted  2-aminobenzothiazole u

    Ni2O3 nanomaterial, a phase of nickel oxide, is synthesized by a simple chemical process. The pure raw materials used in the present process were nickel chloride hexahydrate NiCl2.6H2O and potassium hydroxide KOH by utilizing temperature at 250 oC for 2 hour.  The structural, morphological and optical properties of the synthesized specimens of Ni2O3 were investigated employing diverse techniques such as XRD, AFM, SEM and UV-Vis, respectively. The XRD technique confirms the presence of Ni2O3 nanomaterial with crystal size of 57.083 nm which indexing to the (2θ) of 31.82; this results revealed the Ni2O3 was a phase of nickel oxide with Nano structure. The synthesized Ni2O3 will be useful in manufacturng electrodes materials f