In this study many specimen s were prepared from 2024-T3 Aluminum alloy for corrosion test by the dimensions of (15*15*3) mm according to ASTM G71-31 and then subjected to shot peening process at different time (15, 30, 45) minutes using steel ball having a diameter of 2.75 mm and Rockwell Hardness of 55R_C to induce compressive residual stress which were measured using X-Ray diffraction method, surface roughness and   hardness were tested before and after peening. Electrochemical corrosion test by Tafel extrapolation method was carried out in an environment of 3 .5% NaCl solutions (sea water) where Corrosion rate calculated using Tafle equation.

The obtained results show a favorable influence of SP treatment

This research study examines the impact of information technology on firm profitability and stock returns. Using a comprehensive dataset of firms across various industries, this research employs rigorous statistical analysis techniques to investigate the relationship between IT investments, firm profitability metrics, and stock returns. The study focuses at how IT investments affect financial performance measures including return on assets (ROA) and return on equity (ROE), with P-values of 0.34 and 0.12, respectively. Furthermore, the study investigates the influence of IT on stock returns, taking into account market capitalization, industry trends, and macroeconomic variables. This study's conclusions center on the beneficial assoc

The present paper includes a study of color variation in Iraqi Collared dove Streptopelia decaocto. Three different populations have been recognized: the southern population which belongs to the Indian race, the northern population to the Eurasian race; the dark and light color variation occurs in the Baghdad population because of hybridisation between the two races, found infected with two cestodes,  Raillietina echinobothrida found  in most of our specimens, while the dark face found beside R. echinobothrida infected with Idiogenes sp. getting it probably from vertebrate sources. We believe that most of the Baghdad population was intermediate between north and south races.

Writing in English language demands both mental skills and a suitable level of language proficiency. Some studies showed that writing anxiety has an impact on the acquisition of language learning. This study; however, teaches the cognitive strategies (PLAY & WRITE) as a writing strategy, so as to decrease students’ use of it when experiencing writing anxiety at the academic writing level. The sample has been (100) second-stage Department of English learners at the College of Education (Ibn –Rushd), in the University of Baghdad-Iraq. They have been randomly selected and divided into experimental and control groups; (50) students in each group. To achieve the objective of the study, SLWAI questionnaire has been distributed to the e

Furfural is a toxic aromatic aldehyde that can cause a severe environmental problem especially the wastewater drown from petroleum refinery units. In the present work, a useless by-product from local furniture manufacturing industry; sawdust was used as raw material for the preparation of activated carbon which is chemically activated with phosphoric acid. The effect of adsorption variables which include initial pH of solution (2-9), agitation speed (50-250) rpm, agitation time (15-120) min, initial concentration of furfural (50-250) ppm, and amount of adsorbent material (0.5-2.5) g for the three adsorbents used (prepared activated carbon, commercial activated carbon and raw sawdust) were investigated in a batch process

In this work the effect of annealing temperature on the structure and the electrical properties of Bi thin films was studied, the Bi films were deposited on glass substrates at room temperature by thermal evaporation technique with thickness (0.4 µm) and rate of deposition equal to 6.66Å/sec, all samples are annealed in a vacuum for one hour. The X-ray diffraction analysis shows that the prepared samples are polycrystalline and it exhibits hexagonal structure. The electrical properties of these films were studied with different annealing temperatures, the d.c conductivity for films decreases from 16.42 ? 10-2 at 343K to 10.11?10-2 (?.cm)-1 at 363K. The electrical activation energies Ea1 and Ea2 increase from 0.031 to 0.049eV and