Recent research has examined the improvement of physical and dielectric properties of BaTiO₃ ceramic material by small addition of excess TiO₂ or BaCO₃. The prepared samples sintered at different temperatures and varying soaking time. The results show that increasing the sintering temperature within 1350°C and soaking time of 10 hrs give better electrical and physical properties, which indicate the reaction is complete at higher temperature and period.

Hydroxide upon the chemical composition and dry matter(DM) and organic matter(OM) digestibility . Rice straw was treated with 4% sodium hydroxide using 30% of DM basis moisture, and incubated at 40 ºC for 40 days., DM digestibility (DMD) was significantly affected (P<0.01) by the treatment , where DMD increased The objective of this experiment was to study the effect of physical form (long ,chopped and ground ) and washing rice straw treated with sodium from 42.32 to 45.41% , OM digestibility (OMD) and total digestible nutrient (TDN) increased(P<0.05) from 47.38 and 49.33 to 49.67 and 52.83% ,respectively. While hemicellulose content increased (P<0.05 ) from 261.71 to 268.17 gm/kg DM ,and metabolizable energy (ME) from 7.11 to 7.48 MJ/

Field experiment was conducted to test the effect of saline water 2 and7 dSm-1 potassium fertilizer rate 150,300 and 450 kg/donum on nitrogen fixation in Pisum sativum L. nodules. The experiment included anatomy study .Results water salinity ( 2,7 dSm-1) as a main plot and fertilizer rates as a sub plot. Results indicated that irrigation with saline water 7 dSm-¹ caused a significant decrease in N contents especially in the lower parts of the plants. The percentage of the N decreased in lower leaves to (0.01%) under 7dSm-¹ and 300 kg/donum fertilizer; however the percentage increased in the upper leaves to (2.80%) under with 2dSm-¹of irrigation water and 300 kg/ donum fertilizer rate. Fresh weight decreased to 6.26g under 7 dSm

The aim of this work is to produce samples from Iraqi raw materials like Husyniat Bauxite (raw and burnt) and to study the effect of some additives like white Doekhla kaolin clays and alumina on that material properties were using sodium silica as a binding material. Five mixtures were prepared from Bauxite (raw and burnt) and kaolin clays, with an additive of (40) ml from sodium silica and alumina of (2.5, 5, 7.5,10 wt %) percentage as a binding material. the size grading was through sieving. The formation of all specimens was conducted by a measured gradually semi-dry pressing method under a compression force of (10) Tons and humidity ratio ranging from (5-10) % from mixture weight. Drying all specimens was done and then they were burn