‎ Sixteen new complexes with the general formula [M(L)2(H2O)2] were ‎prepared resulting from the reaction of the two new Schiff base ligands, which ‎are‏: -‏ L1= (E)-5-((2-hydroxybenzylidene)amino)-2-phenyl-2,4-dihydro-3H-pyrazol-3-one)‎ L2 = (E)-5-((2-hydroxy-3-methoxybenzylidene)amino)-2-phenylpyrazolidin-3-one) ‎ ‎ With divalent metal ions (manganese, cobalt, nickel, copper, zinc, cadmium, ‎mercury) and (tetravalent platinum).‎‏ ‏ ‎ Ligands was derived from the reaction of the amine (5-amino-2-phenyl-2,4-‎dihydro-3H-pyrazol-3-one) with Salicylaldehyde and ortho-vanillin, which is ‎linked to the metal ions via the nitrogen atoms are the isomethene group and ‎the oxygen is the hydroxide group of t

Wet granulation method was used instead of conventional pan coating  or fluidized –bed coating technique to prepare enteric-coated diclofenac sodium granules, using ethanolic solution of Eudragit^TM L100 as coating, binding and granulating agent .Addition of PEG400 or di-n-butyl phthalate as a plasticizer was found to improve the enteric property of the coat.

Part of the resulted granules was filled in hard gelatin capsules (size 0), while the other part was compressed into tablets with and without disintegrant.

The release profile of these two dosage forms in 0.1N HCl (pH 1.2)for 2 hours, and in phosphate buffer (pH 6.8) for 45 minutes as well as the release kinetic were compared with that of the en

The current study aimed to adopt a method for inducing callus cells and regenerating the important common red bean using different types of growth regulators such as N6-benzylaminopurine (BAP), Naphthalene acetic acid (NAA), and Thidiazuron (TDZ). Different types of common bean pinto cultivar explants, such as internodes, cotyledons and roots, were inoculated on Murashige and Skoog medium (MS) provided with different combinations of plant growth regulators, including 1- BAP (5 mg/l) 2-BAP (4.5 mg/l) NAA (0.5 mg/l), 3- BAP (4.5 mg/l), and TDZ (0.1mg/l). Callus was initiated on MS culture medium supplied with 5 mg/l BAP for all explants (internodes, cotyledons, and roots) at 50, 20, and 10% respectively, while adding NAA with 0.5mg/l showed

Abstract: In this research, nanofibers have been prepared by using an electrospinning method. Three types of polymer (PVA, VC, PMMA) have been used with different concentration. The applied voltage and the gap length were changed. It was observed that VC is the best polymer than the other types of polymers.

In this research, nanofibers have been prepared by using an electrospinning method. Three types of polymer (PVA, VC, PMMA) have been used with different concentration. The applied voltage and the gap length were changed. It was observed that VC is the best polymer than the other types of polymers.

The aim of this research is to benefit from recycl the aircraft waste oils which is discarded in sewage network, to be used in preparation of greases for industrial purposes and to reduce the environmental pollution. In this research synthetic greases were prepared with special specifications by mixing the waste oils after treating with (silica gel as adsorbent agent, and filtration to precipitate impurities then heated to 110 C? to get rid of water) bentonite produced in Iraq which is available and cheap with existence of high density polyethylene at specific conditions of ( heating and mixing) . The best weight proportion were reached, then paraffin wax and additives were added to improve the properties of grease and give the

Polyvinyl alcohol, (PVA) was prepared using polyvinyl acetate emulsion (manufactured by Al-Jihad factory,
That-Al-Sawary Company) as a local raw material. In this investigation, polyvinyl acetate emulsion was converted to
solid form by coagulation the polymer from its emulsion using sodium sulphate salt as coagulant aid, then alcoholyzed
the solid polyvinyl acetate in methanol using sodium hydroxide as catalyst, polyvinyl alcohol produced by this method is
a dry, white to yellow powder.
Three affecting variables on the degree of hydrolysis of PVA were studied, these variable are Catalyst to
polymer weight ratio in the range of 0.01 – 0.06, reaction time in the range of 20 – 90 min, and reaction temperature in
the

Background: The formation of white spot lesions around fixed orthodontic attachments is a common complication during and after fixed orthodontic treatment, which hinders the result of a successfully completed orthodontic treatment. The aim of the study was to assess the effectiveness of the Caries Infiltrant (ICON®) on prevention of caries on the smooth enamel surface when applied alone or combined with conventional adhesives. Materials and methods: Seventy eight human premolar enamel discs were randomly assigned to six groups (n=13). The discs were etched and treated with resins of different monomer content forming the following groups: (1)Untreated etched samples served as the negative control, (2) ICON® (DMG), (3) Adper™ S

Background: White spot lesions are esthetic problems caused by subsurface enamel demineralization that seen as white opacity. Aim of the study: This study aimed to evaluate and to compare the color change after the treatment of the white spot lesions with resin ‹nϔ‹Žtrƒt‹on and micro abrasion. Materials and Methods: rt‹ϔ‹…‹ƒŽ white spot lesions were generated on 48 premolar teeth by the use of a demineralization solution. The teeth were randomly divided using the Diagnodent into three study groups (16 teeth for each group) depending on the depth of the induced lesions: outer enamel, inner enamel and outer dentine. Then each group was fatherly subdivided into two groups (8 teeth for each group) the ϔ‹rst group was treated wit

Premature degradation is the problem of maxillofacial silicones, significantly affected by ultraviolet exposure, contributing to silicones photodegradation. Degradation necessitates frequent replacement of prostheses that increase the total cost of rehabilitation.