In this work, varying compositions of SiO₂ micro filler were added
with the Polyvinyl Chloride (PVC) and samples have been prepared
using film casting technique. The results have been analyzed and
compared for PVC samples with (1 wt%, 3 wt%, 5 wt% and 10 wt%)
SiO2 micro filler. Mechanical characteristics such as tensile strength,
elongation at break and Young`s modulus were measured for all the
samples, where the tensile strength was increased from 8.39 Mpa for
purified PVC to 16 Mpa for 3% SiO₂/PVC composite. Also, thermal
conductivity measurement values illustrated that composite materials
have a good thermal insulation at 10 wt. %, thermal conductivity was
decreased from 0.1684 W/m.

Background: Poly (methylmethacrylate) is the most widely used material in denture fabrication. The characteristics of acrylic resin which support microorganism development can threaten the oral health of denture users. This study was assigned to prepareand incorporate Ag-Zn zeolite powder into heat cured denture base material as antimicrobial material and to investigate its effect on some properties of heat cured acrylic denture base materials. Materials and methods: Sliver –zinc zeolite was prepared by ion exchange method and characterized then incorporated into poly (methylmethacrylate) powder in0.5% by weight. Specimens were constructed and divided into 6 groups according to the using tests; each group was subdivided into 2 groups

The study was conducted to identify the toxicity of chromium on scenedesmus quadricauda algae alone and in the presence of nutrient metal (Nitrogen). Different concentrations of chromium (0.5, 1.5 , 2.5, 3.5 , 4.5mg/L) were used and the presence nitrogen is (5 ,10 ,50 ,100mg/L) on cultur media(chu-10) with used for cultivation of the algae in controlled conditions(25oC , light intensity 380 –?E/m2 /s. The results showed increasing in the toxicity of the metal when is alone , excess of concentrations an time of exposure. The growth rate decreased from 0.44 to 0.06 cell/ hour after 12 day of the biging of the experiment and of concentrate 4.5 mg/L of chromium. The intermediate active concentrations of the chromium(EC50) was increase

Four local hemolysin producer bacterial isolates were selected, tow of them gram negative bacteria (Escherichia coli ,Pseudomonas aeruginosa ) and the other two were gram positive bacteria (Staphylococcus aureus , Bacillus cereus ). Minimum inhibitory concentration of the aqueous and alcoholic extracts of Punica granatum L. pericarp were determined towards the four bacterial isolates ,results obtaind showed that MICs of the aqueous extract were 200 mg/ml for E .coli and P. aeruginosa isolates while were 5 mg/ml and 2 mg/ml for B. cereus, S. aureus , respectively The MICs for the ethanolic extract were 50 mg/ml , 20 mg/ml ,1 mg/ml ,0.5 mg/ml for E. coli ,P. aeruginosa ,B. cereus ,S. aureus , respectively. The effect of Sub-MICs o

This study deals with the impact of leadership styles in its three main dimensions (democratic, autocratic, lenient) as an independent variable of the dimensions of functional combustion (emotional stress, inhumanity, personal achievement). The research sought to achieve a set of goals, the most prominent of which are: studying the reality of the researched organization to identify the leadership patterns used in its management and its impact on the phenomenon of functional combustion, Moreover, knowing the extent of support for these established patterns and their contribution to mitigating the phenomenon of functional combustion in the organization's environment, and testing the impact of these leadership patte

Background: This study was formulated to compare the effect of 5%hydrofluoric acid in comparison to 37%phosphoric acid with and without the application of silane on bond strength of composite to porcelain. Materials and Methods: Specimen preparation was divided in to two phases, metal-disks fabrication (8mm-diameter and 4mm-thickness) and ceramic veneering. Thirty two specimens were prepared, sandblasted with 50 μm aluminum oxide, and divided into four groups of eight samples. Groups I and III were etched with 37%phosphoric acid while groups II and IV were etched with 5%hydrofluoric acid; and groups I and II were silaneted while groups III and IV were not. Heliobond, and resin composite were applied to each specimen using a plastic transpa

Background: Psychological stress is considered the major etiological factor precipitating myofacial pain and temporomandibular disorders.It is known that stress induce various adaptational responses of physiologic systems. The process includes increase in the activity of the hypothalamic-pituitary-adrenal axis which promotes cortisol secretion. Salivary cortisol has been used as a measure of free circulating cortisol levels.The use of salivary biomarkers has gained increased popularity since collecting samples is non-invasive and painless. The aim of thisstudy was to evaluate the level of cortisol in saliva among sample of university students having myofacial pain, during the final exam period and whether this finding could have a significa

In this study, the effect of Nd: YAG laser on the activity of superoxide dismutase (SOD) and alcoholdehydrogenase (ADH) was investigated. The Saccharomyces cells were irradiated using 532nm Q-Switched Nd: YAG laser with (1Hz) frequency. Different fluences 11.3, 22.6 and 33.9mJ/cm2 and different number of pulses 15, 30 and 60 pulse were used. The irradiated cells were incubated in a liquid nutritive medium for 24 hours. After incubation, the cells were harvested and disrupted to extract the intracellular enzymes and their activities were assessed. In comparison with the control, the irradiated cells showed a significant increase in the activity and the specific activity of SOD at energy densities of 11.3 and 22.6mJ/cm2 at 30 and 60 pulses

Background Microorganisms and fungal growth especially Candida albicans, on soft denture lining material are the most common problem which can lead to chronic mucosal inflammation. The aim of this study was to evaluate the effect of zirconium nanoparticles into acrylic-based heat cured soft denture lining material against Candida albicans, and the amount of zirconium ion release of soft liner/ZrNPs composite. Furthermore, evaluate shear bond strength after ZrNPs addition to soft liner. Materials and methods: Zirconium nanoparticles were added into acrylic-based soft denture liner in various percentages (1%, and 1.5% by weight). Two hundred and fifty specimens were arranged and isolated into four groups as per the test to be done The antifu