The present research was conducted to reduce the sulfur content of Iraqi heavy naphtha by adsorption using different metals oxides over Y-Zeolite. The Y-Zeolite was synthesized by a sol-gel technique. The average size of zeolite was 92.39 nm, surface area 558 m2/g, and pore volume 0.231 cm3/g. The metals of nickel, zinc, and copper were dispersed by an impregnation method to prepare Ni/HY, Zn/HY, Cu/HY, and Ni + Zn /HY catalysts for desulfurization. The adsorptive desulfurization was carried out in a batch mode at different operating conditions such as mixing time (10,15,30,60, and 600 min) and catalyst dosage (0.2,0.4,0.6,0.8,1, and 1.2 g). The most of the sulfur compounds were removed at 10 min for all catalyst types. The maximum

    The study included isolation and diagnosis of fungi that infect Foeniculum vulgare Mill planted in the Department of Drugs and Medicinal Plants, Pharmacy College - University of Baghdad, different symptoms such as wilting and yellowing, stunting on the plants were observed fungi: Alternaria alternata, Rhizoctonia solani, Phoma herbarum and Fusarium oxysporum, The disease incidence ranging between 5-10%. Studied the effect of Foeniculum vulgare plant seeds extract against Alternaria alternata, Rhizoctonia solani, Phoma herbarum and Fusarium oxysporum,where tested  the concentrations  0,2.5 and 5%  of alcoholic extract of fennel seeds showed ef

Fluconazole was used to test the susceptibility of Candida albicans isolated from different clinical samples, and to detect mutations in ERG11 gene, and their relationship to fluconazole resistance. Forty-eight isolates of Candida albicans were tested for susceptibility using the disc diffusion method (M-44). ERG11 genes of six isolates were amplified (four resistant, two susceptible) and sequenced. The sequenced genes were analyzed to detect the mutations. Out of 48 isolates of Candida albicans, 4 (8%) were resistant to fluconazole. Sixteen-point mutations were detected included 13 silent mutations, and three missense mutations. The mutations of A945C (E266D) and G1609A (V488I) were found only in susceptible Candida albicans isolates, whil

The removal of heavy metal ions from wastewater by sorptive flotation using Amberlite IR120 as a resin, and flotation column, was investigated. A combined two-stage process is proposed as an alternative of the heavy metals removal from aqueous solutions. The first stage is the sorption of heavy metals onto Amberlite IR120 followed by dispersed-air flotation. The sorption of metal ions on the resin, depending on contact time, pH, resin dosage, and initial metal concentration was studied in batch method .Various parameters such as pH, air flow rate, and surfactant concentration were investigated in the flotation stage. Sodium lauryl sulfate (SLS) and Hexadecyltrimethyl ammonium bromide (HTAB) were used as anionic and cationic surfactant re

Activated carbon prepared from date stones by chemical activation with ferric chloride (FAC) was used an adsorbent to remove phenolic compounds such as phenol (Ph) and p-nitro phenol (PNPh) from aqueous solutions. The influence of process variables represented by solution pH value (2-12), adsorbent to adsorbate weight ratio (0.2-1.8), and contact time (30-150 min) on removal percentage and adsorbed amount of Ph and PNPh onto FAC was studied. For PNPh adsorption,( 97.43 %) maximum removal percentage and (48.71 mg/g) adsorbed amount was achieved at (5) solution pH,( 1) adsorbent to adsorbate weight ratio, and (90 min) contact time. While for Ph adsorption, at (4) solution pH, (1.4) absorbent to adsorbate weight ratio, and (120 min) contact

In this study, Al2O3 thin films were prepared by dc reactive sputtering technique using different gas mixtures of argon and oxygen gases (90:10, 70:30, 50:50, 30:70, and 10:90). These films were characterized to introduce their surface morphology and elemental composition as functions of the oxygen content in the gas mixture. The gas mixing ratio plays a crucial role in controlling the nanoscale morphology of the prepared thin films. The [Al]/[O] ratio varies non-linearly with the Ar:O2​ mixing ratio. Increasing the oxygen content leads to a progressive decrease in surface roughness, resulting in smoother and more uniform films with finer granular features. These results presented herein are useful to optimize the sputtering process to ac