Curing of concrete is the maintenance of a satisfactory moisture content and temperature for a
period of time immediately following placing so the desired properties are developed. Accelerated
curing is advantages where early strength gain in concrete is important. The expose of concrete
specimens to the accelerated curing conditions which permit the specimens to develop a significant
portion of their ultimate strength within a period of time (1-2 days), depends on the method of the
curing cycle.Three accelerated curing test methods are adopted in this study. These are warm water,
autogenous and proposed test methods. The results of this study has shown good correlation
between the accelerated strength especially for

The twelve samples of agricultural soils from four regions in Al-Najaf governorate with sampling plant with soil. Physical properties of the soil where studied, such as electrical conductivity ranged from (136.33-1070.00)μS/cm^-3, and moisture which ranged between the values (0.39-36.48)%. The chemical analysis of the soil have included the proportion of calcium carbonate the ratio between (44.00-48.00%) has been observed increasing amounts of calcium carbonate in surface models. The pH where results indicate that pH values ​​were close to study models ranged between (6.88-7.42) these values ​​generally within the normal range for the measured pH values ​​of the Iraqi soil. The amount of gypsum ranged betwe

Background:Amino acid disorders are a major group of inborn error metabolism (IEM) with variable clinical presentation; its diagnosis constitutes a real challenge in a community with high consanguinity rate and no systematic newborn screening.

Objectives: to provide data about amino acid disorders detected in high-risk Iraqi children by using quantitative amino acid fluorescent high performance liquid chromatography (HPLC) analysis.

Type of the study: Cross-sectional study.

Methods: a descriptive cross sectional study from 1st February to 1st December 2014, at Neurological ward and clinic of the Children Welfare teaching Hospital, in Baghdad - Ira

Inthisstudy,FourierTransformInfraredSpectrophotometry(FTIR),XRay Diffraction(XRD)andlossonignition(LOI),comparativelyemployedtoprovideaquick,relativelyinexpensiveandefficientmethodforidentifyingandquantifyingcalcitecontentofphosphateoresamplestakenfromAkashatsiteinIraq.Acomprehensivespectroscopicstudyofphosphate-calcitesystemwasreportedfirstintheMid-IRspectra(4004000cm-1)usingShimadzuIRAffinity-1,fordifferentcutsofphosphatefieldgradeswithsamplesbeneficiatedusingcalcinationandleachingwithorganicacidatdifferenttemperatures.Thenusingtheresultedspectratocreateacalibrationcurverelatesmaterialconcentrationstotheintensity(peaks)ofFTIRabsorbanceandappliesthiscalibrationtospecifyphosphate-calcitecontentinIraqicalcareousphosphateore.Theirpeakswereass

Background: Dental implant surface technologies have been evolving rapidly to enhance a more rapid bone formation on their surface and improve implant therapy.Implant threads should be designed to increase surface contact areathat induced better stability. In addition, implant surface coating with Flaxseed was used to enhance bone formation at the bone-implant interface. Materials and methods: Ninety-six commercially pure titanium (CpTi) screws were implanted in rabbits' tibiae and divided into three groups as dual-threaded group, flaxseed-coated group and control group. All groups were evaluated mechanically, histologically and radiographically after each healing periods (2, 4, 6 and 8) weeks and the resulting data were statistically analy

In this research the hard chromium electroplating process, which is one of the common methods of overlay coating was used, by using chromium acid as source of chromium and sulphuric acid as catalyst since the ratio between chromic acid and sulphuric acid is (100 : 1) consequently. Plating process was made by applying current of density (40 Amp / dm²) and the range of solution temperature was (50 – 55^oC) with different time periods (1-5 hr). A  low carbon steel type (Ck₁₅) was used as substrate for hard chromium electroplating. Solid carburization was carried out for hard chromium plating specimen at temperature (925^oC) with time duration (2 hr) to be followed with quenching and tempering