ZnTe possesses the proper optoelectronic properties as a candidate for device development. The structure and optical properties of ZnTe semiconductor thin films of 500 nm were studied using thermal evaporation technique. The influence of annealing temperatures on ZnTe thin films in the range ( R.T - 473 K). XRD and surface morphological analyses are used to examine the films. The ZnTe films are comparatively polycrystalline and cubic in phase, according to the XRD analysis. with a lattice constant of 0.61 nm upon an (111) orientation. The intensities of all the peaks rapidly increase though they show the same tendencies; it shows the crystallinity of the films becomes higher crystal size diameters (from 8.41 to 12.18nm) both increas

Modified unsaturated polyester (MUPE) was blended with Cellulose (Cls) and with ethyl cellulose (ECls) at ambient conditions in the presence of ethyl methyl ketone peroxide (EMKP) as hardener. The blends containing different weight percentages (5-25 %) of Cls or ECls. Mechanical properties (impact strength, hardness, and bending) and dielectric constant were determined. The results observed that Cls increases the impact strength, hardness, and dielectric constant and decreases the bending of the MUPS, while ECls causes an increase in the three mechanical behaviours and a decrease in the dielectric constant of the MU-PS.

Pure and doped barium titanate with Mg2+ ion at two molar ratios x= (5%, 10%) mol. has been synthesized by solid state reaction technique. The powders sintered at two temperatures (1000 °C and 1400 °C). An XRD technique was used in order to study the crystal structure of pure and doped barium titanate, which confirmed the formation of the tetragonal phase of BaTiO3, and then calculate the lattice parameters of pure and doped barium titanate, the addition of magnesium ion Mg2+ can lead to decreases lattice parameters.

Pure and doped barium titanate with Mg2+ ion at two molar ratios x= (5%, 10%) mol. has been synthesized by solid state reaction technique. The powders sintered at two temperatures (1000 °C and 1400 °C). An XRD technique was used in order to study the crystal structure of pure and doped barium titanate, which confirmed the formation of the tetragonal phase of BaTiO3, and then calculate the lattice parameters of pure and doped barium titanate, the addition of magnesium ion Mg2+ can lead to decreases lattice parameters.

This Study aimed to studying the effect of Volatile oil extracted from the leaves of Myrtus communis on the growth and activities of the following types of bacteria: Staphylococcus aureus, Streptococcus pyogenes, Klebsilla pneumoniae, Pseudomonas aeruginosa, and the yeast Candida albicans. The results showed an inhibitory effect of the oil on both the growth and activity of the tested microbes. This was reflected by the minimum inhibitory concentration (MIC) of Staphylococcus aureus, Streptococcus pyogenes, Klebsilla pneumoniae, Pseudomonas aeruginosa which was: (2.5, 1.25, and 2.5,5 % respectively), and the yeast (5) %. Also, the Minimum bactericidal concentration (MBC) to the bacteria mentioned above was (5, 2.5,5,10 % respectivel

Four complexes of Co(II),Ni(II),Cu(II) and Zn(II) with the azo ligand (4-chloro-N-(2-(dimethylamino)ethyl)-5-((2-hydroxy- 4,6-dimethylphenol)diazenyl)-2-methoxybenzamide) L. The structure of ligand and complexes were confirmed on the basis of their analytical and spectral data, these dyes were tested as dyeing in cotton fabric, and also testing in light and cleaner firmness. Also, antimicrobial and antifungal activities of ligand and their complexes were evaluated and the results showed that the ZnL compound showed the higher antibacterial activity with inhibition zone of 13mm against Staphyloco-ccus epidermidis, Steptococcus sp. and Escherichia coli compared with ligand and other metal complexes .In case of ZnL compound the antifungal acti

Four complexes of Co(II),Ni(II),Cu(II) and Zn(II) with the azo ligand (4-chloro-N-(2-(dimethylamino)ethyl)-5-((2-hydroxy-4,6-dimethylphenol)diazenyl)-2-methoxybenzamide) L. The structure of ligand and complexes were confirmed on the basis of their analytical and spectral data, these dyes were tested as dyeing in cotton fabric, and also testing in light and cleaner firmness. Also, antimicrobial and antifungal activities of ligand and their complexes were evaluated and the results showed that the ZnL compound showed the higher antibacterial activity with inhibition zone of 13mm against Staphyloco-ccus epidermidis, Steptococcus sp. and Escherichia coli compared with ligand and other metal complexes .In case of ZnL compound the antifungal activ

 Polyaniline organic Semiconductor polymer was prepared by oxidation polymerization by adding hydrochloric acid concentration of 0.1M and potassium per sulfate concentration of 0.2M to 0.1M of aniline at room temperature, the polymer was deposited at glass substrate, the structural and optical properties were studies through UV-VIS, IR, XRD measurements, films have been operated as a sensor of vapor  H₂SO₄ and HCl  acids.

Nanocomposite was prepared using unsaturated polyester (UP) resin as a matrix and graphene nanoparticles as a reinforcement material in six percentage weights (0, 0.1, 0.2, 0.3, 1 and 1.5%). Mechanical, calorimetric and thermal studies were performed on the (UP) resin/graphene nanocomposite. All tests showed a clear improvement of all mechanical properties examined (hardness, flexural strength (F.S), impact strength (I.S) and tensile strength (T.S)) with increasing graphene percentage. In addition, the temperature of glass transition and thermal conductivity of this composite increased with increasing graphene content.