No-fine concrete (NFC) is cellular concrete and it’s light weight concrete produced with the exclusion of sand from the concrete. This study includes the mechanical properties of lightweight reinforced by steel fiber, containing different proportions of steel fiber. This study was done using number of tests. These tests were density, compressive strength, flexural strength and absorption. These tests of the molds at different curing time. The results of tests that implication of fiber to No. fine concrete did not affect significantly on the compressive strength, While the flexural strength were gets better. Results explained that, the flexural strength of (1%) fiber No- fine concrete molds are four times that of the reference mold

The present investigation considers the effect of curing temperatures (30, 40, and 50˚C) and curing compound method on compressive strength development of high performance concrete, and compares the results with concrete cured at standard conditions and curing temperature (21˚C). The experimental results showed that at early ages, the rate of strength development at high curing temperature is greater than at lower curing temperature, the maximum increasing percentage in compressive strength is 10.83% at 50C˚ compared with 21C˚ in 7days curing age. However, at later ages, the strength achieved at higher curing temperature has been less, and the maximum percentage of reduction has been 5.70% at curing temperature 50C˚ compared with 21

In this paper, CdS/Si hetrojunction solar cell has been made by
Chemical Bath Deposition (CBD) of CdS thin film on to
monocrystalline silicon substrate. XRD measurements approved that
CdS film is changing the structure of CdS films from mixed
hexagonal and cubic phase to the hexagonal phase with [101]
predominant orientation. I-V characterization of the hetrojunction
shows good rectification, with high spectral responsivity of 0.41
A/W, quantum efficiency 90%,and specific detectivity 2.9*1014
cmHz1/2W -1 .

Room temperature ionic liquids show potential as an alternative to conventional organic membrane solvents mainly due to their properties of low vapour pressure, low volatility and they are often stable. In the present work, the technical feasibilities of room temperature ionic liquids as bulk liquid membranes for phenol removal were investigated experimentally. In this research several hydrophobic ionic liquids were synthesized at laboratory. These ionic liquids include (1-butyl-3-methylimidazolium bis (trifluoromethylsulfonyl) imide[Bmim][NTf₂], 1-Hexyl-3-methylimidazolium bis (trifluoromethylsulfonyl) imide[Hmim][NTf₂], 1-octyl-3-methylimidazolium bis (trifluoromethylsulfonyl)imide[Omim][NTf₂],1‐butyl

Background: A global health concern is methicillin-resistant Staphylococcus aureus (MRSA). The use of bacteriophages is one of the many novel control strategies against MRSA that are frequently sought. However, it is quite challenging to isolate enough lytic anti-MRSA phages. In order to extract, optimize, and remodel anti-MRSA phages, this study sought novel approaches.

Methods: Two ATCC MRSA strains and nine clinical MRSA isolates were used to isolate wild anti-MRSA phages from hospital settings, dirt, and sewage. The wild phages were optimized using plaque-based biokinetic techniques. Usi

The study showed that all extracts (aqueous, ethanolic and acetonic) of the leaves of Eucalyptus and Myrtus plants had a inhibitory effect on the growth of all types of yeasts studied, acetone extract recorded the highest inhibition of yeastat 100ppm concentration,The inhibition was 35mm, 34mm, 24mm and 20mm for Candida parapsilosis, Candida glabrata, Candida tropicalis and Candida albicans respectively, The experiments above showed the least significant differences at 0.05 level.The results ofE. Cammldulensis ethanolic tincture analysis has shown the presence of 44 biologically active substances. The main Eucalyptus leaves component was: 2-Bicyclo (2-2.1) heptanol (12.37%), Ledol (8.23%),1,2,4- Benzenetriol (8.45%) and that contain spathul

The aim of this study was to isolate and identify the cyanobacterium Scytonema hofmanni Var. calcicolum from the domestic drinking tanks as a new record in Iraqi drinking water. Scytonema hofmanni var. calcicolum, a filamentous freshwater cyanobacterium (blue-green alga). This alga was isolated from the walls of the domestic plastic water tanks in Al- karkh/ Baghdad city on July 2014. The sampling was performed by collecting three samples from this tanks, the three examined samples microscopically revealed the dominance of this cyanobacterium as unialgal in the studied samples. The results showed this alga has the ability to tolerate high temperature up to 42 Cº and very low light intensity inside the tanks which up to 10 μE/m²/s.

Abstract The surface of kaolin was diagnosed by an AFM and the results were shown The height of the highest peak reached by a quantity of Kaolin ‎surface is 2.5 µm, the granules, and their diameter with an average diameter of 666.1nm. Using Kaolin's adsorption properties, erythrosine was removed of its aqueous solution. It was determined that the maximal dye adsorption ranged 36.53–40.61%. ‎‎‎‎The results of using the Freundlich, Langmuir, and Temkin adsorption isotherms revealed that at temperatures of (298,308,318) K, the Freundlich model was followed, the Langmuir model did not match, and the Temkin model could only be partially applied. There is also physical adsorption. One of the three kinetic models of the