This research foxed on the effect of fire flame of different burning temperatures (300, 400 and 500)oC on the compressive strength of reactive powder concrete (RPC).The steady state duration of the burning test was (60)min. Local consuming material were used to mixed a RPC of compressive strength around (100) MPa. The tested specimens were reinforced by (3.0) cm hooked end steel fiber of (1100) MPa yield strength. Three steel fiber volume fraction were adopted in this study (0, 1.0and 1.5)% and two cooling process were included, gradual and sudden. It was concluding that increasing burning temperature decreases the residual compressive strength for RPC specimens of(0%) steel fiber volume fraction by (12.16, 19.46&24.49) and (18.20, 27.77 &3

In this study, geopolymer mortar was designed in various experimental combinations employing 1% micro steel fibers and was subjected to different temperatures, according to the prior works of other researchers. The geopolymer mortar was developed using a variety of sustainable material proportions (fly ash and slag) to examine the influence of fibers on its strength. The fly ash weight percentage was 50%, 60%, and 70% by slag weight to study its effect on the geopolymer mortar's properties. The optimal ratio produced the most significant results when mixed at a 50:50 ratio of fly ash and slag with 1% micro steel fibers at curing temperature 240oC for 4 hours through two days. The compressive strength of the geopolymer mortar increas

   Adsorption of o-Nitrophenol (o-Nph), m- Nitrophenol (m-Nph) and p- Nitrophenol (pNph) on the sedimentary sand of the Tigress River which is known locally by “Zemeej” from aqueous solution at 288, 298, 308, 318 and 328 k0 . This study indicates that o-Nph and mNph take multi-layered S type according to Giles classification while p-Nph takes a multilayered L type according to the same classification. The isotherms treated by Freundlich model and show a good response to this model because the heterogeneous nature of the surface. The adsorption for all materials was endothermic as shown from ΔH values and explained through the porous nature of the surface, the remaining thermodynamic functions ΔG and ΔS w

This experiment was carried out at the Field of Poultry, Department of Animal Resources, College of Agriculture, University of Baghdad, during the period from 1/5/2011 until 5/7/2011 to study the effect of adding arginine to laying hens diet on certain blood traits. A total of 100 Brown Lohmann laying hen chickens, 38 weeks of age, were randomly distributed into four treatment groups, with 25 hens for each treatment. Treatment groups were: T1: bird-fed diet with no additional arginine (control group); T2, T3, and T4: bird-fed diet supplemented with 0.4, 0.7, and 0.9%, respectively. Therefore, the total amounts of arginine in the four treatments (T1, T2, T3, and T4) become 1.1, 1.5, 1.8, and 2.0%, respectively. Results of this experiment rev

Background: to evaluate the effect of different dentifrices on the surface roughness of two composite resins (nanofilled-based and nanoceramic – based composite resins). Materials and methods: Forty specimens (diameter 12 mm and height of 2mm) prepared from different composite resin materials: Z350 (nanofilled composite, and Ceram-X (nanoceramic) .they were subjected to brushing simulation equivalent to the period of 1 year. The groups assessed were a control group brushed with distilled water (G1), Opalescence whitening toothpasteR (G2), Colgate sensitive pro-relief (G3) and Biomed Charcoal Toothpaste (G4). The initial and final roughness of each group was tested by surface roughness tester. The results were statistically analyzed using

Background: With the increased in the demands of adult orthodontics, the challenge of direct bonding to non-enamel surface (zirconium) had been increased. The present study was carried out to compare the shear bond strength of three different brackets (stainless steel, sapphire and composite) bonded to zirconium surface and study the mode of bond failure. Materials and methods: The sample was comprised of 30 models (8mm *6mm*1.5mm) of full contour zirconium veneers. They were divided into three groups according to the brackets type; all samples were treated first by sandblast with aluminum oxide particle 50 µm then coated by z-prime plus primer. A central incisor bracket of each group was bonded to the prepared zirconium surface with lig

From a large number of bacterial samples collected from different hospital in Iraq in central  health laboratory ,only ten isolates were identified primary as Vibrio. A number of  morphology and biochemical test were carried out to complete this identification that showed all bacterial isolates were related to Vibrio cholerae .In this study  all Vibrio isolates were investigated for Bio typing and the result showed that all (10) isolate were related to (Eltor biotypes) .Also, the susceptibility test towards eight antibiotics were carried  out .

Results shows that  ciprofloxacin , Norfloxacin, Erythromycin, Ampicillin,  ceftriaxone  and Amikacin were the most effective

Corrosion experiments were carried out to investigate the effect of several operating parameters on the corrosion rate and corrosion potential of carbon steel in turbulent flow conditions in the absence and presence of sodium benzoate inhibitor using electrochemical polarization technique. These parameters were rotational velocity (0 - 1.57 m/s), temperature (30oC – 50oC), and time. The effect of these parameters on the corrosion rate and inhibition efficiency were investigated and discussed. It was found that the corrosion rate represented by limiting current increases considerably with increasing velocity and temperature and that it decreased with time due to the formation of corrosion product layer. The corrosion potential shifted t

Methotrexate (MTX) is widely used chemotherapeutic agent with different side effects including germ cells toxicities. Silibinin is one of the structural isomers of silymarin, with different phytotherapeutic applications, and its possible protective effects against MTX induced germ cells damage were investigated in this work. Twenty five male mice were divided into five groups (n=5) allocated as follows: Group 1 received buffer for five days given by single intraperitoneal (IP) injection per day; Group 2 in addition to buffer for five days, animals received at day five single dose of 20mg/kg of MTX IP. Groups (3, 4, and 5) received respectively, (50, 100, or 150mg/kg body weight) of silibinin IP single daily dose for five days then at day fi