This study explored the development and qualities of the response of electrochemical properties of enrofloxacin-selective electrodes using precipitation based on producing phosphotungstic, after utilizing a matrix of polyvinyl chloride (PVC) and dibutyl phthalate or dibutyl phosphate as a plasticizer. The resulting membrane sensors were an enrofloxacin-phosphotungstic electrode (sensors 1) and an ENR-DOP-PTA electrode (sensors 2). Linear responses of (ENR-DBPH-PTA) and (ENR-DOP-PTA) within the concentration ranges of 2.1×10^-6-10^-1 and 3.0×10^-6-10^-2 mol. L^-1, respectively, for both sensors were observed. Slopes of 51.61±0.24 and 39.40± 0.16 mV/decade and pH ranges equal to 2.5-8.5

Commercially pure titanium (cpTi) is widely used as dental implant material although it was found that titanium exhibited high modulus of elasticity and the lower corrosion tendency in oral environment. Niobium(Nb) was chosen for this study as an alternative to cpTi implant material due to its bioinert behavior and good elastic modulus and moderate cost in addition to corrosion resistance. This study was done to evaluate the effect of biomimetic coating on the surface properties of the commercially pure titanium and niobium implants by in vitro and in vivo experiments. The in vitro study was involved etching the samples of each material in HCl then soaking in 10M NaOH aqueous solution. These samples were then immersed in a 5 times concent

Helminthiasis is a significant economic burden on grazing cattle. Increased resistance to currently available synthetic anthelmintics used to treat helminthiasis, and anthelmintic residues in meat and dairy products pose a significant worldwide health threat. These obstacles require the development of new anthelmintics capable of combating drug resistance while also exhibiting improved safety profiles. Rhynchosia cana (Fabaceae) is a herb that has historically been used as a worm expeller. To evaluate the phytochemical profile and explore the anti-oxidant and anthelmintic effects of different extracts of Rhynchosia cana (R. cana) by In silico and In vitro methods. Using standardised chemical t

This study compared in vitro the microleakage of a new low shrink silorane-based posterior composite (Filtek™ P90) and two methacrylate-based composites: a packable posterior composite (Filtek™ P60) and a nanofill composite (Filtek™ Supreme XT) through dye penetration test. Thirty sound human upper premolars were used in this study. Standardized class V cavities were prepared at the buccal surface of each tooth. The teeth were then divided into three groups of ten teeth each: (Group 1: restored with Filtek™ P90, Group 2: restored with Filtek™ P60, and Group 3: restored with Filtek™ Supreme XT). Each composite system was used according to the manufacturer's instructions with their corresponding adhesive systems. The teeth were th

In vitro antifungal susceptibility test of itraconazole was carried out against 38 isolates from nails, skin, oral cavity, vagina and wounds, This study was done in Ramadi Teaching Hospital in period from January to August 2010. According to the National Committee for Clinical Laboratory Standard (NCCLS ) M 27- A by using the broth dilution method. Inoculum size was 1-5X10³ CFU/ ml, while final concentrations of itraconazole ranged from 0.025 – 6.4 μg / ml by using RPMI – 1640 broth media and the fungus was incubated at 35 ^oC.  No resistant stain was recorded. MIC ranged from 0.05 – 6.4 μg / ml and the Mean ± SEM was 0.89 ± 0.28. MIC for nail isolates was 0.05 –

Titanium dioxide nanotubes were synthesized by anodizing Ti sheets in the ethylene glycol solution and were covered in Pt nanoparticles onto the surface of TiO₂NTs using electrodeposition method from using five derivatives of Mannich base Pt complexes which have been used as precursor of platinum. The mean size, shape, elemental composition of the titanium dioxide nanotubes and platinum deposited on the template were evaluated by different techniques such as field emission scanning electron microscope (FE-SEM), transmission electron microscopy (TEM), X-ray diffraction pattern (XRD), and energy dispersive X-ray (EDX) technique. From all these analyses, the TiO₂NTs prepared and Ptnanoparticles deposited on it were ide

Titanium dioxide nanotubes were synthesized by anodizing Ti sheets in the ethylene glycol solution and were covered in Pt nanoparticles onto the surface of TiO2NTs using electrodeposition method from using five derivatives of Mannich base Pt complexes which have been used as precursor of platinum. The mean size, shape, elemental composition of the titanium dioxide nanotubes and platinum deposited on the template were evaluated by different techniques such as field emission scanning electron microscope (FE-SEM), transmission electron microscopy (TEM), X-ray diffraction pattern (XRD), and energy dispersive X-ray (EDX) technique. From all these analyses, the TiO2NTs prepared and Ptnanoparticles deposited on it were identified. The diagnoses pr