Objective: The objectives of the present study were to evaluate the effectiveness of the instructional intervention
about medical and health knowledge of patients with diabetes mellitus type II.
Methodology: A Quasi- experimental study was carried out in National Center for Diabetes Mellitus/ Almustansria
University, started from 4th January 2012, to 1st April 2012. Non-probability (purposive sample) of (50) diabetes
mellitus type II, who visit National Center for Diabetes Mellitus/ Almustansria University. The study sample is
divided equally into (25) study and (25) control groups. The study group received the instructional intervention.
While the control not exposed to the instructional intervention. The data are coll

Ricinus communis L. is an important medical plant hence it contains many active compounds. The aim of this research is to study the effect of plant growth regulators on callus induction and Rutin concentration. A combination of Benzyle adenine (BA) and Indol Acetic acid (IAA) at (0.0,1.0,2.0) mg/L was added to the media, the highest fresh weight of the induced callus from stem explant was (4.97) gr . at (1.0,1.0) mg/L BA and IAA consenquently the same combination gave the highest dry weight of callus (0.42) gr. while the combination at (2.0,1.0) mg/L BA and IAA gave the highest fresh weight of induced callus from Leaves explant (5.28) gr., then (2.0,1.0) mg/L BA and IAA gave the highest dry weight for callus induced from leaves at (0.55

Blades of gas turbine are usually suffered from high thermal cyclic load which leads to crack initiated and then crack growth and finally failure. The high thermal cyclic load is usually coming from high temperature, high pressure, start-up, shut-down and load change. An experimental and numerical analysis was carried out on the real blade and model of blade to simulate the real condition in gas turbine. The pressure, temperature distribution, stress intensity factor and the thermal stress in model of blade have been investigated numerically using ANSYS V.17 software. The experimental works were carried out using a particular designed and manufactured rig to simulate the real condition that blade suffers from. A new cont

The electrical properties of polycrystalline cadmium telluride thin films of different thickness (200,300,400)nm deposited by thermal evaporation onto glass substrates at room temperature and treated at different annealing temperature (373, 423, 473) K are reported. Conductivity measurements have been showed that the conductivity increases from 5.69X10-5 to 0.0011, 0.0001 (?.cm)-1 when the film thickness and annealing temperature increase respectively. This increasing in ?d.c due to increasing the carrier concentration which result from the excess free Te in these films.

Alloys of InxSe1-x were prepared by quenching technique with
different In content (x=10, 20, 30, and 40). Thin films of these alloys
were prepared using thermal evaporation technique under vacuum of
10-5 mbar on glass, at room temperature R.T with different
thicknesses (t=300, 500 and 700 nm). The X–ray diffraction
measurement for bulk InxSe1-x showed that all alloys have
polycrystalline structures and the peaks for x=10 identical with Se,
while for x=20, 30 and 40 were identical with the Se and InSe
standard peaks. The diffraction patterns of InxSe1-x thin film show
that with low In content (x=10, and 20) samples have semi
crystalline structure, The increase of indium content to x=30
decreases degree o