The operating characteristics of optoelectronic devices depend critically on the properties physical of the constituent materials, interesting compound has been focused on this research formed from group III and V of the periodic table. Thin film n-InSb heterjuntion were successfully fabricated on p-Si substrates by thermal evaporation technique at different annealing temperature (as prepared, 400,500,600) °C. The effect of annealing temperature on the structural, surface morphology, optical and optoelectronic properties of InSb films were investigated and studied. The crystal structure of the film was characterized by X-ray diffraction and techniques. AFM techniques inspect the surface morphology of InSb films, the study presented the val

In the present work, 9-fluorenone-2-carboxylic acid methyl ester (1) was prepared from 9-fluorenone-2-carboxylic acid and then converted into the acid hydrazide (2). Compound (2), is the key intermediate for the synthesis of several series of new compounds such as substituted 1,3,4-oxadiazole derivatives (3-6) were synthesized from the condensation of different substituted benzoic acids with compound (2) using POCl3 as condensing agent. Treatment of compound (2) with formic acid gave the N-formyl hydrazide (7), which upon refluxing with phosphorous pentoxide in benzene yielded the corresponding 5-(9-fluorenone-2-yl)-1,3,4-oxadiazole (8). Reaction of hydrazide (2) with phenyl isocyanate to give N-phenyl semicarbazide derivative (9), then thi

The synthesis of zeolite NaX from locally available kaolin has been studied. The operating conditions for zeolite NaX production from kaolin with good crystallinity were as follows; a gel formation step of metakaolin in alkaline medium in presence of additional silica to crystallize the zeolite was achieved at 60 oC for 1 hr,and with stirring. In ageing step of the reactants at room temperature for 5 days and crystallization step at 87±2 oC for 24 hr. The catalytic activity of catalyst prepared from local kaolin was studied by using cumene cracking as a model for catalytic cracking and compared with standard HY zeolite and HX zeolite catalysts. The activity test was carried out in a laboratory continuous flow unit with fixed bed reactor

Magnetic plaster kiln dust (MPKD) was synthesized as a unique, low-cost composite reused of byproduct plaster kiln dust (PKD), which is considered a source of air pollution. The FESEM, EDS, XRD, FTIR, VSM, and BET tests were used to characterize the MPKD. The characterization revealed that the MPKD was nanotubes non-agglomerated and super-paramagnetic with a high specific surface area (102.7 m²/g). Compared with the specific area of other materials (composites), the MPKD could be considered a promising substance in the field of water/wastewater treatment.