Wheat straw was modified with malonic acid in order to get low cost adsorbent have a good ability to remove copper and ferric ions from aqueous solutions, chemical modification temperature was 120°C and the time was 12 h. Parameters that affect the adsorption experiments were studied and found the optimum pH were 6 and 5 for copper and iron respectively and the time interval was 120 min and the adsorbent mass was 0.1 g. The values for adsorption isotherms parameters were determined according to Langmuir [qmax were 54.64 and 61.7 mg/g while b values were 0.234 and 0.22 mg/l] , Freundlich [Kf were 16.07 and 18.89 mg/g and n were 2.77 and 3.16], Temkin [B were 0.063 and 0.074 j/mol and At were 0.143 and 1.658 l/g] and for Dubinin-Radushkev

In this work, varying compositions of SiO₂ micro filler were added
with the Polyvinyl Chloride (PVC) and samples have been prepared
using film casting technique. The results have been analyzed and
compared for PVC samples with (1 wt%, 3 wt%, 5 wt% and 10 wt%)
SiO2 micro filler. Mechanical characteristics such as tensile strength,
elongation at break and Young`s modulus were measured for all the
samples, where the tensile strength was increased from 8.39 Mpa for
purified PVC to 16 Mpa for 3% SiO₂/PVC composite. Also, thermal
conductivity measurement values illustrated that composite materials
have a good thermal insulation at 10 wt. %, thermal conductivity was
decreased from 0.1684 W/m.

A new copolymer (MFA) was prepared from condensation of melamine (M) with p- methyl – anisole (A) in the presence of condensation agent like 37% (w/v) of formaldehyde. The new copolymer was characterized by elemental, IR and HNMR spectra. The chelating ion-exchange property of this polymer was studied for methylene blue dye in aqueous solution in 100-200ppm concentrations. The adsorption study was carried out over a wide range of pH, shaking time and in media of various kinetic parameters models. Thermal parameters like enthalpy, entropy and Gibbs free energy of adsorption process of methylene blue on surface of MFA resin were determined on the basis of kinetic parameters at different temperatures. To describe the equilibrium of adsorp

The present study aims to evaluate the effects of methotrexate (MTX) with and without vitamin A (Vit. A) on some biochemical parameters and histological structure in male rabbits liver. Twenty male rabbits weighing 1250-1480 gm were divided into four equal number groups. The first group was given 2 ml distilled water as control group. The second group was given MTX (20 mg/kg), the third group was given Vit. A (5000 IU), while the fourth group was given MTX (20 mg/kg) +Vit. A (5000 IU) in alternative days. Following four weeks of treatment, lipid profile total cholesterol (TC), triglycerides (TG), high-density lipoprotein (HDL), [low-density lipoprotein (LDL) and very low-density lipoprotein (VLDL)]; in addition to thyroid hormones tr

Incremental sheet forming (ISF) process offers a high degree of flexibility in the manufacturing of different sheet parts, which makes it an ideal candidate for prototype parts as well as efficient at fabricating various customized products at low production costs compared to traditionally used processes. However, parts produced in this process exhibit notable geometrical inaccuracy and considerable thickness reduction. In this paper, the single point incremental sheet forming variant of the process has been implemented to manufacture a highly customized cranial implant starting from the computed tomography (CT) scan data of the patient's anatomy. A methodology, from the modeling to the realization of the implant, is presented and discus

The Cu2SiO3 composite has been prepared from the binary compounds (Cu2O, and SiO2) with high purity by solid state reaction. The Cu2SiO3 thin films were deposited at room temperature on glass and Si substrates with thickness 400 nm by pulsed laser deposition method. X-ray analysis showed that the powder of Cu2SiO3 has a polycrystalline structure with monoclinic phase and preferred orientation along (111) direction at 2θ around 38.670o which related to CuO phase. While as deposited and annealed Cu2SiO3 films have amorphous structure. The morphological study revealed that the grains have granular and elliptical shape, with average diameter of 163.63 nm. The electrical properties which represent Hall effect were investigated. Hall coeffici

The objectives of this study revolve around identifying the extent of funding impact on the future of the printed Iraqi press, and whether it threatens their chances of survival, stating the extent of technological development on the income of the printed newspaper, and identifying the causes of the financial crisis on the newspaper. This research is classified as descriptive research, and the researcher used the survey method, and adopted the questionnaire of the views of the contactors, in five Iraqi newspapers (morning - extent - time - the way of the people - the call). The research community included (68) respondents, whereby the comprehensive inventory method was used to define the research community, and the researcher used t

Background: The formation of white spot lesions around fixed orthodontic attachments is a common complication during and after fixed orthodontic treatment, which hinders the result of a successfully completed orthodontic treatment. The aim of the study was to assess the effectiveness of the Caries Infiltrant (ICON®) on prevention of caries on the smooth enamel surface when applied alone or combined with conventional adhesives. Materials and methods: Seventy eight human premolar enamel discs were randomly assigned to six groups (n=13). The discs were etched and treated with resins of different monomer content forming the following groups: (1)Untreated etched samples served as the negative control, (2) ICON® (DMG), (3) Adper™ S

The weight of larvae virgins and Alcamlat for males more than the weight of females of the roles themselves that the highest rate of loss in weight of larvae developed to virgins when field conditions were (21.5,22,21.3) mg during June and July and August respectively, recorded the highest degrees of heat and less attributed to moisture