The aim of this work is to produce samples from Iraqi raw materials like Husyniat Bauxite (raw and burnt) and to study the effect of some additives like white Doekhla kaolin clays and alumina on that material properties were using sodium silica as a binding material. Five mixtures were prepared from Bauxite (raw and burnt) and kaolin clays, with an additive of (40) ml from sodium silica and alumina of (2.5, 5, 7.5,10 wt %) percentage as a binding material. the size grading was through sieving. The formation of all specimens was conducted by a measured gradually semi-dry pressing method under a compression force of (10) Tons and humidity ratio ranging from (5-10) % from mixture weight. Drying all specimens was done and then they were burn

Due to the broad range uses of chromium for industrial purposes, besides its carcinogenic effect, an efficient, cost effective removal method should be obtained. In this study, cow bones as a cheap raw material were utilized to produce active carbon (CBAC) by physiochemical activation, which was characterized using: SEM to investigate surface morphology and BET to estimate the specific surface area. The best surface area of CBAC was 595.9 m²/gm which was prepared at 600 ^ᵒC activation temperature and impregnation ratio of 1:1.5. CBAC was used in aqueous chromium ions adsorption. The investigated factors and their ranges are: initial concentration (10-50 mg/L), adsorption time (30-300 min), temperature (20-50

The aim of this study is to formulate and evaluate ezetimibe nanoparticles using solvent antisolvent technology. Ezetimibe is a practically water-insoluble drug which acts as a lipid lowering drug that selectively inhibits the intestinal absorption of cholesterol and related phytosterols. Ezetimibe prepared as nano particles in order to improve its solubility and dissolution rate.

Thirty formulas were prepared and different stabilizing agents were used with different concentrations such as poly vinyl pyrrolidone (PVPK-30), poly vinyl alcohol (PVA), hydroxy propyl methyl cellulose E5 (HPMC), and poloxamer. The ratios of drug to stabilizers used to prepare the nanoparticles were 1: 2, 1:3 and 1:4.

The prepared nanoparticles

Amino acids are the basic building block for peptides and proteins. They are raw materials for generating hormones, purines, pyrimidines and vitamins. Amino acids also provide the body with energy through their carbon structures. The study analyzed the amino acid in the kidneys of the albino mice embryo at 17 and 19 gestation days, using a high-performance liquid chromatography device (HPLC). Samples were obtained after removing them from the embryo and placing them in an ice bath to prevent cell lysis and acid loss. The study found 18 amino acids in the kidneys of the albino mice embryo. They are Asparagine (Asn), Glutamine (Glu), Serine (Ser), Glycine (Gly), Threonine (Thr), Histidine (His), Cysteine (Cys), Alanine (Ala), Proline

This research involves study effect of chloride ions in concentration range (0.01 – 0.50 mol.dm^-3) on the corrosion behavior of Al-Zn alloy in basic media of 1x10^-3 mol.dm^-3 NaOH at pH=11 and four different temperatures in the range (298-313 K). Cathodic and anodic Tafel slopes (b_c &b_a) and transfer coefficients (α_c & α_a) were calculated and the results interprets according to the variation of the rate – determining steps. The results also indicate that the chloride ions are bonded chemically in the interface as an initial step of formation of different mixed oxohydroxy – and chloro complexes. Polarization resistance (R_p) is calculates

Background: Polymethyl methacrylate (PMMA) is the most commonly used material in denture fabrication. The material is far from ideal in fulfilling the mechanical requirements. Midline fracture; poor thermal conductivity and water sorption, are common problem in this material. The purpose of this study was to evaluate the effect of addition of surface treated Aluminum oxide nano fillers on some properties of heat cured (PMMA). Materials and methods: In addition to controlled group of heat cured PMMA the silanized (Al2O3) nanoparticles was added to PMMA powder by weight in three different percentages 1wt%, 2wt% and 3wt%, mixed by probe ultra-sonication machine. 200 specimens were constructed and divided into 5 groups according to the test (e

Pulsed liquid laser ablation is considered a green method for the synthesis of nanostructures because there are no byproducts formed after the ablation. In this paper, a fiber laser of wavelength 1.064 µm, peak power of 1 mJ, pulse duration of 120 ns, and repetition rate of 20 kHz, was used to produce carbon nanostructures including carbon nanospheres and carbon nanorods from the ablation of asphalt in ethanol at ablation speeds of (100, 75, 50, 10 mm/s).  The morphology, composition and optical properties of the synthesized samples were studied experimentally using FESEM, HRTEM, EDS, and UV-vis spectrophotometer. Results showed that the band gap energy decreased with decreasing the ablation speed (increasing the ablation time), the mi

KE Sharquie, SA Al-Mashhadani, A A Noaimi, RK Al-Hayani, SA Shubber, Iraqi Journal of Community Medicine, 2017 - Cited by 1