A polycrystalline CdSe thin films doped with (5wt%) of Cu was fabricated using vacuum evaporation technique in the substrate temperature range(Ts=RT-250)oC on glass substrates of the thickness(0.8?m). The structure of these films are determined by X-ray diffraction (XRD). The X-ray diffraction studies shows that the structure is polycrystalline with hexagonal structure, and there are strong peaks at the direction (200) at (Ts=RT-150) oC, while at higher substrate temperature(Ts=150-250) oC the structure is single crystal. The optical properties as a function of Ts were studied. The absorption, transmission, and reflection has been studied, The optical energy gap (Eg)increases with increase of substrate temperature from (1.65

The eff ect of partial substitution for lanthanum (La) on the structural properties of the compound Y1-xLaxBa4Cu7O15+δ were studied. The variation of (x) are x=0.1, 0.2 and 0.3, which was synthesized by solid state reaction method. The mixed powder was pressed with pressure (7 ton / cm2) as a disc (1.5 cm) diameter and a thickness of (0.25 to 0.3 cm). The samples were sintering by 120 °C / hour with a changing rate from room temperature to 850 ° C through 72 hours. XRD analysis using to calculate crystal size, strain and degree of crystallinity. It was found all samples have orthorhombic structure and change of structure with increasing lanthanum concentration. It was shown that the change lanthanum concentrations of all our samp

Several schottky diodes were fabricated from polyaniline/ Carbon nanotube (single and multiwalled) composites. These composites were synthesized with different concentration and two carbon nanotubes types, Single and Multi-Walled Carbon Nanotubes (SWCNT & MWCNT). Aluminum and silver paste were chosen as schottky and ohmic contact respectively. physical and electrical were used to studied these composite by using Atomic Force Microscopy (AFM) and electrical measurements. The Root Mean Square RMS surface roughness of the composite samples was found to be around 4nm. The currentvoltage characteristic were measurements for all samples in the bias range ±15V at room temperature. The results shows the increasing in carbon nanotubes concentration

The aim of this research is to develop mechanical properties of a new aluminium-lithium-copper alloy. This alloy prepared under control atmosphere by casting in a permanent metal mould. The microstructure was examined and mechanical properties were tested before and after heat treatment to study the influence of heat treatment on its mechanical properties including; modulus of elasticity, tensile strength, impact, and fatigue. The results showed that the modulus of elasticity of the prepared alloy is higher than standard alloy about 2%. While the alloy that heat treated for 6 h and cooled in water, then showed a higher ultimate tensile stress comparing with as-cast alloy. The homogenous heat treatment gives best fatigue

This experiment was carried out at the Grdarash field belongs to the Agricultural researches directorate/general Agriculture directorate-Erbil in September (2007)، 27 Arabic lambs aged (5-6 months) With average initial weight (39.178 Kg/lamb) were used. Lambs were divided in to (3) groups (9 lambs/group). Control group was fed on (85% barely، 10% bran and 5% straw)، and second and third groups were fed on various by-product in replacement with barely in loss and block shape respectively.

The total gain of three groups were (392708.32، 634826.52 & 445613.72 ID resp

Background: Decalcification of surface enamel adjacent to fixed orthodontic appliances, in the form of white spot lesions, is a wide spread and familiar well-known side effect of orthodontic treatment. The present study was carried out to evaluate the effect of enamel protective agent (Clinpro white varnish) on shear and tensile bond strength of Dentaurum orthodontic stainless steel brackets by using 3M Unitek and Ormco as orthodontic adhesive agents. Materials and methods: Sixty-four extracted human upper first premolar teeth were selected and randomly divided into two groups with 32 teeth each, representing the shear and tensile bond strength testing groups. Then according to the type of bonding adhesive and the addition of Clinpro before

nouns , because deriving these names will lead to eternity which is impossible, and restrict the derivation only in agent nouns from their verbs, and the adjective names from their adjectives with the condition of truth in derivation.
The derivation of “Allah” names was denied due to a creed thoughts, because saying that “Allah” names is derived will not describe the eternal essence of “Allah”, and if it were derived this will make “Allah” is a Compound from his essence and Attributes.
The Al-Zaher people had recant the derivation of the agent nouns by preventing the derivation of “Allah” names because it will make “Allah” is a Compound from his essence and Attributes.
The Al-Zaher people had recant from

Dentures that are not cleaning and maintained properly may prone to contamination by different microbial pathogens that result in several oral conditions. This study was design to compare the antimicrobial effect of different denture cleansers oxalic, tartaric, citric acids and alkaline peroxide with microwave irradiation on the growth of Candida albicans and Staphylococcus aureus respectively. Microwave oven used to disinfect specimens of heat-activated acrylic resin and soft linear. Oxalic, citric, tartaric acids, and alkaline peroxide were also used. Microorganisms that tested were Candida albicans and Staphylococcus aureus separately. Treatment with microwave or tartaric acid could achieve sterilization of both hot cured acrylic resins